The influence of varnish and high fluoride on erosion and abrasion in a laboratory investigation

Influence of fluoride characteristics on tooth surface protection in an erosive condition: A multifaceted characterization approach

OBJECTIVE

To evaluate the effect of fluoride consistency and composition to protect enamel and dentin against the dental erosion.

MATERIALS AND METHODS

Bovine enamel and dentin specimens were treated with artificial saliva, neutral fluoride gel (NFG), acidulated phosphate fluoride gel (AFG), neutral fluoride foam (NFF), and acidulated phosphate fluoride foam. The samples were subjected to cycling. Micro energy-dispersive X-ray fluorescence spectrometry, surface roughness (Ra), contact angle (CA), and scanning electron microscopy (SEM) were performed. Composition, CA and Ra data were analyzed by ANOVA and multiple comparison test (p < 0.05).

RESULTS

The dentin protected had a significantly higher mineral content than in the control. Eroded unprotected enamel had higher Ra values than normal surfaces. Fluoride treatments increased the Ra in dentin samples. AFG increased the CA in enamel. Fluoride foams increased CA in dentin with reduced mineral loss. SEM analysis found a deposited layer on enamel treated with AFG and remnants of deposits on dentin treated with NFG and NFF.

CONCLUSION

Regardless of the form of application, fluoride provided protection against erosion, however with different levels.

CLINICAL SIGNIFICANCE

Applying the adequate fluoride form is relevant since the formulations have different effects on both enamel and dentin.

Pilot clinical study to evaluate the efficacy of a professionally delivered high fluoride varnish on erosive tooth wear in an in-situ model

OBJECTIVES

The aim for this pilot study was to investigate the effect of a sodium fluoride varnish on step height measured by a profilometer from human enamel worn by healthy volunteers with a novel in situ/ex vivo erosion design.

METHOD

Healthy volunteers aged 18-70 years wore a palatal splint containing 8 human enamel samples and underwent two 3-day treatment periods for 6 h a day with a varnish containing sodium fluoride at 22,600 ppm and the control with the same ingredients but without fluoride. Each splint contained 4 polished and 4 unpolished samples. The interventions were applied to the surface of the enamel samples in randomised order, removed after 6 h, then immersed ex-vivo in 1 %, pH 2.7 citric acid for 2 min, repeated 4 times a day, over 2 days. Measurements of enamel were assessed blindly by microhardness on day 2 and by non-contact laser profilometry on day 3 for the two treatments.

RESULTS

24 volunteers, 2 males and 22 females aged 27-54 years, were screened and recruited. The delta microhardness, from polished samples removed at the end of day 2, for the control and fluoride treatment was 95.7 (22.9) kgf/mm2 and 123.7 (28.9) kgf/mm2, respectively (p < .005). The mean (SD) step height for the control polished enamel surfaces was 3.67 (2.07) µm and for the fluoride varnish was 1.79 (1.01) µm (p < .0005). The control unpolished enamel surfaces had a mean 2.09 (1.53) µm and the fluoride varnish was 2.11 (1.53) µm but no statistical difference was detected.

CONCLUSIONS

The results from this pilot study, utilizing an in-situ model where enamel was exposed to acid over the course of 2 days, demonstrated that a high fluoride varnish containing sodium fluoride at 22,600 ppm prevented erosive wear compared to a control on the polished enamel surfaces.

CLINICAL SIGNIFICANCE

Intra-oral study demonstrated that a high fluoride varnish containing sodium fluoride at 22,600 ppm reduced erosive tooth wear.

Effect of three different remineralising agents on prevention against acidic erosion of primary teeth: an in vitro study

PURPOSE

This study aimed to evaluate and compare the protective effect of fluoride varnish (Enamelast™, Ultradent Inc., Cologne, Germany), casein phosphopeptide-amorphous calcium phosphate fluoride/CPP-ACPF (MI Paste Plus, GC Corp., Tokyo, Japan) and self-assembling P11-4 peptide (Curodont™ Protect, Credentis AG, Windisch, Switzerland), against acidic erosion of primary teeth.

METHODS

Forty primary anterior teeth were randomly assigned to four groups (n = 10): group 1: control, group 2: fluoride varnish, group 3: CPP-ACPF and group 4: self-assembling P11-4 peptide. After applying remineralising agents, except for the control group, all specimens underwent an erosive challenge of carbonated soft drink and artificial saliva for 15 cycles of 6 s each at 6-h intervals for a day. Groups were compared in terms of surface microhardness, roughness readings, and surface scanning with an extra-oral scanner (D800; 3Shape A/S) before and after the erosive process.

