Bone Regenerative Potential of Modified Biphasic Graft Materials

Influence of physicochemical characteristics of calcium phosphate-based biomaterials in cranio-maxillofacial bone regeneration. A systematic literature review and meta-analysis of preclinical models

Objectives

Calcium phosphate-based biomaterials (CaP) are the most widely used biomaterials to enhance bone regeneration in the treatment of alveolar bone deficiencies, cranio-maxillofacial and periodontal infrabony defects, with positive preclinical and clinical results reported. This systematic review aimed to assess the influence of the physicochemical properties of CaP biomaterials on the performance of bone regeneration in preclinical animal models.

Methods

The PubMed, EMBASE and Web of Science databases were searched to retrieve the preclinical studies investigating physicochemical characteristics of CaP biomaterials. The studies were screened for inclusion based on intervention (physicochemical characterization and in vivo evaluation) and reported measurable outcomes.

Results

A total of 1532 articles were retrieved and 58 studies were ultimately included in the systematic review. A wide range of physicochemical characteristics of CaP biomaterials was found to be assessed in the included studies. Despite a high degree of heterogeneity, the meta-analysis was performed on 39 studies and evidenced significant effects of biomaterial characteristics on their bone regeneration outcomes. The study specifically showed that macropore size, Ca/P ratio, and compressive strength exerted significant influence on the formation of newly regenerated bone. Moreover, factors such as particle size, Ca/P ratio, and surface area were found to impact bone-to-material contact during the regeneration process. In terms of biodegradability, the amount of residual graft was determined by macropore size, particle size, and compressive strength.

Conclusion

The systematic review showed that the physicochemical characteristics of CaP biomaterials are highly determining for scaffold's performance, emphasizing its usefulness in designing the next generation of bone scaffolds to target higher rates of regeneration.

Evaluation of an In Situ Hardening β-Tricalcium Phosphate Graft Material for Alveolar Ridge Preservation. A Histomorphometric Animal Study in Pigs

The purpose of this study was to investigate the effectiveness of a resorbable alloplastic in situ hardening bone grafting material for alveolar ridge preservation in a swine model. Seven Landrace pigs were used. In each animal, the maxillary left and right deciduous second molars were extracted, and extraction sites were either grafted with a resorbable alloplastic in situ hardening bone substitute, composed of beta-tricalcium phosphate (β-TCP) granules coated with poly(lactic-co-glycolic) acid (PLGA), or left unfilled to heal spontaneously. Animals were euthanized after 12 weeks, and the bone tissue was analyzed histologically and histomorphometrically. Linear changes of ridge width were also clinically measured and analyzed. Pronounced bone regeneration was found in both experimental and control sites, with no statistically significant differences. At the experimental sites, most of the alloplastic grafting material was resorbed and remnants of the graft particles were severely decreased in size. Moreover, experimental sites showed, in a statistically nonsignificant way, less mean horizontal dimensional reduction of the alveolar ridge (7.69%) compared to the control sites (8.86%). In conclusion, the β-TCP/PLGA biomaterial performed well as a biocompatible resorbable in situ hardening bone substitute when placed in intact extraction sockets in this animal model.