Experimental polyethylene-hydroxyapatite carrier-based endodontic system: an in vitro study on dynamic thermomechanical properties, sealing ability, and measurements of micro-computed tomography voids

Three-Dimensional Measurement of Obturation Quality of Bioceramic Materials in Filling Artificial Internal Root Resorption Cavities Using Different Obturation Techniques: An In Vitro Comparative Study

INTRODUCTION

Pathologic conditions such as internal root resorption (IRR) may complicate root canal filling. This study aimed to evaluate and compare the obturation quality by measuring the percentage of obturation volume (POV) in root canals with artificial IRR obturated with different materials and techniques using cone beam computed tomography (CBCT).

METHODS

Forty single canal extracted mandibular premolars were decoronated to standardize their length to 14 mm. Following instrumentation, the roots were cut horizontally, and artificial IRR cavities were made at the level of 7 mm from the apex. The root halves were joined using cyanoacrylate adhesive. The samples were randomly assigned to 4 groups (n = 10), and the canals were filled as follows: single-cone technique (SC), bulk-fill Bio-C Sealer (BF), and Bio-C Repair for the coronal and middle third (BCR) + cold lateral condensation technique (CLC) for the apical third and continuous wave compaction technique (CWC). The pre- and postobturation volumes and the POV were measured in the total canal and for the apical, middle, and coronal thirds separately using CBCT and Mimics Medical software. The results were analyzed statistically using one-way ANOVA and Tukey HSD test, and statistical significance was set at P < .05.

RESULTS

BF group resulted in significantly lower total, coronal, middle and apical POV values compared to SC, BCR + CLC, and CWC groups (P < .05), respectively. Also, at the apical third, the BCR + CLC group showed significantly lower POV than the SC and CWC groups (P < .05), respectively. The intra-group comparison showed that BF and BCR + CLC groups had a significantly lower POV in the apical third compared to the middle third (P < .05). Conversely, the CWC group had a significantly higher apical POV than the middle third (P < .05).

CONCLUSIONS

The maximum POV was obtained using the CWC technique, Bio-C Repair, and SC technique with Bio-C Sealer, making their application in IRR more preferable than the BF Bio-C Sealer.

A critical analysis of research methods and experimental models to study root canal fillings

Canal filling materials and techniques have been one of the most studied topics in Endodontics. A simple search using the mesh term "root canal filling" in PubMed revealed more than 11,000 articles, an impressive number that is much higher than "root canal disinfection" (5,544 articles) or even the popular "root canal preparation" (8,527 articles). The overriding importance attributed to root filling procedures is not merely intuitive. It derived from the appealing relevance given by the appearance of the white lines in common radiographs grounded on retrospective clinical data that had identified the quality of a root filling as one of the major causes of treatment failure (lack of healing). Since the publication of the Washington study, impressive efforts have been made for the release of new materials and techniques, as well as, for the development of a plethora of laboratory methods to assess the quality of root filling procedures. This narrative review aims to address and discuss the most relevant laboratory methods to assess the root canal filling. Since filling quality improvements have not translated into higher success rates, as reported in longitudinal clinical studies, more than to deliver a simple methodology-based review, this paper aims to present an in-depth critical view on the assessment of laboratory methods used to study the filling materials and techniques. Recent data indicate that the long-term dimensional stability/degradation over time of endodontic sealers plays a central role in the treatment outcome. In this context, laboratory methods should be developed focusing on predicting, at least to some degree, the long-term clinical behaviour of root canal fillings, rather than simply ranking different materials or techniques.

A laboratory study to assess the physical, mechanical, and 3-D structural properties of nano-apatite grafted glass fibre-based endodontic posts

AIM

To fabricate and characterize nano-hydroxyapatite (nHA) grafted and non-grafted glass fibre-based endodontic posts.

METHODOLOGY

Experimental glass fibre posts were fabricated using silanized nHA grafted (ex-HA) and non-grafted glass fibre (ex-P) reinforced resins. The structural analysis and morphological patterns were analysed with Fourier transform infrared spectroscopy and scanning electron microscopy, respectively. EverStick^® glass fibre posts (eS) were used as a control group. The degree of conversion, flexural strength, and flexural modulus was investigated and the fractured structure was evaluated with a scanning electron microscope. Root canals were prepared in human extracted teeth restored with experimental and control posts. The push-out bond strength was evaluated with radicular dentine at days 7, 30, and 90, and the presence of voids at the interface were measured at day 1, 7, 30, and 90 with micro-computed tomography. The Shapiro-Wilk test and one-way ANOVA post-hoc Tukey's test were performed. The level of significance was set at 0.05.

RESULTS

The SEM and FTIR confirmed the presence of a silane-coupling agent on the glass fibres. The ex-HA post had a significantly lower degree of conversion compared to the ex-P post (p = .0008), but a significantly higher conversion than the eS post (p = .0014). The maximum flexural strength value was obtained with the ex-HA post with an insignificant difference (p = .366) compared to ex-P post and a significant difference (p = .029) compared to the eS post. The flexural modulus of ex-HA, ex-P, and eS posts were significantly different (p = .037). Similarly, the ex-HA post had a significantly higher push-out bond strength at days 7 and 30 (p = .037) compared to the ex-P and eS posts. The volume of voids had a nonlinear behaviour amongst the groups with no significant difference between the posts.

CONCLUSION

The fabrication of the experimental posts was successful and the ex-HA post had greater flexural strength and push-out bond strength compared to the ex-P post. The degree of conversion of the ex-HA post was lower than the ex-P and eS posts. The volume of voids of ex-HA and ex-P posts was lower than that of eS posts.