RESULTS

All experimental groups showed superior results than the control group regarding microhardness, surface roughness, and substance loss. The fluoride varnish group showed significantly favourable results in microhardness change. There was no significant difference between the experimental groups regarding surface roughness and enamel loss measurements.

CONCLUSION

5% NaF fluoride varnish, CPP-ACPF and self-assembling P11-4 peptide protect the enamel of primary teeth against erosion compared to artificial saliva alone.

Effect of silver diamine fluoride/potassium iodide treatment on the prevention of dental erosion in primary teeth: an in vitro study

INTRODUCTION

Dental erosion has a great effect on oral health, when diagnosed it is irreversible, this sets the importance of different preventive measures being investigated against dental erosion.

AIM

This in vitro study aims to evaluate the effectiveness of silver diamine fluoride and Potassium iodide (SDF-KI) in comparison to casein phosphopeptide-amorphous calcium phosphate fluoride (CPP-ACPF) varnish, sodium fluoride (NaF) varnish, silver diamine fluoride (SDF) alone and deionized water as a control group in the prevention of dental erosion in primary teeth and assessing its staining effect.

MATERIALS AND METHODS

Forty deciduous teeth enamel specimens were randomly allocated into the five study groups. Tested materials were applied. An erosive challenge was done by immersing the specimens in a citric acid-containing soft drink with pH 2.85, for 5 min, 4 times/day, for 5 days. Changes in surface microhardness, mineral loss, and color change were evaluated besides recording of the surface topography and surface roughness for selected specimens.

RESULTS

The highest decrease in surface microhardness was recorded in the control group (-85.21 ± 10.60%), with a statistically significant difference (p = 0.002). SDF-KI group (-61.49 ± 21.08%) showed no statistically significant difference when compared to CPP-ACPF, NaF, and SDF groups. For calcium and phosphorous loss, control group was statistically significantly higher compared to the treatment groups (p = 0.003) and (p < 0.001) respectively, while there was no statistically significant difference between the tested treatment groups. The highest mean value for color change was recorded in SDF group (26.26 ± 10.31), followed by SDF-KI group (21.22 ± 12.87) with no statistically significant difference between groups.

CONCLUSIONS

SDF-KI is as effective as CPP-ACPF, NaF varnishes and SDF in the prevention of dental erosion in primary teeth, there was no statistically significant difference regarding its staining potential.

The early wear susceptibility of cementum, enamel and dentine in vitro

OBJECTIVES

To assess the differential early wear susceptibility of cementum, enamel and dentine at a micron level.

METHODS

Whole human molar buccal surfaces incorporating natural enamel and cementum (n = 20) confirmed by imaging (digital microscopy: Keyence, VHX-7000 Milton Keynes, UK), were mounted, scanned (profilometry: XYRIS 4000, Taicaan, Southampton, UK), and allocated to receive erosion (citric acid, pH 2.7, 30 min (n = 10)) or erosion/abrasion challenges (3 cycles of (citric acid, pH 2.7, 10 min, 60 300 g linear abrasion strokes), n=10). Samples were polished and the experiment repeated on polished enamel, and polished coronal and radicular dentine within the same tooth. Profilometric wear data were obtained using superimposition: GeoMagic (3Dsystems, Darmstadt, Germany) and subtraction: MountainsMap (DigitalSurf, Besancon, France). Data were normal. A general linear model was used to assess differences between groups and substrates.

RESULTS

The mean step height (SD) for natural enamel was 8.82 μm (2.53) for erosion and 11.48 μm (2.95) for erosion/abrasion. For natural cementum, the mean step height was 6.00 μm (2.29) for erosion and 4.67 μm (1.58) for erosion/abrasion. Dentine step heights ranged from 7.20 μm (1.53) for erosion and 9.79 μm (1.01) for erosion/abrasion with no statistical differences in dentine wear. Natural cementum surfaces had the lowest wear (p<0.001). Dentine had significantly less wear than natural enamel (p<0.02).

CONCLUSIONS

Cementum surfaces demonstrated the most wear resistance, followed by dentine under erosion dominant conditions in this in vitro study. Further in-vivo investigations are needed to confirm the intraoral stability of cementum.

