Transport properties of Nd1.85Ce0.15CuO4+ delta crystals before and after reduction

Electron Number-Based Phase Diagram of Pr_{1-x}LaCe_{x}CuO_{4-δ} and Possible Absence of Disparity between Electron- and Hole-Doped Cuprate Phase Diagrams

We performed annealing and angle resolved photoemission spectroscopy studies on electron-doped cuprate Pr_{1-x}LaCe_{x}CuO_{4-δ} (PLCCO). It is found that the optimal annealing condition is dependent on the Ce content x. The electron number (n) is estimated from the experimentally obtained Fermi surface volume for x=0.10, 0.15 and 0.18 samples. It clearly shows a significant and annealing dependent deviation from the nominal x. In addition, we observe that the pseudo-gap at hot spots is also closely correlated with n; the pseudogap gradually closes as n increases. We established a new phase diagram of PLCCO as a function of n. Different from the x-based one, the new phase diagram shows similar antiferromagnetic and superconducting phases to those of hole doped ones. Our results raise a possibility for absence of disparity between the phase diagrams of electron- and hole-doped cuprates.

Microscopic annealing process and its impact on superconductivity in T'-structure electron-doped copper oxides

High-transition-temperature superconductivity arises in copper oxides when holes or electrons are doped into the CuO(2) planes of their insulating parent compounds. Whereas hole doping quickly induces metallic behaviour and superconductivity in many cuprates, electron doping alone is insufficient in materials such as R(2)CuO(4) (R is Nd, Pr, La, Ce and so on), where it is necessary to anneal an as-grown sample in a low-oxygen environment to remove a tiny amount of oxygen in order to induce superconductivity. Here we show that the microscopic process of oxygen reduction repairs Cu deficiencies in the as-grown materials and creates oxygen vacancies in the stoichiometric CuO(2) planes, effectively reducing disorder and providing itinerant carriers for superconductivity. The resolution of this long-standing materials issue suggests that the fundamental mechanism for superconductivity is the same for electron- and hole-doped copper oxides.

Thermal conductivity of Pr1.3-xLa0.7CexCuO4 single crystals and signatures of stripes in an electron-doped cuprate

It was recently demonstrated that the anisotropic phonon heat transport behavior is a good probe of the stripe formation in La(2-x)Sr(x)CuO(4) (LSCO) [Phys. Rev. B 67, 104503 (2003)]]. Using this probe, we examined an electron-doped cuprate Pr(1.3-x)La(0.7)Ce(x)CuO(4) (PLCCO) and found that essentially the same features as those in LSCO are observed. Moreover, the in-plane resistivity rho(ab) of lightly doped PLCCO shows metallic behavior (drho(ab)/dT>0) in the Néel ordered state with a mobility comparable to that in LSCO. It is discussed that these peculiar properties in common with LSCO signify the existence of stripes in electron-doped cuprates.