Bone heating and implant removal using a high-frequency electrosurgical device: An in vivo experimental study

The effects of collagen cross-link deficiency on osseointegration process of pure titanium implants

PURPOSE

This study aimed to investigate the effect of collagen cross-link deficiency on collagen fiber formation around an implant and its effect on the osseointegration process.

METHODS

Wistar rats were fed 0.1% beta-aminopropionitrile (BAPN) dissolved in water to induce collagen cross-link deficiency. Custom-made mini-implants with machined surfaces were placed proximal to the tibia. At 1, 2, and 4 weeks postoperatively, the bone area around the implant, bone-implant contact ratio, osteoclast/osteocyte activity, and osseointegration strength were evaluated using histological and immunohistochemical analyses and biomechanical tests.

RESULTS

Long-term disturbance of collagen cross-link formation in the BAPN group resulted in faster collagen fiber maturation than that in controls, with a defective collagen structure, low bone formation quantity, and low bone-implant contact values. Deficiency of collagen cross-links resulted in increased bone resorption and decreased osteocyte activity.

CONCLUSIONS

Collagen cross-linking is important for the formation of the collagen matrix, and their deficiency may impair bone activity around implants, affecting the osseointegration process.

Non-Destructive Removal of Dental Implant by Using the Cryogenic Method

Background and Objectives: The gold standard for a successful prosthetic approach is the osseointegration of an implant. However, this integration can be a problem in cases where the implant needs to be removed. Removing the implant with minimal damage to the surrounding tissues is important. Osteocytes cannot survive below −2 °C, but epithelial cells, fibroblasts, and other surrounding tissue cells can. Remodeling can be triggered by cryotherapy at temperatures that specifically affect osteocyte necrosis. In this study, we aimed to develop a method for reversing the osseointegration mechanism and for protecting the surrounding tissues by bone remodeling induced by CO2 cryotherapy. Materials and Methods: In this study, eight 2.8 mm diameter, one-piece mini implants were used in New Zealand rabbit tibias. Two control and six implants were tested in this study. After 2 months of osseointegration, a reverse torque force method was used to remove all osseointegrated implants at 5, 10, 20, and 30 Ncm. The osseointegration of the implants was proven by periotest measurements. Changes in bone tissue were examined in histological sections stained with toluidine blue after rabbit sacrifice. The number of lacunae with osteocyte, empty lacunae, and lacunae greater than 5 µm and the osteon number in a 10,000 µm2 area were calculated. Cryotherapy was applied to the test implants for 1 min, 2 min, and 5 min. Three implants were subjected to cryotherapy at −40 °C, and the other implants were subjected to cryotherapy at −80 °C. Results: Empty lacunae, filled osteocytes, lacunae >5 µm, and the osteon count around the implant applied at −40 °C were not significantly different from the control implants. The application of −40 °C for 1 min was found to cause minimal damage to the bone cells. The implants, which were applied for 1 min and 2 min, were successfully explanted on the 2nd day with the 5 Ncm reverse torque method. Test implants, which were applied cold for 5 min, were explanted on day 1. Tissue damage was detected in all test groups at −80 °C. Conclusions: The method of removing implants with cryotherapy was found to be successful in −40 °C freeze−thaw cycles applied three times for 1 min. To prove implant removal with cryotherapy, more implant trials should be conducted.

Evaluation of Implant Stability and Trephination Depth for Implant Removal-An In Vitro Study

Malpositioned and broken implants are usually fully osseointegrated; hence, their removal, especially from the lower arch, can be very challenging. Implant removal techniques include reverse torque and trephination. Trephination is an invasive technique that can jeopardize vital structures, cause mandibular fatigue fractures, or lead to osteomyelitis. In this study, we aimed to assess the relationship between trephination depth and implant stability by recording implant stability quotient (ISQ) readings at varying trephination depths in vitro. Materials and methods: Forty-eight implants were inserted into dense synthetic polyurethane foam blocks as artificial bone. Primary implant stability was measured with a Penguin resonance frequency analysis (RFA) device. Implants of two designs with a diameter of 3.75 mm and a length of 13 or 8 mm were inserted. Twenty-four internal hexagon (IH) (Seven®) and twenty-four conical connection (CC) implants (C1®; MIS® Implants, Ltd., Misgav, Israel) were used. The primary implant stability was measured with the RFA device. Trephination was performed, and implant stability was recorded at depths of 0, 3, and 6 mm for the 8 mm implants and 0, 3, 6, 8, 10, and 11.5 mm for the 13 mm implants. Results: Linear regression revealed a significant relation between the trephination depth and the ISQ (F (1, 213) = 1113.192, p < 0.001, adjusted r2 = 0.839). The trephination depth significantly predicted the ISQ (β = −5.337, p < 0.001), and the ISQ decreased by −5.33 as the trephination depth increased by 1 mm. Conclusion: Implant stability reduction as measured using an RFA device during trephination may be a valuable guide to achieving safe reverse torque for implant removal. Further studies are needed to evaluate these data in clinical settings.