CLINICAL SIGNIFICANCE

Cementum may be the least susceptible of dental substrates to wear and dentine does not wear at a faster rate than enamel under erosive conditions. This adds to our knowledge on the development of non-carious cervical lesions and questions whether wear rates will accelerate once dentine is exposed.

Risk factors for and prevention of caries and dental erosion in children and adolescents with asthma

There are many studies and reviews of the relationship between the asthma disease in young individuals on the one hand and caries and dental erosion on the other. The causes of caries and dental erosion might be related to the asthmatic drugs, low pH and the sweeteners that the inhaled drug contains and perhaps even the lifestyle of children and adolescents with asthma. The main focus of this review is therefore to describe various preventive strategies, based on long experience of preventive dental care in Sweden. Two fact boxes are presented, one on fluoride toothpaste as a population-based intervention for different ages and one on diet counselling in children and adolescents with asthma. The most important thing is to introduce fluoride toothpaste early in the child's life and that the parents brush the child's teeth twice a day, in the morning after breakfast and at night before bedtime, up to the age of 10. Moreover, a high-risk approach with an additional fluoride supply at home is presented, together with the application of fluoride varnish at the clinic. Regarding diet counselling, it is important to make sure that the child has regular meals during the day, maximum five to six times a day, to allow the teeth to rest between meals and restrict sweets and soft drinks to once a week. It is important to identify children and adolescents with asthma as early as possible and to refer them to a dental team for preventive treatment.

Anti-erosive profile of an experimental 5% SnCl₂ varnish containing different concentrations of NaF

Abstract This in vitro study evaluated the anti-erosive effect of an experimental varnish containing 5% stannous chloride (SnCl₂) associated with different concentrations of NaF (NaF-free, 2.5% NaF, or 5.2% NaF) on bovine enamel and root dentin. One hundred samples were pre-eroded (0.3% citric acid, pH 2.6, 10 min) and randomized into five groups (n=10 for each substrate): Negative control - milli-Q water; NaF-free - Experimental varnish SnCl₂-free and NaF-free; 2.5 NaF - Experimental varnish 5% SnCl₂ associated with 2.5% NaF; 5.2 NaF: Experimental varnish 5% SnCl₂ associated with 5.2% NaF and positive control - Commercial varnish containing 5% NaF (Duraphat). After the varnishes were applied, the erosive and abrasive challenges were carried out for five days. Loss of tooth structure (TSL) was determined by optical profilometry, and the loss of calcium (ΔCa2+) using atomic absorption spectroscopy. Dentin analysis was also performed by SEM. A one-way ANOVA/Bonferroni test was performed to analyze the data (α=0.05). The experimental 2.5 NaF and 5.2 NaF groups showed greater effectiveness in preventing TSL when compared to the other groups (p <0.05), regardless of the substrate. In addition, these groups showed lower loss in Ca2+ content when compared to the other groups (p <0.05), for enamel and dentin. Dentin showed greater TSL and ΔCa2+ loss when compared to enamel in all treatments (p <0.05). The 5.2% and 2.5% NaF-containing experimental varnishes showed promising results in both, the prevention of TSL and the loss of Ca2+, regardless of the substrate studied.

Effect of fluoride varnish on glass ionomer microhardness changes in endogenous acid erosion challenge

OBJECTIVE

This study aimed to assess the effect of fluoride varnish on glass ionomer microhardness changes after endogenous acid erosion challenge.

METHODOLOGY

In this study, 40 conventional glass ionomer (CGI; Fuji IX) and 40 resin-modified glass ionomer (RMGI; Fuji IILC) discs were fabricated and divided into 4 subgroups (n = 10) for immersion in synthetic gastric acid or saliva for 27 h with/without fluoride varnish application. The surface microhardness was measured at baseline and after immersion, and the change in microhardness was calculated. Data were analyzed using analysis of variance and T-test.

RESULTS

A reduction in microhardness was noted in all subgroups following immersion. The lowest change in microhardness of both CGI and RMGI occurred in artificial saliva. In CGI groups, the highest reduction in microhardness occurred in synthetic gastric acid with fluoride varnish application, and the reduction was significantly different from that of the CGI group with fluoride varnish application (p value = .01). In RMGI groups, the highest reduction in microhardness was noted in synthetic gastric acid without fluoride varnish application, and the reduction was significantly different from that of the other groups (p value < .05).

CONCLUSIONS

Exposure to synthetic gastric acid caused a significant reduction in microhardness of RMGI. Varnish application significantly decreased the acid susceptibility of RMGI, but not that of CGI.

