Effect of 457 nm diode-pumped solid state laser on the polymerization composite resins: microhardness, cross-link density, and polymerization shrinkage

Effect of Two Different Ultrafast Curing Exposure Durations on the Surface Hardness of Bulk Fill Composite - An In-Vitro Study

AIM

The aim of the present study is to assess the microhardness of resin-based composites (RBCs) cured with ultrafast curing mode at two different exposure durations.

STUDY DESIGN

This is an experimental in-vitro study. Forty-five cylindrical composite specimens were prepared to a dimension of 5 mm height and 4 mm diameter. Curing was done using three different exposure modes and duration with dual mode LED curing light as follows: Group I: Ultrafast curing mode for 1 second at 2300 mW/cm2 (n = 15); Group II: Ultrafast curing mode for 3 second at 2300 mW/cm2 (n = 15) and Group III: Standard exposure mode for 20 second at 1000 mW/cm2 (n = 15). Vicker's microhardness measurement was done on both the curing and non-curing sides of the specimen using a motorised diamond-faced micro-indenter (Wilson Wolpwert, Germany) using a load of 50 gram and a dwell time of 30 second.

STATISTICAL ANALYSIS

Kruskal Wallis ANOVA was used to test for difference between the three groups followed by Mann-Whitney U test for post-hoc analysis.

RESULTS

The microhardness values of the composite cured with a conventional curing unit were significantly higher than the ultrafast cured specimens.

CONCLUSION

Low-intensity conventional curing lights were found to perform better than the high-intensity ultrafast curing units.

Awareness and Utilization of Bulk-Fill Composites among Dental Practitioners in Saudi Arabia

Objective:

The aim of this study was to assess the knowledge and utilization of Bulk-Fill (BF) resin composites among dental practitioners in Saudi Arabia.

Materials and Methods:

An online survey was distributed through Twitter, Instagram and WhatsApp applications among dentists in Saudi Arabia. A 31-item questionnaire covering personal data, general knowledge and utilization of BF composites was used. Responses were collected and analyzed for trends. A knowledge scale was developed based on answers with specific weight for each correct answer provided by the participants. A score of ≥ 50% was considered as a satisfactory knowledge level for participants. Statistical analysis was conducted using One-sample Z- and Chi-square tests followed by Bonferroni correction at 0.05 significance level.

Results:

The total number of participants of the survey was 183, of which 41.5% had some knowledge and utilized BF composites in their practice. Only 9.84% of the participants score ≥ 50% on the knowledge scale. A significantly low proportion recognized accurately the compositional difference between BF and conventional resin composite as well as the minimum irradiance values needed for proper polymerization of BF. There was no effect for gender or years of experience on the knowledge or utilization of BF materials (p-value = 0.172).

Conclusion:

The proportions of practitioners with adequate knowledge and utilization of BF materials were very low. Additional focus must be provided in order to expose graduating dentists to advances in resin composite formulations.

Irradiance of Different Curing Modes of Common Light Cure Devices: An In Vitro Study

Aim:

The aim of this study was to test the irradiance values of different curing modes of commonly available light cure devices (LCDs).

Materials and Methods:

An in vitro investigation was carried out to compare the irradiance output of 10 brands of LCDs available in Saudi Arabia measured using a digital radiometer. Values were recorded for three time points when applicable (0, 10, and 20s). This technique was repeated five times for each LCD. Normal, high-intensity, and soft-start modes were evaluated for all brands with the features available. Irradiance values between brands were analyzed using one-way analysis of variance followed by Bonferroni method. Changes in irradiance between different time points were analyzed using one sample t test for normal and high-intensity modes and using paired t test for soft-start mode. All comparisons were carried out at 0.05 significance level.

Results:

The highest values were reported for Ortholux Luminous, Elipar DeepCure-S, Elipar DeepCure, and KaVo mini-LED with values above 1000 mW/cm². All LCDs showed values above 600 mW/cm². Three LCDs had high-intensity mode and only one device had soft-start mode. Changes over the different time points were not statistically significant exept for soft-start mode.

Conclusion:

All tested LCDs had irradiance values sufficient for adequate polymerization of resin composite. Only four of these are capable of curing bulk-fill composites.

Effect of the manual manipulation of composite resin with latex gloves

Purpose: This in vitro study aimed to evaluate the influence of the manual manipulation of two composite resins: Filtek™ Z350XT (3M ESPE) and Herculite Précis® (Kerr), with latex gloves contaminated with powder, human saliva and alcohol, on the microhardness values. Material and Methods: Manual manipulation was evaluated using latex gloves with powder, latex gloves without powder, latex gloves without powder with saliva, latex gloves without powder with alcohol, and without hand manipulation or contaminants (control). Each resin was manually manipulated for 10 seconds and photoactivated for 20 seconds with a light intensity of 1000mW/cm2 using a VALO –Ultradent LED light– cured unit, and then each sample was evaluated on the microhardness Vickers tester Leitz (Wetzlar). The collected data were analyzed using Kruskal –Wallis and Mann – Whitney post-test (p<0.05). Results. Microhardness values showed a significant difference between the evaluated and control groups, showing lower microhardness values in the group of latex glove with powder for Filtek™ Z350XT and the group of latex glove without powder with saliva for Herculite Précis®. Conclusion. The manual manipulation of composite resins decreases their surface microhardness.