Inhibition of enamel demineralization and bond-strength properties of bioactive glass containing 4-META/MMA-TBB-based resin adhesive

Investigation of mechanical properties, remineralization, antibacterial effect, and cellular toxicity of composite orthodontic adhesive combined with silver-containing nanostructured bioactive glass

BACKGROUND

The formation of white spots, which represent early carious lesions, is a major issue with fixed orthodontics. The addition of remineralizing agents to orthodontic adhesives may prevent the formation of white spots. The aim of this study was to produce a composite orthodontic adhesive combined with nano-bioactive glass-silver (nBG@Ag) for bracket bonding to enamel and to investigate its cytotoxicity, antimicrobial activity, remineralization capability, and bond strength.

METHODS

nBG@Ag was synthesized using the sol-gel method, and characterized using transmission electron microscopy (TEM), X-ray diffraction (XRD), and Fourier-transform infrared spectroscopy with an attenuated total reflectance attachment (ATR-FTIR). The cytotoxicity test (MTT) and antimicrobial activity of adhesives containing 1%, 3%, and 5% (wt/wt) nBG@Ag were evaluated, and the shear bond strength of the adhesives was measured using a universal testing machine. Remineralization was assessed through microhardness testing with a Vickers microhardness tester and scanning electron microscopy (SEM). Statistical analyses were conducted using the Shapiro-Wilk test, Levene test, one-way ANOVA, Robust-Welch test, Tukey HSD method, and two-way ANOVA.

RESULTS

The biocompatibility of the adhesives was found to be high, as confirmed by the lack of significant differences in the cytotoxicity between the sample and control groups. Discs made from composites containing nBG@Ag exhibited a significant reduction in the growth of Streptococcus mutans (p < 0.05), and the antibacterial activity increased with higher percentages of nBG@Ag. The shear bond strength of the adhesives decreased significantly (p < 0.001) after the addition of nanoparticles, but it remained above the recommended value. The addition of nBG@Ag showed improvement in the microhardness of the teeth, although the differences in microhardness between the study groups were not statistically significant. The formation of hydroxyapatite deposits on the tooth surface was confirmed through SEM and energy-dispersive X-ray spectroscopy (EDX).

CONCLUSION

Adding nBG@Ag to orthodontic adhesives can be an effective approach to enhance antimicrobial activity and reduce enamel demineralization around the orthodontic brackets, without compromising biocompatibility and bond strength.

The formation of cariogenic plaque to contemporary adhesive restorative materials: an in vitro study

The research exploiting the ability of dental materials to induce or prevent secondary caries (SC) development still seems inconclusive. Controlling bacterial adhesion by releasing bacteriostatic ions and improving the surface structure has been suggested to reduce the occurrence of SC. This paper analyses the impact of five distinctively composed dental materials on cariogenic biofilm formation. Forty-five specimens of three composites (CeramX Spectra ST, Admira Fusion, Beautifil II) and two glass-ionomers (Fuji II LC, Caredyne Restore), respectively, were incubated in bacterial suspension composed of Streptococcus mutans, Lactobacillus acidophilus, Streptococcus mitis, Streptococcus sanguinis, and Streptococcus salivarius at pH 7.0 and 5.5. Coverslips were used as a control. Adhered bacteria were collected after 2, 4, 6, 12, 24, and 48 h and analyzed using quantitative polymerase chain reaction (qPCR). Fluoride leakage was measured at each collection. The specimens' surface topography was assessed using interferometry. In the present study, surface roughness seemed to have a partial role in bacterial adhesion and biofilm formation, together with chemical composition of the materials tested. Despite differences in fluoride leakage, biofilm accumulation was similar across materials, but the number of adhered bacteria differed significantly. A release of other ions may also affect adhesion. These variations suggest that certain materials may be more prone to initiating secondary caries.

POSS hybrid bioactive glass dental composite resin materials: Synthesis and analysis

INTRODUCTION

This study create a dental composite by hybirding polyhedral oligo-sesquioxide nano monomers and bioactive glass BG 45S5.