Comparative Effects of CPP-ACP and Xylitol F-Varnishes on the Reduction of Tooth Erosion and Its Progression

Abstract Evaluated the effect of CPP-ACP/NaF and xylitol/NaF varnishes in reduce erosion and progression of erosion. Forty enamel blocks were divided into four groups (n=10): G1=CPP-ACP/NaF varnish (MI varnishTM); G2=xylitol/NaF varnish (Profluorid®); G3=NaF varnish (Duraphat®, positive control) and G4=deionized water (MilliQ®, negative control). Samples were immersed in Sprite ZeroTM (pH 2.58, 4x/day, 3 days), in between immersions, the specimens stayed in artificial saliva. After 3 days of erosion, the eroded area was divided in two (half of one received an additional varnish layer while the other half repeated the same 3-day erosion cycle). The 3D, non-contact profilometry technique was used to determinate tooth structure loss (TSL) and surface roughness (SR). Scanning electron microscopy (SEM) and 3D images were utilized to evaluate the topography of the samples. Mann-Whitney, one-way ANOVA and Tukey tests were used (significance level of 0.05%). SEM and 3D images were descriptively evaluated. After 3 or 6 days of erosion, all tested varnishes were better than G4 (p<0.05) for TSL and SR. In addition, G1 had lower values for TSL than G3 (p<0.05) after 3 days of erosion. Under SEM and 3D images observation, all groups presented porosity, irregularities and depressions on the surface enamel after 3 and 6 days of erosion, more pronounced in G4. An application of topical NaF varnishes was effective in reducing TSL and enamel roughness after erosion challenges, being the CCP-ACP/NaF varnish more effective than NaF varnish and water after 3 days of erosion.

Effect of the usage of Er,Cr:YSGG laser with and without different remineralization agents on the enamel erosion of primary teeth

The aim of the present study was to evaluate the effects of different remineralization agents associated with erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) (0.5 W power, 20 Hz frequency, 60% water, 40% air, 25 mJ pulse energy, 8.84 J/cm² fluence, 60 μs pulse duration, 600 μm tip diameter, and an approximate 1-1.5 mm distance to the target) laser irradiation on erosion induced by the consumption of carbonated drinks in human primary enamel. There were 8 groups and 10 primary teeth in each g0roup. The distribution was as follows: group 1, casein phosphopeptide-amorphous calcium phosphate with fluoride (CPP-ACPF); group 2, Er,Cr:YSGG laser+CPP-ACPF; group 3, fluor varnish; group 4, Er,Cr:YSGG Laser+fluoride varnish; group 5, ROCS® medical mineral gel; group 6, Er,Cr:YSGG laser + ROCS® medical mineral gel; group 7, Er,Cr:YSGG laser; and group 8, artificial saliva. The samples in the groups were submerged in artificial saliva and acid twice a day for 6 s at 6-h intervals and were then exposed to an erosion cycle 15 times. In the groups in which the Er,Cr:YSGG laser was applied in combination with the remineralization agents, the laser application was made first, and then the remineralization agents were applied for 4 min in each group. The Friedman and Wilcoxon signed-rank tests and the Bonferroni correction were used in statistical analyses, and the significance level was taken as p < 0.05. According to the results, all agents had a statistically significant difference (groups 1, 2, 3, 4, and 6: p = 0.005, p < 0.017; groups 5 and 7: p = 0.007, p < 0.017) between BL-RM periods. However, all agents had a statistically significant remineralization effect on primary teeth enamel (groups 1, 2, 3, 6, and 7: p = 0.005, p < 0.017; group 4: p = 0.011, p < 0.017) except that group 5 (p = 0.074, p < 0.017) between DM-RM periods. The coadministration of an agent with the laser did not make any difference at a statistical level (p = 0.804, p > 0.05). The results were supported by scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. As a result of this study, CPP-ACPF had a notable impact in terms of the remineralization effect on eroded enamel, and the Er,Cr:YSGG laser alone may be an alternative method, which may be related to the modified hydroxyapatite structure, 38.5% H_0.56Ca_4.56O₁₃P₃Y_0.44, that was determined in XRD analysis.

