The Effect of Metal Primer Application and Nd:YAG Laser Irradiation on the Shear-Bond Strength Between Polymethyl Methacrylate and Cobalt-Chromium Alloy

Experimental and Chitosan-Infused Adhesive with Dentin Pretreated with Femtosecond Laser, Methylene Blue-Activated Low-Level Laser, and Phosphoric Acid

Aim: To prepare experimental adhesive (EA) with 1% and without chitosan nanoparticles on dentin conditioned with a conventional technique phosphoric acid (PA) compared with two different contemporary techniques: photodynamic therapy (PDT) and femtosecond laser (FSL). Method: The methodology consisted of synthesis of EA and 1% chitosan-modified adhesive (CMA). Scanning electron microscopy, dentin adhesive interface assessment, energy-dispersive spectroscopy, shear bond strength (SBS), degree of conversion (DC), and bond failure were assessed. Teeth were selected, disinfected, and mounted in acrylic up to the cementoenamel junction. Occlusal enamel was removed and teeth were randomly allocated into groups and conditioned. These included Group 1: samples treated with PA; Group 2: specimens conditioned with methylene blue photosensitizer (MBP) activated by PDT; and Group 3: samples conditioned with FSL. Following different conditioning regimes, specimens were bonded using 1% CMA and EA. The composite buildup was followed by SBS testing and a bond failure assessment. DC was assessed for both EA and CMA. Analysis of variance and Tukey's post hoc test were used to compare the mean and standard deviation of SBS and DC in different experimental groups, with a significance level of p < 0.05. Results: Dentin pretreated with etch and rinse demonstrated the highest bond strength with 1% CMA. Dentin conditioned with MBP activated by PDT and bonded to EA showed the lowest bond scores. Overall SBS values of 1% CMA were better than EA irrespective of the conditioning regime of dentin. The DC was higher in EA adhesive. This was followed by DC in 1% CMA. DC in EA was found to be comparable with 1% CMA. Conclusions: PA remains the gold standard for dentin conditioning. The incorporation of 1% chitosan in adhesive improves SBS and results in no change in DC. The use of FSL in dentin conditioning can be used as an alternative approach as it results in SBS within acceptable limits. The study was approved by the ethical board of King Saud University.

Effect of laser etching on surface characteristics and porcelain bond to soft milled and direct metal laser sintered cobalt chromium alloys

STATEMENT OF PROBLEM

The surface topography of metal substrate can affect its bond to porcelain. A neodynium-doped yttrium aluminum garnet (Nd:YAG) laser has been introduced to modify the metal surface topography and improve porcelain bond strength. However, studies on the effect of laser etching on metal to porcelain bond strength are lacking.

PURPOSE

The purpose of this in vitro study was to determine the effect of Nd:YAG laser etching on the surface roughness and wettability of and the porcelain bond strength to cobalt chromium (Co-Cr) substrate fabricated by milling and direct metal laser sintering (DMLS).

MATERIAL AND METHODS

Thirty-two 0.5×3×25-mm Co-Cr specimens were fabricated by milling soft Co-Cr (M group) and DMLS Co-Cr metal powder (DML group). The surface topography of representative specimens from each study group was assessed under a scanning electron microscope (SEM) and an atomic force microscope (AFM). All specimens were assessed for surface roughness using a contact profilometer, and for wettability with a contact angle goniometer. Half of the specimens of each study group (n=8) were subjected to surface laser etching by using a Nd:YAG laser. The specimens subjected to etching were assessed again for surface topography and wettability. All specimens in both study groups were veneered with porcelain. The porcelain bond strength was tested with a 3-point bend test in a universal testing machine. The results were statistically analyzed with 2-way ANOVA test followed by the post hoc Tukey test for pairwise comparisons (α=.05).

RESULTS

After etching, the M group had a higher mean ±standard deviation Ra and Rz of 2.9 ±0.6 and 17.7 ±3.2 µm and significantly better wettability and bond strength of 79 ±6 and 52 ±13 MPa. In contrast, after etching, the DMLS group had a significantly lower Ra and Rz of 7.9 ±2.4 and 41.8 ±9.3 µm and significantly lower wettability and bond strength of 87 ±4 and 70 ±10 MPa. The DMLS group had a significantly higher roughness and bond strength than the M group before and after laser etching. The SEM and AFM showed different surface topography in the study groups.

CONCLUSIONS

The manufacturing process of Co-Cr substrate had a significant effect on surface characteristics and porcelain bond strength. Laser etching improved the surface topography and bond strength of milled Co-Cr but not of DMLS Co-Cr.