METHODS

Make an experimental composite resin material with a 60 % filler content overall by substituting 20 % of the filler with BG 45S5. The experimental resins are grouped and named P0, P2, P4, P6 and P8 based on the reactive nanomonomer methacrylic acid-based multifaceted oligomeric sesquisiloxane (POSS) added by 2 %-8 % in the resin matrix portion of each group. Utilize a universal testing machine to analyze and compare the mechanical properties of these, then perform Fourier infrared spectrum analysis, double bond conversion analysis, and scanning electron microscope analysis. Based on this, after soaking the experimental materials artificial saliva solution or lactic acid solution for a while, the pH changes of the solution, the release of Ca2+ and PO43- ions, and the precipitation of apatite on the resin material's surface were tested and analyzed. Cell viability tests were used to assess sample cell viability and quantify the cytotoxicity of biological cells. The independent sample t-test was used to examine the group comparisons, and a difference was considered statistically significant at P<0.05.

RESULTS

Outstanding mechanical and the double bond conversion are demonstrated by the nanocomposites when the POSS concentration hits 4 wt%. Agglomeration will cause the performance to deteriorate if the concentration beyond this threshold. In the P4 group, the double bond conversion, CS, and FS rose by a large margin, respectively, in comparison to the blank control group P0. Thankfully, the data demonstrate that adding POSS increases adhesive ability when compared to the blank group P0, however, there is no discernible difference between the other experimental groups. The acid neutralization capacity of the P4 group is essentially the same as that of the control group (P0). Ca2+ and PO43- ions are released in significant amounts following treatment with lactic acid solution, although this tendency is clearly less pronounced in artificial saliva. SEM and EDX data indicate that when the experimental resin is soaked in lactic acid solution and artificial saliva, apatite precipitation will happen on its surface. The results of the cell viability test indicated that there was no statistically significant difference between the experimental groups, and the viability of the cells increased after 24hours and 48 hours.

CONCLUSIONS

POSS was included into the composite resin along with 20% bioactive glass as a filler. When the proportion of POSS is less than 4%, the indices of composite resin materials rise in a dose-dependent way. When this value is surpassed, performance begins to deteriorate. The inclusion of POSS has no influence on the biological activity of the composites, which means that the hybrid composite resin is capable of acid neutralization, ion release, and apatite precipitation.

CLINICAL SIGNIFICANCE

The experimental composite resin can be used as an intelligent material in clinical treatment. It has the clinical application potential of preventing demineralization of tooth hard tissue, promoting remineralization, and improving edge sealing through apatite precipitation.

In vitro evaluation of a novel fluoride-coated clear aligner with antibacterial and enamel remineralization abilities

OBJECTIVE

To investigate the antibacterial and enamel remineralization performances as well as physicochemical properties and biocompatibility of a fluoride-coated clear aligner plastic (FCAP).

MATERIALS AND METHODS

FCAP and normal clear aligner plastic (CAP) was bought from the manufacturer (Angelalign Technology Inc, China). The FCAP was observed under scanning electron microscopy. Its element composition, resistance to separation, contact angle, and protein adhesion performance were characterized. Colony-forming unit (CFU) count and 3-(4,5)-dimethylthiazol(-z-y1)-3,5-diphenyltetrazolium bromide (MTT) assay were used to evaluate the antibacterial ability of Streptococcus mutans. Fluoride release-recharge patterns were obtained. Apatite formation was evaluated after immersing FCAP in artificial saliva. Enamel remineralization capability was evaluated in the demineralization model (immersing samples in demineralization solution for 36 h) and pH cycling model (immersing samples in demineralization solution and remineralization solution in turns for 14 days). Cell Counting Kit-8 (CCK-8) and live/dead cell staining kits were used for cytotoxicity assay.

RESULTS

The FCAP showed uniformly distributed fluoride and did not compromise protein adhesion performance. CFU count (5.47 ± 0.55 for CAP, 3.63 ± 0.38 for FCAP) and MTT assay (0.41 ± 0.025 for CAP, 0.28 ± 0.038) indicated that the FCAP had stronger antibacterial activity compared with normal CAP (P < 0.05 for both evaluations). The FCAP could release fluoride continuously for 14 days and could be recharged after immersing in NaF solution. The FCAP could induce the formation of hydroxyapatite in artificial saliva and could reduce the microhardness decrease, color change, and mineral loss of enamels in both two models (P < 0.05 for all evaluations). CCK-8 and live/dead cell staining analyses showed that the coating did not compromise the biocompatibility of the clear aligner (P > 0.05 for CCK-8 evaluation).