Protective Effect of Fluoride Varnish Containing Trimetaphosphate against Dentin Erosion and Erosion/Abrasion: An in vitro Study

This in vitro study evaluated the protective effect of fluoride varnishes containing sodium trimetaphosphate (TMP) against dentin erosion and abrasion. Specimens of coronal dentin were divided into: placebo, 2.5% NaF, 5% NaF, 2.5% NaF + 5% TMP, and 5% NaF + 5% TMP groups (n =24/group). After single application of the varnishes, the samples were immersed in citric acid (0.05 mol/L, pH = 3.2, 5 min) followed or not by brushing, and the dentin wear was assessed after 5 days. Varnishes containing fluoride + TMP led to the lowest wear. TMP varnishes showed a superior effect against dentin erosive wear.

Effect of Calcium-phosphate Desensitizers on Staining Susceptibility of Acid-eroded Enamel

OBJECTIVE

To investigate the effect of calcium-phosphate-based desensitizers, Teethmate AP paste (TMAP) and Teethmate Desensitizer (TMD) (Kuraray Noritake Dental, Tokyo, Japan), on the prevention of staining on acid-eroded enamel.

METHODS AND MATERIALS

Forty polished enamel samples (4×4×1 mm) from bovine incisors were randomly divided into five groups (n=8). After immersion in 50 mL of 0.5% citric acid (pH 2.5) for 15 minutes to form acid-eroded surfaces, the surfaces were subjected to different treatments with TMAP, TMD, and NaF (0.21% means 950 ppm) for five minutes. Another eroded group was not treated with desensitizer. For the control group, the samples were not eroded or treated. All the samples were stored in artificial saliva (AS) at pH 7.2 for 24 hours at 37°C. The TMAP, TMD, or NaF was reapplied at eight and 16 hours during the 24 hours of storage time. The surface roughness (Sa) was evaluated following ISO 25178 for surface texture using confocal laser scanning microscopy (VK-X 150 series, Keyence, Osaka, Japan) before acid erosion, after acid erosion, and after 24 hours of incubation in AS. Afterward, the color difference was measured with a dental colorimeter (Shade Eye NCC, Shofu, Kyoto, Japan) before and after staining with tea solution.

RESULTS

One-way repeated measures analysis of variance showed that acid erosion significantly increased Sa (p<0.001). TMAP- and TMD-treated groups exhibited lower Sa values than the NaF group and the no-desensitizer treatment group. The greatest staining was observed in the NaF group and the no-desensitizer group, while the TMAP and TMD groups significantly decreased the formation of stains.

CONCLUSIONS

Acid-eroded enamel increased surface roughness and tended to absorb more stains. However, the application of TMAP and TMD moderated the roughness and thus prevented the formation of extrinsic stains.

TiF4 varnish protects the retention of brackets to enamel after in vitro mild erosive challenge

The effect of fluoride agents on the retention of orthodontic brackets to enamel under erosive challenge is little investigated. The aim of this study was to evaluate the effect of titanium tetrafluoride (TiF4) and sodium fluoride (NaF) agents on the shear bond strength of brackets to enamel and on the enamel microhardness around brackets under erosive challenge. Brackets were bonded to bovine incisors. Five groups were formed according to fluoride application (n=10): TiF4 varnish, TiF4 solution, NaF varnish, NaF solution and control (without application). The specimens were submitted to erosive challenge (90 s cola drink/2h artificial saliva, 4x per day for 7 days). Solutions were applied before each erosive cycle and varnishes were applied once. Vickers Microhardness (VHN) was obtained before and after all cycles of erosion and the percentage of microhardness loss was calculated. Shear bond strength, adhesive remnant index and polarized light microscopy were conducted after erosion. The data were analyzed by ANOVA, Tukey, Kruskal-Wallis and Mann-Whitney U tests (α=0.05). The %VHN had no statistically significant differences among the experimental groups. However, considering the comparisons of all groups with the control group, TiF4 varnish showed the highest protection from enamel demineralization (effect size of 2.94, while the effect size for the other groups was >2.4). The TiF4 varnish group had significantly higher shear bond strength compared to other groups. There was no difference among groups for adhesive remnant index. Polarized light microscopy showed higher demineralization depth for the control group. Application of NaF and TiF4 agents during mild erosive challenge minimized the enamel mineral loss around brackets, however only the experimental TiF4 varnish was able to prevent the reduction of shear bond strength of brackets to enamel.

In vitro quantitative comparison of erosive potential of infant mouthwashes on glass ionomer cement

Background

The widespread use of mouthwashes, specially in children, is a concern, since the long-term use may modify the topography of dental materials. However, this process still unclear regarding the wear related to infant mouthwashes on glass ionomer cement. Thus, the purpose of this investigation was evaluate the erosive potential of infant mouthwashes on glass ionomer cement specimens.