Effect of laser surface treatment on shear bond strength between polyetheretherketone and heat-activated polymethylmethacrylate resin

PURPOSE

To compare the shear bond strength between polyetheretherketone (PEEK) and heat activated polymethylmethacrylate (PMMA) resin after laser treatment.

MATERIALS AND METHODS

A total of 128 PEEK discs were fabricated (10 mm diameter and 2 mm thickness) and allocated into two groups. Group 1 was subjected to surface treatment followed by thermal cycling for 5000 cycles and group 2 was subjected to surface treatment followed by thermal cycling for 10,000 cycles. Each group was further subdivided into four subgroups (n = 16) which were: no surface treatment; primer treatment; acid etching; and laser surface treatment. PEEK was then bonded with PMMA resin using the conventional flasking technique. The shear bond strength was evaluated using a universal testing machine with a crosshead speed of 1 mm/min. Statistical analysis was done using one-way ANOVA for comparing within groups, followed by Tukey HSD test. Student's T-test was done to evaluate between the two groups.

RESULTS

In group 1, the highest shear bond strength was exhibited by the laser group (19.08 ± 0.16 MPa) followed by the acid etch group (14.84 ± 0.23 MPa), and the primer group (6.43 ± 0.20 MPa), while the least shear bond strength was observed in the no surface treatment group (4.98 ± 0.34 MPa) which was found to be significant (p < 0.05). In group 2, the highest shear bond strength was observed in the laser group (18.21 ± 0.23 MPa) followed by the acid etch group (13.77 ± 0.48 MPa), and the primer group (6.04 ± 0.11 MPa), while the least shear bond strength was observed in no surface treatment group (4.35 ± 0.21 MPa) which was found to be significant (p < 0.05).

CONCLUSION

The shear bond strength between PEEK and PMMA resin was highest for specimens that were surface treated with laser and followed by specimens treated with acid etching, primer application, and without surface treatment, respectively. Increasing thermal cycling from 5000 cycles to 10,000 cycles also reduced the bond strength.

Application of Laser Treatment in Adhesive Bonding of Liners to Polymethyl Methacrylate Denture Resins: A Systematic Review and Meta-Analysis

Objective: This systematic review and meta-analysis aimed to assess the influence of laser treatment on adhesive bonding of liners to polymethyl methacrylate (PMMA) denture base resins. Methods: The focused question was: "Does the application of laser treatment (Intervention) influence the adhesive bonding strength (Outcome) of liners to PMMA denture base resins (Population) as compared with untreated or unconditioned surfaces (Control)?" In vitro and clinical reports as well as reports on influence of laser treatments on bonding strength of liners to PMMA denture resins in comparison with untreated surfaces were included. Reports without any control group[s], without any application of laser[s] for PMMA denture bases that did not utilize PMMA denture bases, and not evaluate bond strength of PMMA denture base resins were excluded. An electronic search was conducted on PubMed, Scopus, and Web of Science. Meta-analyses were performed for calculating the standard mean difference (SMD) with a 95% confidence interval (95% CI). Results: Nine of the 12 included studies found that laser irradiation treatment produced significant surface texture alterations of the PMMA denture base and improved the adhesion between the PMMA denture base and soft lining. According to the meta-analysis, tensile bond strength showed an SMD of -2.49% (95% CI: -3.89 to -1.08; p = 0.0005), suggesting a statistically significant difference between the control and test groups (i.e., favoring laser-treated samples than untreated samples). Regarding shear bond strength scores, the outcomes showed an SMD of -2.24% (95% CI: -3.79 to -0.69; p = 0.005), suggesting a statistically significant difference between the control and test groups (i.e., favoring laser-treated samples than untreated samples). Conclusions: Despite the high heterogeneity among the included studies, it can be concluded that laser treatment might improve the bonding strengths of liners to PMMA denture base resins as compared with untreated surfaces. To validate the aforementioned conclusions, further verification is required through the implementation of well-designed randomized controlled trials with large sample sizes.

Dental Alloy Adhesive Primers and Bond Strength at Alloy-Resin Interface: A Systematic Review and Meta-analyses

AIM

The present systematic review aimed to report the studies concerning the primers in improving bond strength and identifying pertinent primers for a particular dental alloy by adhering to PRISMA precepts.

MATERIALS AND METHODS

PubMed and Semantic Scholar databases were scoured for articles using 10 search terms. In vitro studies satisfying the inclusion criteria were probed which were meticulously screened and scrutinized for eligibility adhering to the 11 exclusion criteria. The quality assessment tool for in vitro studies (QUIN Tool) containing 12 criteria was employed to assess the risk of bias (RoB).

