Accommodation of vortices to tilted line defects in high-Tc superconductors with various electronic anisotropies

Dynamic and thermodynamic properties of porous vortex matter in Bi(2)Sr(2)CaCu(2)O(8) in an oblique magnetic field

Vortex matter in Bi(2)Sr(2)CaCu(2)O(8) with a low concentration of tilted columnar defects (CDs) was studied using magneto-optical measurements and molecular dynamics simulations. It is found that while the dynamic properties are significantly affected by tilting the magnetic field away from the CDs, the thermodynamic transitions are angle independent. The simulations indicate that vortex pancakes remain localized on the CDs even at large tilting angles. This preserves the vortex thermodynamics, while vortex pinning is considerably weakened due to kink sliding.

Observation of individual vortices trapped along columnar defects in high-temperature superconductors

Many superconductors do not entirely expel magnetic flux-rather, magnetic flux can penetrate the superconducting state in the form of vortices. Moving vortices create resistance, so they must be 'pinned' to permit dissipationless current flow. This is a particularly important issue for the high-transition-temperature superconductors, in which the vortices move very easily. Irradiation of superconducting samples by heavy ions produces columnar defects, which are considered to be the optimal pinning traps when the orientation of the column coincides with that of the vortex line. Although columnar defect pinning has been investigated using macroscopic techniques, it has hitherto been impossible to resolve individual vortices intersecting with individual defects. Here we achieve the resolution required to image vortex lines and columnar defects in Bi2Sr2CaCu2O8+delta (Bi-2212) thin films, using a 1-MV field-emission electron microscope. For our thin films, we find that the vortex lines at higher temperatures are trapped and oriented along tilted columnar defects, irrespective of the orientation of the applied magnetic field. At lower temperatures, however, vortex penetration always takes place perpendicular to the film plane, suggesting that intrinsic 'background' pinning in the material now dominates.