Material and Methods

Forty round-shaped specimens were divided into 4 groups (N=10) and submitted to erosive cycling for 15 days, being exposed 2X/day in the following children’s active agents mouthwash solutions: G1- cetylpyridinium chloride, G2- xylitol and triclosan and G3 - Malva sylvestris and xylitol. Prior to cycling, the specimens were submitted to the surface roughness measurement. After erosive cycling, the specimens were reanalyzed, and calculated the increase of roughness (∆Ra). Additionally, it was adopted distilled water as a negative control (G4). As an extra analysis, the mouthwashes had their pH values measured. The results were submitted to T-test and ANOVA followed by Tukey test at 5%.

Results

In relation to pH values, G2 presented the most acidic pH value (pH = 6.83) in comparison to other substances. Regarding the comparison of the final roughness values (R) among the groups, it was verified that the mouthwashes showed significant roughness increase in comparison to control group, especially to G3 group (Rf = 1.67 ± 0.14) as well the ΔRa values with statistical difference in comparison to distilled water. Still, with exception of control group outcome, an increase of roughness of each mouthwash was verified after the studied period.

Conclusions

Active agents present in infant mouthwashes were capable of roughness increased of glass ionomer cement surface, demonstrating an erosive potential of this material largely used in pediatric dentistry.

Key words:Dental erosion, dental cements, mouthwash.

Measurement of surface roughness changes of unpolished and polished enamel following erosion

Objectives

To determine if Sa roughness data from measuring one central location of unpolished and polished enamel were representative of the overall surfaces before and after erosion.

Methods

Twenty human enamel sections (4x4 mm) were embedded in bis-acryl composite and randomised to either a native or polishing enamel preparation protocol. Enamel samples were subjected to an acid challenge (15 minutes 100 mL orange juice, pH 3.2, titratable acidity 41.3mmol OH/L, 62.5 rpm agitation, repeated for three cycles). Median (IQR) surface roughness [Sa] was measured at baseline and after erosion from both a centralised cluster and four peripheral clusters. Within each cluster, five smaller areas (0.04 mm²) provided the Sa roughness data.

Results

For both unpolished and polished enamel samples there were no significant differences between measuring one central cluster or four peripheral clusters, before and after erosion. For unpolished enamel the single central cluster had a median (IQR) Sa roughness of 1.45 (2.58) μm and the four peripheral clusters had a median (IQR) of 1.32 (4.86) μm before erosion; after erosion there were statistically significant reductions to 0.38 (0.35) μm and 0.34 (0.49) μm respectively (p<0.0001). Polished enamel had a median (IQR) Sa roughness 0.04 (0.17) μm for the single central cluster and 0.05 (0.15) μm for the four peripheral clusters which statistically significantly increased after erosion to 0.27 (0.08) μm for both (p<0.0001).

Conclusion

Measuring one central cluster of unpolished and polished enamel was representative of the overall enamel surface roughness, before and after erosion.

Fluoride Varnishes against Dental Erosion Caused by Soft Drink Combined with Pediatric Liquid Medicine

Abstract The present study evaluated the effect of NaF and CPP-ACP/NaF varnishes to reduce erosion produced by soft drink (SD) combined or not with pediatric liquid medicine. Enamel specimens were pre-treated with fluoride varnish, according to the following groups: NaF varnish (Duraphat®) or CPP-ACP/NaF varnish (MI varnishTM). Two types of erosive cycles were made: by soft drink erosion (SDE) or by pediatric liquid medicine plus soft drink erosion (PLM/SDE). Bovine enamel specimens were randomly assigned in six groups (n=10): G1=NaF + SDE; G2=CPP-ACP/NaF + SDE; G3=Distilled and deionized (DD) water + SDE; G4=NaF + PLM/SDE; G5=CPP-ACP/NaF + PLM/SDE and G6=DD water + PLM/SDE. Before treatments, the sample surface was divided in two areas (unexposed area-UA and exposed area-EA). The specimens were evaluated by 3D non-contact profilometry technique to determinate tooth structure loss (TSL) and surface roughness (Sa). Scanning electron microscopy (SEM) analysis was also performed. After SDE, G2 presented the lowest TSL values compared to G3 (p=0.008). G1 and G2 did not differ between them (p=0.203) and no groups differed among them despite Sa. Regarding TSL and Sa, G4 and G5 differed from G6 (p=0.0001), but not between them (p=1.00). Examining 3D and SEM images, the greatest differences between UA and EA were observed for G3 and G6. CPP-ACP/NaF varnish seems to be a promising treatment to reduce enamel loss from the erosion produced by a soft drink. Both varnishes also showed capacity to reduce TSL and Sa after erosion by soft drink combined to pediatric liquid medicine.

