Reducing composite restoration polymerization shrinkage stress through resin modified glass-ionomer based adhesives

Selective carious tissue removal and glass ionomer liner reduction of pulp stress in bulk fill resin composite restorations

To evaluate the effect of selective or nonselective carious tissue removal and the use of a resin-modified glass ionomer (RMGIC) liner under bulk fill resin composite restoration on the stress at the pulp chamber, the elastic moduli of hard, firm, soft and intact dentin were calculated using nanoindentation. Post-gel shrinkage of the bulk fill resin composite and RMGIC were determined using the strain-gauge method. Six finite element models were created by using digital radiography with the combination of two study factors: a) carious tissue removal: selective removal or nonselective removal of carious tissue, and b) use of RMGIC liner: with or without 1.0 mm of RMGIC liner. The modified von Mises stresses (mvm) (MPa) were extracted on the nodes of the internal wall of the pulp ceiling chamber at 100 N occlusal loading. Data were analyzed descriptively and recorded quantitively. Both study factors influenced the stress distribution. The mvm stress during the restorative procedure was higher for nonselective carious tissue removal without RMGIC (25.9 MPa) and lower for selective carious tissue removal associated with RMGIC (13.5 MPa). The dentin elastic modulus increased from soft carious (3.6 ± 0.3 MPa) to firm carious (5.2 ± 1.0 MPa) to hard carious (10.9 ± 1.2 MPa) to intact dentin (22.7 ± 3.0 MPa). Molars with carious lesions showed high mvm stress at the pulp ceiling (89.6 MPa) and at fragilized coronal structure remaining. Selective carious tissue removal followed by restoration using a Vitrebond liner and Tetric N-Ceram Bulk fill reduced the stress at the pulp chamber ceiling.

A comprehensive review of the antibacterial activity of dimethylaminohexadecyl methacrylate (DMAHDM) and its influence on mechanical properties of resin-based dental materials

The repetitive restorative cycle should be avoided, aiming at the smallest number of restorations' replacements to ensure greater tooth longevity. Antibacterial materials associated with the control of caries etiological factors can help improve restoration's durability. This review aimed to analyze the results of in vitro studies that added Dimethylaminohexadecyl methacrylate (DMAHDM), an antibacterial monomer, to restorative materials. The PubMed, SCOPUS, Web of Science, and Biblioteca Virtual em Saúde databases were screened for studies published between 2015 and 2020. After full-text reading, 24 articles were included in the final sample. DMAHDM has demonstrated antibacterial efficacy against several bacteria related to dental caries and periodontal diseases, causing a transition in the biofilm balance without inducing resistance. When DMAHDM was included in acrylic resin, the material cytotoxicity increased, and changes in mechanical properties were observed. In contrast, resin composites had their mechanical properties maintained in most studies; however, toxicity was not examined. The association between DMAHDM and 2-methacryloyloxyethyl phosphorylcholine or silver nanoparticles improved the antibacterial effect. Besides, the association with nanoparticles of amorphous calcium phosphate or nanoparticles of calcium fluoride can provide remineralization capacity. There is a lack of information on the cytotoxicity and bacteria resistance induction, and further studies are needed to address this.

Polymerization shrinkage stress of resin-based dental materials: A systematic review and meta-analyses of technique protocol and photo-activation strategies

PURPOSE

A systematic review was conducted to determine whether there were any alternative technique or additional step strategies available to reduce and control polymerization shrinkage stress development in dental resin-based restorative materials.

DATA SOURCES

This report followed the PRISMA Statement. A total of 36 studies were included in this review. Two reviewers performed a literature search up to December 2016, without restriction of the year of publication, in seven databases: PubMed, Web of Science, Scopus, SciELO, LILACS, IBECS, and BBO.

STUDY SELECTION

Only in vitro studies that evaluated polymerization shrinkage stress by direct testing were included. Pilot studies, reviews and in vitro studies that evaluated polymerization shrinkage stress by indirect methods (e.g., microleakage or cuspal deflection measurements), finite elemental analysis or mathematical models were excluded. Of the 6.113 eligible articles, 36 studies were included in the qualitative analysis, and the meta-analysis was performed with 25 studies. A global comparison was performed with random-effects models (α = 0.05). The strategies were subdivided as follows: the use of an alternative technique protocol of placing the material inside the tooth cavity; the modification of the irradiation intensity or total energy delivered to the material; the use of an alternative light-curing source; or the use of an alternative photo-activation mode. All alternative strategies showed statistically significant differences when compared with their respective controls (p < 0.05).

CONCLUSION

The use of alternative light-curing sources contributed more to minimizing stress development than placing the material by means of an alternative technique protocol or by modifying the irradiant intensity or total energy delivered to the material during photo-activation. Moreover, the use of an alternative photo-activation mode (intermittent light, exponential, soft-start or pulse delay modes) was shown to be an effective strategy for reducing and controlling stress development in resin-based dental materials.