CONCLUSIONS

The FCAP had antibacterial, fluoride recharge, and enamel remineralization abilities while it did not compromise physicochemical properties and biocompatibility.

CLINICAL RELEVANCE

The FCAP has the potential to prevent enamel demineralization during clear aligner treatment.

Inorganic Compounds as Remineralizing Fillers in Dental Restorative Materials: Narrative Review

Secondary caries is one of the leading causes of resin-based dental restoration failure. It is initiated at the interface of an existing restoration and the restored tooth surface. It is mainly caused by an imbalance between two processes of mineral loss (demineralization) and mineral gain (remineralization). A plethora of evidence has explored incorporating several bioactive compounds into resin-based materials to prevent bacterial biofilm attachment and the onset of the disease. In this review, the most recent advances in the design of remineralizing compounds and their functionalization to different resin-based materials' formulations were overviewed. Inorganic compounds, such as nano-sized amorphous calcium phosphate (NACP), calcium fluoride (CaF₂), bioactive glass (BAG), hydroxyapatite (HA), fluorapatite (FA), and boron nitride (BN), displayed promising results concerning remineralization, and direct and indirect impact on biofilm growth. The effects of these compounds varied based on these compounds' structure, the incorporated amount or percentage, and the intended clinical application. The remineralizing effects were presented as direct effects, such as an increase in the mineral content of the dental tissue, or indirect effects, such as an increase in the pH around the material. In some of the reported investigations, inorganic remineralizing compounds were combined with other bioactive agents, such as quaternary ammonium compounds (QACs), to maximize the remineralization outcomes and the antibacterial action against the cariogenic biofilms. The reviewed literature was mainly based on laboratory studies, highlighting the need to shift more toward testing the performance of these remineralizing compounds in clinical settings.

Effect of Dentin Desensitizer Containing Novel Bioactive Glass on the Permeability of Dentin

The objective of this study was to evaluate the effect of novel bioactive glass (BAG)-containing desensitizers on the permeability of dentin. Experimental dentin desensitizers containing 3 wt% BAG with or without acidic functional monomers (10-MDP or 4-META) were prepared. A commercial desensitizer, Seal & Protect (SNP), was used as a control. To evaluate the permeability of dentin, real-time dentinal fluid flow (DFF) rates were measured at four different time points (demineralized, immediately after desensitizer application, after two weeks in simulated body fluid (SBF), and post-ultrasonication). The DFF reduction rate (ΔDFF) was also calculated. The surface changes were analyzed using field emission scanning electron microscopy (FE-SEM). Raman spectroscopy was performed to analyze chemical changes on the dentin surface. The ΔDFF of the desensitizers containing BAG, BAG with 10-MDP, and BAG with 4-META significantly increased after two weeks of SBF storage and post-ultrasonication compared to the SNP at each time point (p < 0.05). Multiple precipitates were observed on the surfaces of the three BAG-containing desensitizers. Raman spectroscopy revealed hydroxyapatite (HAp) peaks on the dentin surfaces treated with the three BAG-containing desensitizers. Novel BAG-containing dentin desensitizers can reduce the DFF rate about 70.84 to 77.09% in the aspect of reduction of DFF through the HAp precipitations after two weeks of SBF storage.

Effect of Novel Bioactive Glass-Containing Dentin Adhesive on the Permeability of Demineralized Dentin