Toothbrush abrasivity in a long-term simulation on human dentin depends on brushing mode and bristle arrangement

Objective

The aim of this study was to evaluate the susceptibility of dentin to brushing abrasion using four different toothbrushes (rotating-oscillating, sonic and two types of manual toothbrushes) with the same brushing forces.

Methods

Dentin samples (n = 72) were selected from 72 impacted third molars. Half of the surface of dentin samples was covered with an adhesive tape, creating a protected and a freely exposed area in the same specimen. Brushing was performed with either a: sonic (Sonicare PowerUp, Philips GmbH, Hamburg, Germany), b: oscillating-rotating (Oral B Vitality Precisions Clean, Procter & Gamble, Schwalbach am Taunus, Germany) or two different manual toothbrushes c: flat trim brush head toothbrush (Dr. Best: Original, Glaxo-Smith-Kline, Bühl, Germany) and d: rippled-shaped brush head toothbrush (Blend-a-Dent, Complete V-Interdental, Blend-a-med, Schwalbach, Germany) in a custom made automatic brushing machine. The brushing force was set to 2 N and a whitening toothpaste (RDA = 150) was used. The simulation period was performed over a calculated period to mimic a brushing behavior of two times a day brushing for eight years and six months. Dentin loss was quantitatively determined by profilometry and statistically analyzed by Wilcoxon and Mann-Whitney-U Test (p < 0.05).

Results

The mean (standard deviation) surface loss was 21.03 (±1.26) μm for the sonic toothbrush, 15.71 (±0.85) μm for the oscillating-rotating toothbrush, 6.13 (±1.24) μm for the manual toothbrush with flat trim brush head and 2.50 (±0.43) μm for the manual toothbrush with rippled-shaped brush head. Differences between all groups were statistically significant at p<0.05.

Conclusion

Using the same brushing force and a highly abrasive toothpaste, manual toothbrushes are significantly less abrasive compared to power toothbrushes for an 8.5—year simulation.

Dentin Protection of Different Desensitizing Varnishes During Stress Simulation: An In Vitro Study

OBJECTIVE

The aim of this study was to investigate dentin protection of different desensitizing varnishes (light- and self-curing) during acid action/abrasion stress and thermocyclic loading in vitro.

METHODS

Dentin discs of 2 mm thickness were cut from 120 human molars, embedded, and polished. Specimens were randomized into five groups (n=24): A, negative control; B, Gluma Desensitizer; C, Cervitec plus (self-curing); D, Seal&Protect; and E, Admira Protect (light-curing). In groups B-E, varnish was applied on two-thirds of the dentin surface, and one-third acted as internal control. Stress cycle (2 cycles/day) for specimens were as follows: 1, acid action (pH: 2.9: five minutes); 2, remineralization (synthetic saliva: 60 minutes); 3, brushing (100 strokes); 4, thermocycling (five cycles); and 5, remineralization (synthetic saliva: six hours) for each group (n=12) for 30 (15 days) or 60 times (30 days). Specimens were analyzed using an incident light microscope. Substance loss was measured in micrometers. Statistical analysis was performed with the multiple contrast test (p<0.05).

RESULTS

Groups B and C had a significantly lower dentin loss than A (p<0.01). After 30 days, group A showed the highest dentin loss (p<0.01), whereas the other groups lacked a significant difference regarding their substance loss (dentin and/or varnish; p>0.05). Varnish layer loss was shown for groups D and E with a remaining protective layer; groups A-C showed dentin removal.

CONCLUSION

All four varnishes are protective compared with an untreated control. Light-curing varnishes might provide higher dentin protection than self-curing materials.

