OBJECTIVE

The aim of this study was to compare the postoperative fixation properties of a biodegradable osteosynthesis "free-form" plate achieved with countersunk screws with those provided by screws with cut-off screw heads.

STUDY DESIGN

Acrylic pipes were fixed together to simulate fracture fixation for tensile testing. Additional plates were fixed to a polyurethane block with a single screw for plate-screw pullout testing. Specimens were incubated in phosphate buffer solution at 37 degrees C, and testing was conducted at various time points during hydrolytic degradation of 26 weeks. In both tests the specimens were loaded at a speed of 5 mm/min until failure. The yield load, maximum load, and stiffness were recorded, and failure mode was visually determined.

RESULTS

Both countersunk screws and screws with cut-off screw heads provided similar plate fixation properties over degradation time.

CONCLUSION

According to these results, fixation of the biodegradable osteosynthesis free-form plate with screws with cut-off screw heads seems to be feasible.

Biomechanical in vitro evaluation of the effect of cyclic loading on the postoperative fixation stability and degradation of a biodegradable ankle plate

The effect of cyclic loading on the postoperative fixation stability of a biodegradable ankle plate was tested biomechanically during 12 weeks of hydrolytic degradation. Fracture of the lateral malleolus was simulated, and the parameters of cyclic loading were chosen to represent the physiological conditions during the healing period. Additionally, the effect of cyclic loading on degradation was investigated by measuring the inherent viscosities. In Group I, the cyclic loading was conducted in four phases with gradual increases in estimated walking distance and speed during the healing period. In Group II, cyclic loading was conducted after 12 weeks. Group III was used as a control for inherent viscosity measurements. None of the specimens failed under cyclic loading. No significant differences were found between the loaded groups in any of the parameters measured. Additionally, no significant difference was found in inherent viscosities at 12 weeks. The initial fixation stability provided by the biodegradable ankle plate remains biomechanically unchanged over 12 weeks. Cyclic loading, applied either during or after 12 weeks of hydrolytic degradation, does not seem to have any clinically relevant effect on the fixation stability or the degradation properties.