This study aimed to evaluate the effect of a novel bioactive glass (BAG)-containing dentin adhesive on the permeability of demineralized dentin. Bioactive glass (85% SiO₂, 15% CaO) was fabricated using the sol-gel process, and two experimental dentin adhesives were prepared with 3 wt% silica (silica-containing dentin adhesive; SCA) or BAG (BAG-containing dentin adhesive; BCA). Micro-tensile bond strength (μTBS) test, fracture mode analysis, field-emission scanning electron microscopy (FE-SEM) analysis of adhesive and demineralized dentin, real-time dentinal fluid flow (DFF) rate measurement, and Raman confocal microscopy were performed to compare SCA and BCA. There was no difference in μTBS between the SCA and BCA (p > 0.05). Multiple precipitates were evident on the surface of the BCA, and partial occlusion of dentinal tubules was observed in FE-SEM of BCA-approximated dentin. The DFF rate was reduced by 50.10% after BCA approximation and increased by 6.54% after SCA approximation. Raman confocal spectroscopy revealed an increased intensity of the hydroxyapatite (HA) peak on the dentin surface after BCA application. The novel BAG-containing dentin adhesive showed the potential of both reducing dentin permeability and dentin remineralization.

Role of bioglass in enamel remineralization: Existing strategies and future prospects-A narrative review

Enamel, once formed, loses the ability to regenerate due to the loss of the formative ameloblasts. It is subjected to constant damaging events due to exposure to external agents and oral microbiomes. An enamel remineralization process targets to replenish the lost ionic component of the enamel through a multitude of methods. Enamel remineralization is highly challenging as it has a complex organized hierarchical microstructure. Hydroxyapatite nanocrystals of the enamel vary in size and orientation along alignment planes inside the enamel rod. The inability of the enamel to remodel unlike other mineralized tissues is another substantial deterrent. One of the well-known biomaterials, bioglass (BG) induces apatite formation on the external surface of the enamel in the presence of saliva or other physiological fluids. Calcium, sodium, phosphate, and silicate ions in BG become responsive in the presence of body fluids, leading to the precipitation of calcium phosphate. Studies have also demonstrated the bactericidal potential of BG against Streptococcus mutans biofilms. The anticariogenicity and antibacterial activity were found to be enhanced when BG was doped with inorganic ions such as F, Ag, Mg, Sr, and Zn. Due to the versatility of BG, it has been combined with a variety of agents such as chitosan, triclosan, and amelogenin to biomimic remineralization process. Key strategies that can aid in the development of contemporary enamel remineralization agents are also included in this review.

Anti-demineralizing protective effects on enamel identified in experimental and commercial restorative materials with functional fillers

The aim of this study was to investigate whether experimental and commercial dental restorative materials with functional fillers can exert a protective anti-demineralizing effect on enamel that is not immediately adjacent to the restoration. Four experimental resin composites with bioactive glass and three commercial restorative materials were investigated. Enamel blocks were incubated in a lactic acid solution (pH = 4.0) at a standardized distance (5 mm) from cured specimens of restorative materials. The lactic acid solution was replenished every 4 days up to a total of 32 days. Surfaces of enamel blocks were periodically evaluated by Knoop microhardness measurements and scanning electron microscopy. The protective effect of restorative materials against acid was identified as enamel microhardness remaining unchanged for a certain number of 4-day acid addition cycles. Additionally, the pH of the immersion medium was measured. While enamel microhardness in the control group was maintained for 1 acid addition cycle (4 days), restorative materials postponed enamel softening for 2–5 cycles (8–20 days). The materials capable of exerting a stronger alkalizing effect provided longer-lasting enamel protection. The protective and alkalizing effects of experimental composites improved with higher amounts of bioactive glass and were better for conventional bioactive glass 45S5 compared to a fluoride-containing bioactive glass. Scanning electron micrographs evidenced the protective effect of restorative materials by showing a delayed appearance of an etching pattern on the enamel surface. A remotely-acting anti-demineralizing protective effect on enamel was identified in experimental composites functionalized with two types of bioactive glass, as well as in three commercial ion-releasing restorative materials.

Biophysical and Fluoride Release Properties of a Resin Modified Glass Ionomer Cement Enriched with Bioactive Glasses