Effect of a Single Application of TiF4 Varnish versus Daily Use of a Low-Concentrated TiF4/NaF Solution on Tooth Erosion Prevention in vitro

This study investigated the isolated and combined effect of a single application of TiF4 or NaF varnish versus daily use of a solution containing a low concentration of TiF4/NaF against tooth erosion in vitro. A total of 90 bovine enamel and 108 root dentin samples were treated as follows: control (no treatment), solution containing TiF4/NaF (500 ppm F-, pH 4.4), NaF varnish (24,500 ppm F-, pH 5.0), TiF4 varnish (24,500 ppm F-, pH 1.0), TiF4 varnish + solution, and NaF varnish + solution. The erosive challenges were performed 4 × 90s/day (0.1% citric acid, pH 2.5) and, between them, the samples were immersed in artificial saliva. The tooth loss was measured using contact profilometry (after 7 days for dentin and after 7, 10, and 14 days for enamel). All treatments were effective in reducing tooth loss, except NaF varnish for enamel on day 7 (p < 0.0001). TiF4/NaF solution and TiF4 varnish did not differ with respect to enamel loss for 10 days; thereafter, TiF4 varnish lost its protective effect compared to TiF4/NaF solution. The combination of vehicles was more effective in reducing enamel loss than both varnishes on their own but not compared to the solution. For dentin, TiF4 varnish was more effective than NaF varnish, while TiF4/NaF solution and NaF varnish were similar. The combination of vehicles improved the protective effect only when compared to NaF varnish on its own (p < 0.0001). Both types of TiF4 applications, isolated or combined, were effective against tooth erosion, but some differences in their performance were seen between enamel and dentin.

Influence of Bristle Stiffness of Manual Toothbrushes on Eroded and Sound Human Dentin--An In Vitro Study

Aim

The aim of this study was to determine the influence of manual toothbrushes with different bristle stiffness on the abrasivity on eroded and sound human dentin.

Materials and Methods

Dentin specimens were made from impacted third molars and attributed to three groups: erosion-abrasion (EA), abrasion (A) and erosion (E). The specimens from EA and E were treated with 1% citric acid (pH 2.3) for 1 min rinsed, and neutralized with artificial saliva for 15 min. This cycle was repeated five times. Thereafter, specimens from EA and A were treated with three toothbrushes types with different bristle stiffness (soft, medium, and hard) in a custom-made toothbrushing machine. The brushing was performed at a load of 3 N with a toothpaste slurry for 630 s. This procedure was repeated five times, in group EA after each erosion cycle. EA and A groups passed through five cycles with a total of 6300 strokes. The abrasivity was analyzed by contact-free profilometry. Kruskal-Wallis and Mann-Whitney U tests were performed for statistical analysis.

Results

With respect to bristle stiffness there was no statistically significant difference in dentin loss within the EA group. In group A, a statistically significantly higher dentin loss was found for the soft in comparison to the hard bristles. No statistically significant differences were measured between soft/medium and medium/hard toothbrushes. The amount of dentin loss from specimens in the EA group was significantly higher than in the A group.

Conclusions

Within the limitations of this study, the dentin loss in the Abrasion group was higher with soft bristles than with hard ones. This result might have an influence on the toothbrush recommendations for patients with non-carious cervical lesions.

Three-dimensional in vitro measurements of tooth wear using fluoridated dentifrices

BACKGROUND

The aim of this study was to compare differences in wear of human enamel and dentine in vitro using a 3D measurement method comparing silica versus non-silica containing fluoridated dentifrices (Colgate Total(™) [CT] or Fluor Protector Gel(™) [FPG]).

METHODS

Mounted native enamel (n = 36) and polished dentine (n = 36) samples were subjected to 10 wear cycles. Each cycle consisted of: (1) 1 hour remineralization in artificial saliva (AS); (2) 10 minute erosion (0.3% citric acid; pH = 2.8); (3) 2 minute toothbrush abrasion in AS (G1, control) or a slurry of 3:1 by weight of AS:dentifrice (G2 = CT; G3 = FPG) under a load of 2 N. Each group contained 12 enamel and 12 dentine samples. Paired pre- and post-wear scans made with a contacting scanner were digitally superimposed using ball bearings as datum.

RESULTS

Mean and (SD) enamel wear was G1 = 21.9 μm (6.4); G2 = 15.2 μm (2.8); G3 = 16.9 μm (3.2). Enamel wear was not different between dentifrices (p = 0.99). Both dentifrices resulted in less enamel wear compared to the control (p < 0.05). Dentine wear was G1 = 41.3 μm (8.1); G2 = 29.1 μm (4.4); G3 = 22.1 μm (3.5). Differences in measurements were observed between dentifrices and control (p < 0.05) and between dentifrices (p = 0.014) with FPG showing less dentine wear than CT.

CONCLUSIONS

FPG offered protection against erosive/abrasive tooth wear in dentine compared to CT. FPG did not offer such protective effect on enamel wear.