RESULTS

A total of 48 studies assessing shear bond strength (SBS) and 15 studies evaluating tensile bond strength (TBS) were included in the qualitative synthesis. Concerning SBS, 33.4% moderate and 66.6% high RoB was observed. Concerning TBS, 26.8% moderate and 73.2% high RoB was discerned. Seventeen and two studies assessing SBS and TBS, respectively, were included in meta-analyses.

CONCLUSIONS

Shear bond strength and TBS increased for the primed alloys. Cyclic disulfide primer is best-suited for noble alloys when compared with thiol/thione primers. Phosphoric acid- and phosphonic acid ester-based primers are opportune for base alloys.

CLINICAL SIGNIFICANCE

The alloy-resin interface (ARI) would fail if an inappropriate primer was selected. Therefore, the selection of an appropriate alloy adhesive primer for an alloy plays a crucial role in prosthetic success. This systematic review would help in the identification and selection of a congruous primer for a selected alloy.

Effect of Fiber Laser Irradiation on the Shear Bond Strength between Acrylic Resin and Titanium

OBJECTIVES

The aim of this study is to investigate the shear bond strength of an acrylic resin to titanium after different surface treatment methods.

MATERIAL AND METHODS

A total of seventy-two disc-shaped specimens (10 mm × 10 mm × 2 mm) were prepared from titanium alloy. The specimens were randomly allocated to six equal groups: Group S (sandblasting), Group MP (metal primer), Group 10W (fiber laser 10 W), Group 20W (fiber laser 20 W), Group 10WMP (fiber laser 10 W+metal primer), and Group 20WMP (fiber laser 20 W+metal primer). All of the specimens were thermocycled up to 5000 cycles. After thermal cycling, a shear bond strength test was conducted. The shear bond strength data were analyzed with one-way ANOVA and Tukey's post hoc pairwise comparisons (p < 0.05).

RESULTS

While the highest values were determined in Group MP, the lowest values were observed in Group S. Additionally, Group MP exhibited significantly higher shear bond strength values than any of the other groups (p < 0.05) except Group 10WMP. Similar results were observed between Group MP and Group 10WMP (p > 0.05). The groups in which a metal primer was applied (Group MP, 10WMP, and 20WMP) showed significantly higher values than Group S. The shear bond strength values of Group 10W and Group 20W were similar.

CONCLUSIONS

The application of a metal primer significantly improved the bond strength of acrylic resin to titanium. Fiber laser application may be an alternative method to sandblasting for improving the bond strength of acrylic resin to titanium.

Comparative Evaluation of Effects of Laser Modalities on Shear Bond Strengths of Veneering Porcelains to Laser Sintered Substructures: An In Vitro Study

OBJECTIVE

Laser modalities and direct metal laser sintering (DMLS) have a potential to enhance micromechanical bonding between dental super- and infrastructures. However, the effect of different manufacturing methods on the metal-ceramic bond strength needs further evaluation. We investigated the effect of surface treatment with Er:YAG, Nd:YAG, and Ho:YAG lasers on the shear bond strength (SBS) of high-fusion dental porcelains (Vita and G-Ceram) to infrastructures prepared with DMLS in vitro settings.

MATERIALS AND METHODS

Study specimens (n = 128) were randomly divided into study subsets (n = 8), considering treatment types applied on the surface of infrastructures, including sandblasting and selected laser modalities; infrastructure types as direct laser sintered (DLS) and Ni-Cr based; and superstructure porcelains as Vita and G-Ceram. The SBS test was performed to assess the effectiveness of surface modifications that were also examined with a stereo microscope.

RESULTS

Considering laser procedure types, the highest SBS values were obtained by Er:YAG laser, followed by, with a decreasing efficiency, Ho:YAG laser and sandblasting procedures, and Nd:YAG laser procedure (p < 0.05). Nd:YAG laser decreases the bonding of Vita and G-Ceram in all the infrastructures compared with sandblasting. Considering porcelains, the highest SBS values were obtained by Vita (p < 0.05). Considering infrastructures, the highest SBS values were obtained by DMLS procedure (p < 0.05). The laser procedures caused surface irregularities as revealed by the stereo microscopic examination.

CONCLUSIONS

In current experimental settings, Er:YAG laser applied to DLS infrastructure veneered with Vita porcelain increases bonding strength more distinctly, and Nd:YAG laser applied to Ni-Cr-based infrastructure veneered with G-Ceram porcelain alters bonding strength unfavorably.