The aim of this study was to evaluate the bond strength, microleakage, cytotoxicity, cell migration and fluoride ion release over time from a resin-modified glass-ionomer cement (RMGIC) enriched with bioactive glasses (BAGs) and a nanohybrid restorative polymer resin agent used as adhesion material in the cemented brackets. One hundred and twenty bovine lower incisors were divided into three groups: (Transbond Plus Self Etching Primer (TSEP)/Transbond XT (TXT), TSEP/ACTIVA, orthophosphoric acid gel/ACTIVA) and brackets were bonded. A bond strength test and microleakage test were applied. A fluoride release test was applied after 60 days for the TXT and ACTIVA group. To evaluate cytotoxicity and cell migration, a cell viability and scratch migration assay were done for each group. p values < 0.05 were considered significant. Regarding bond strength and microleakage test, no significant differences were found between TSEP/TXT and TSEP/ACTIVA. At 6.4 pH, ACTIVA showed a higher degree of fluoride ion release, which increased with acid pH (3.5), with a maximum fluoride secretion at 30 days. MTT assay revealed that TXT reduces the viability of gingival cells with significant differences (p < 0.001) compared to the untreated cells (control group). ACTIVA provides optimal adhesive and microfiltration properties, releases substantial amounts of fluoride ions in both acid and neutral media, and its biocompatibility is greater than that of traditional composite resin adhesive systems.

The use of bioactive glass (BAG) in dental composites: A critical review

OBJECTIVE

In recent years, numerous studies have analyzed the role of bioactive glass (BAG) as remineralizing additives in dental restorative composites. This current review provides a critical analysis of the existing literature, particularly focusing on BAGs prepared via the melt-quench route that form an "apatite-like" phase when immersed in physiological-like solutions.

METHODS

Online databases (Science Direct, PubMed and Google Scholar) were used to collect data published from 1962 to 2020. The research papers were analyzed and the relevant papers were selected for this review. Sol-gel BAGs were not included in this review since it is not a cost-effective manufacturing technique that can be upscaled and is difficult to incorporate fluoride.

RESULTS

BAGs release Ca²⁺, PO₄^3- and F^- ions, raise the pH and form apatite. There are numerous published papers on the bioactivity of BAGs, but the different glass compositions, volume fractions, particle sizes, immersion media, time points, and the characterization techniques used, make comparison difficult. Several papers only use certain characterization techniques that do not provide a full picture of the behavior of the glass. It was noted that in most studies, mechanical properties were measured on dry samples, which does not replicate the conditions in the oral environment. Therefore, it is recommended that samples should be immersed for longer time periods in physiological solutions to mimic clinical environments.

SIGNIFICANCE

BAGs present major benefits in dentistry, especially their capacity to form apatite, which could potentially fill any marginal gaps produced due to polymerization shrinkage.

Biomimetic Aspects of Oral and Dentofacial Regeneration

Biomimetic materials for hard and soft tissues have advanced in the fields of tissue engineering and regenerative medicine in dentistry. To examine these recent advances, we searched Medline (OVID) with the key terms “biomimetics”, “biomaterials”, and “biomimicry” combined with MeSH terms for “dentistry” and limited the date of publication between 2010–2020. Over 500 articles were obtained under clinical trials, randomized clinical trials, metanalysis, and systematic reviews developed in the past 10 years in three major areas of dentistry: restorative, orofacial surgery, and periodontics. Clinical studies and systematic reviews along with hand-searched preclinical studies as potential therapies have been included. They support the proof-of-concept that novel treatments are in the pipeline towards ground-breaking clinical therapies for orofacial bone regeneration, tooth regeneration, repair of the oral mucosa, periodontal tissue engineering, and dental implants. Biomimicry enhances the clinical outcomes and calls for an interdisciplinary approach integrating medicine, bioengineering, biotechnology, and computational sciences to advance the current research to clinics. We conclude that dentistry has come a long way apropos of regenerative medicine; still, there are vast avenues to endeavour, seeking inspiration from other facets in biomedical research.

Opportunities for caries prevention using an ion-releasing coating material: a randomised clinical study

Ion-releasing materials (containing fluoride and boron, for example) have shown caries-preventive effects in vitro. The purpose of the present study was to investigate the impact of multi-ion-releasing coating material on pH stabilisation, plaque accumulation and the bacterial composition of dental plaque during a time period of 90 days. The null hypothesis tested here was that the evaluated material would not show any differences in pH stabilisation, plaque accumulation or bacterial composition compared with control material.

The study was carried out as a double-blind, split-mouth, randomised, controlled clinical trial in 28 volunteers. Over the evaluation period (days 4, 30, 60 and 90), pH measurements, plaque index and plaque sampling for bacterial analyses were conducted in a calibrated, standardized manner. The study received ethical permission and was carried out in accordance with the Helsinki Declaration.

A significant difference was observed, with less plaque accumulation over time in the subjects in whom the ion-releasing material was applied in comparison to the non-active group. No significant difference was evident in terms of either pH stabilisation or plaque levels of mutans streptococci.

The null hypothesis relating to plaque accumulation was rejected, with a lower plaque index shown for the test group up to 60–90 days. No adverse effects during the observation period were observed. Since the studied cohort was healthy from a caries perspective, more clinical studies are needed to further evaluate the caries-prevention potential of the ion-releasing material in other patient groups.

Synergetic Effect of 2-Methacryloyloxyethyl Phosphorylcholine and Mesoporous Bioactive Glass Nanoparticles on Antibacterial and Anti-Demineralisation Properties in Orthodontic Bonding Agents

2-methacryloyloxyethyl phosphorylcholine (MPC) is known to have antibacterial and protein-repellent effects, whereas mesoporous bioactive glass nanoparticles (MBN) are known to have remineralisation effects. We evaluated the antibacterial and remineralisation effects of mixing MPC and MBN at various ratios with orthodontic bonding agents. MPC and MBN were mixed in the following weight percentages in CharmFil-Flow (CF): CF, 3% MPC, 5% MPC, 3% MPC + 3% MBN, and 3% MPC + 5% MBN. As the content of MPC and MBN increased, the mechanical properties of the resin decreased. At 5% MPC, the mechanical properties decreased significantly with respect to CF (shear bond strength), gelation of MPC occurred, and no significant difference was observed in terms of protein adsorption compared to the control group. Composition 3% MPC + 5% MBN exhibited the lowest protein adsorption because the proportion of hydrophobic resin composite decreased; CF (91.8 ± 4.8 μg/mL), 3% MPC (73.9 ± 2.6 μg/mL), 3% MPC + 3% MBN (69.4 ± 3.6 μg/mL), and 3% MPC + 5% MBN (55.9 ± 1.6 μg/mL). In experiments against S. mutans and E. coli, addition of MPC and MBN resulted in significant antibacterial effects. In another experiment, the anti-demineralisation effect was improved when MPC was added, and when MBN was additionally added, it resulted in a synergetic effect. When MPC and MBN were added at an appropriate ratio to the orthodontic bonding agents, the protein-repellent, antibacterial, and anti-demineralisation effects were improved. This combination could thus be an alternative way of treating white spot lesions.

The Effect of Bioactive Glass-Enhanced Orthodontic Bonding Resins on Prevention of Demineralization: A Systematic Review

At present, bioactive glasses (BAGs) are demonstrating promising results in the remineralization of hard tissues. Their bioactive properties can potentially overcome the demineralization effect accompanying orthodontic treatment. This review aimed to evaluate the effectiveness of bioactive glass enhanced orthodontic bonding resins on enamel remineralization, in addition to their antibacterial, ion release and acid neutralization effect. Four databases (PubMed, MEDLINE, Web of Science and Scopus) were searched. Two hundred and fifty-one full-text articles were screened independently, out of which seven studies satisfied the inclusion criteria. Quality appraisal was performed by two independent reviewers. Methodologies used to assess the anti-demineralization effect included Micro-Computed Tomography, Polarized Light Microscopy and Hardness Testing (Knoop and Berkovich). All seven articles confirmed the superior remineralization effect of BAG orthodontic bonding resins compared to their non-BAG counterparts. A proportional relationship was proved between BAG concentrations and increased anti-demineralization effect. The addition of antibacterial agents to BAG does not necessarily improve its anti-demineralization effect. Although studies have confirmed the effectiveness of BAG orthodontic bonding resins on enamel remineralization, there was a degree of heterogeneity across studies due to the lack of an in vitro studies standardized protocol.

Light Transmittance and Polymerization of Bulk-Fill Composite Materials Doped with Bioactive Micro-Fillers

This study investigated the effect of bioactive micro-fillers on the light transmittance and polymerization of three commercially available bulk-fill resin composites. These were mixed with 20 wt% bioactive glass 45S5, Portland cement, inert dental barium glass, or nothing (controls). Composites were photo-activated and light transmittance through 4 mm thick specimens was measured in real time. Moreover, degree of conversion (DC) and Knoop hardness (KHN) were assessed. Light transmittance of all bulk-fill composites significantly decreased (p < 0.05) with addition of 20 wt% bioactive glass 45S5 but not when inert barium glass was added. For bulk-fill composites modified with Portland cement, light irradiance dropped below the detection limit at 4 mm depth. The DC at the top surface of the specimens was not affected by addition of bioactive or inert micro-fillers. The bottom-to-top ratio of both DC and KHN surpassed 80% for bulk-fill composites modified with 20 wt% bioactive or inert glass fillers but fell below 20% when the composites were modified with Portland cement. In contrast to Portland cement, the addition of 20 wt% bioactive glass maintains adequate polymerization of bulk-fill composites placed at 4 mm thickness, despite a decrease in light transmittance compared to the unmodified materials.

Fluorinated Bioactive Glass Nanoparticles: Enamel Demineralization Prevention and Antibacterial Effect of Orthodontic Bonding Resin

Orthodontic treatment involving the bonding of fixed appliances to tooth surfaces can cause white spot lesions (WSLs). WSLs increase the likelihood of cavity formation and hence require preservation and prosthetic restoration. Therefore, the prevention of WSLs is of greater importance than treatment. Application of fluoride or the use of fluoride-containing mouthwash can prevent WSLs, but this requires patient cooperation and additional time and cost. Bioactive glass containing 2.5% fluoride was synthesized and mixed with the orthodontic bonding adhesive Transbond XT Low Flow (LV) at ratios of 1, 3, and 5% to prepare orthodontic adhesive samples. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used to characterize the samples. The Vickers hardness test, bracket retention test, and adhesive remnant index (ARI) of the samples were analysed to determine their mechanical properties. To determine the biological cytotoxicity, the cell activity of the samples was evaluated using cell viability tests and the antibacterial activity was analysed using Streptococcus mutans. To evaluate the anti-demineralization effect, the sample was bonded to extracted teeth and a pH cycle test was performed. Micro computed tomography data were obtained from the bonded teeth and sample, and the anti-demineralization effect was evaluated using the ImageJ software program. The Vickers hardness of the sample was higher than that of LV and was dependent on the concentration of fluoride-containing bioactive glass (FBAG). The bracket retention test and ARI of the sample showed no significant differences from those of LV. The cell viability test showed no significant changes at 24 and 48 h after application of the sample. The fluoride ion release test indicated an ion release rate of 9.5–17.4 μg/cm². The antibacterial activity of the experimental group containing FBAG was significantly higher than that of the LV group. The anti-demineralization test showed a concentration-dependent increase. However, the resin containing 5 mass% FBAG (FBAG5) showed a statistically-significant increase compared with LV. The orthodontic adhesive containing FBAG showed antibacterial and anti-demineralization effects, thus indicating possible WSL prevention activity.

Enamel Surface Remineralization Effect by Fluorinated Graphite and Bioactive Glass-Containing Orthodontic Bonding Resin

All orthodontic appliances are potentially cariogenic. The plaque around the orthodontic appliance can make demineralization on tooth surface causing white spot lesion (WSL). The most effective method to prevent WSL is Fluoride appliance and gargling, but this requires patient cooperation, which consumes additional treatment time and cost. As suggested in this study, biomaterials like bioactive glass and fluorinated graphite (FGt) having antibacterial and anti-demineralization ability effective and easy to use in the clinic. To clinically use orthodontic bonding resins containing Graphite Fluoride BAG (FGtBAG), its properties, biological stability, antimicrobial activity, and remineralization effect must be verified. BAG was mixed with 2.5% FGt containing 51 to 61% fluorine. This mixture was mixed with the CharmFill Flow (CF) in the ratios of 1, 3, and 5 wt%. Microhardness and shear bond strength tests were performed to evaluate its mechanical properties. MTT (3-(4, 5-dimethyl thiazol-2-yl)-2, 5-diphenyl tetra) assay was performed for evaluating its safety. Streptococcus mutans, which is major cariogen by producing lactic acid, was evaluated for antibacterial ability of reducing WSL. In addition, x-ray images were obtained by CBCT (Cone beam computed tomography) after a pH cycle. The remineralization effect was verified in vivo and by Image J. FGtBAG did not differ significantly from CF in mechanical tests. The MTT assay found no significant differences between the groups. The antibacterial activity of FGtBAG at 24 h and 48 h was significantly higher than that of CF. The fluoride release rate tended to increase with the FGtBAG content. The pH cycle results showed that FGtBAG had higher concentration-dependent remineralization effect than CF. The results of this study suggests that orthodontic resins containing FGtBAG can prevent WSL owing to their antibacterial activity and remineralization effect.

A review of bioceramics-based dental restorative materials

Currently, much has been published related to conventional resin-based composites and adhesives; however, little information is available about bioceramics-based restorative materials. The aim was to structure this topic into its component parts and to highlight the translational research that has been conducted up to the present time. A literature search was done from indexed journals up to September 2017. The main search terms used were based on dental resin-based composites, dental adhesives along with bioactive glass and the calcium phosphate family. The results showed that in 123 articles, amorphous calcium phosphate (39.83%), hydroxyapatite (23.5%), bioactive glass (16.2%), dicalcium phosphate (5.69%), monocalcium phosphate monohydrate (3.25%), and tricalcium phosphate (2.43%) have been used in restorative materials. Moreover, seven studies were found related to a newly developed commercial bioactive composite. The utilization of bioactive materials for tooth restorations can promote remineralization and a durable seal of the tooth-material interface.

Enamel Anti-Demineralization Effect of Orthodontic Adhesive Containing Bioactive Glass and Graphene Oxide: An In-Vitro Study

White spot lesions (WSLs), a side effect of orthodontic treatment, can result in reversible and unaesthetic results. Graphene oxide (GO) with a bioactive glass (BAG) mixture (BAG@GO) was added to Low-Viscosity Transbond XT (LV) in a ratio of 1, 3, and 5%. The composite’s characterization and its physical and biological properties were verified with scanning electron microscopy (SEM) and X-ray diffraction (XRD); its microhardness, shear bond strength (SBS), cell viability, and adhesive remnant index (ARI) were also assessed. Efficiency in reducing WSL was evaluated using antibacterial activity of S. mutans. Anti-demineralization was analyzed using a cycle of the acid-base solution. Adhesives with 3 wt.% or 5 wt.% of BAG@GO showed significant increase in microhardness compared with LV. The sample and LV groups showed no significant differences in SBS or ARI. The cell viability test confirmed that none of the sample groups showed higher toxicity compared to the LV group. Antibacterial activity was higher in the 48-h group than in the 24 h group; the 48 h test showed that BAG@GO had a high antibacterial effect, which was more pronounced in 5 wt.% of BAG@GO. Anti-demineralization effect was higher in the BAG@GO-group than in the LV-group; the higher the BAG@GO concentration, the higher the anti-demineralization effect.

Remineralization Property of an Orthodontic Primer Containing a Bioactive Glass with Silver and Zinc

White spot lesions (WSLs) are irreversible damages in orthodontic treatment due to excessive etching or demineralization by microorganisms. In this study, we conducted a mechanical and cell viability test to examine the antibacterial properties of 0.2% and 1% bioactive glass (BAG) and silver-doped and zinc-doped BAGs in a primer and evaluated their clinical applicability to prevent WSLs. The microhardness statistically significantly increased in the adhesive-containing BAG, while the other samples showed no statistically significant difference compared with the control group. The shear bond strength of all samples increased compared with that of the control group. The cell viability of the control and sample groups was similar within 24 h, but decreased slightly over 48 h. All samples showed antibacterial properties. Regarding remineralization property, the group containing 0.2% of the samples showed remineralization properties compared with the control group, but was not statistically significant; further, the group containing 1% of the samples showed a significant difference compared with the control group. Among them, the orthodontic bonding primer containing 1% silver-doped BAG showed the highest remineralization property. The new orthodontic bonding primer used in this study showed an antimicrobial effect, chemical remineralization effect, and WSL prevention as well as clinically applicable properties, both physically and biologically.