Effect of maleic acid on the bond strength of fibre posts to root dentine

Glycolic acid on push-out bond strength of fiber post and smear removal: an in vitro study

This study aims to investigate glycolic acid (GA) as a final irrigant on push-out bond strength of fiber post and smear removal. Ninety mandibular premolars were stabilized with a silicone key and photographed, and canal cross-section was calculated by image processing software. Round canal morphology was selected. The specimens were divided into five groups (n = 18); 10%GA, 17%EDTA, NaOCl + 10%GA, NaOCl + 17%EDTA, and the control. Fifteen specimens were used for the push-out. Three specimens were evaluated using a scanning electron microscope after post space preparation. Two-way ANOVA and Chi-square were used for statistics. GA presented higher strength than EDTA (p < 0.05). The NaOCl + GA showed higher strength than the NaOCl + EDTA (p < 0.05). The highest values were observed in cervical and lowest in apical thirds (p < 0.05). The most failure type was between dentin and resin (p < 0.05). GA removed the smear in the post space including the apical third. The NaOCl + GA has superiority to NaOCl + EDTA on push-out strength. Glycolic acid improved the bond strength of fiber post when used as a final post space irrigant. The combination of NaOCl and glycolic acid did not negatively affect the bond strength and was more effective compared to the combination with EDTA. Glycolic acid improved the bond strength of fiber post when used as a final post space irrigant. The combination of NaOCl and glycolic acid did not negatively affect the bond strength and was more effective compared to the combination with EDTA.

Influence of different intraradicular chemical pretreatments on the bond strength of adhesive interface between dentine and fiber post cements: A systematic review and network meta-analysis

Systematic review and network meta-analyses were performed to answer the question: Do intraradicular chemical pretreatments affect the bond strength of the adhesive interface between dentine and fiber post cements? A literature search was performed in PubMed, Scopus, Web of Science, LILACS, BBO, and Cochrane Library in October 2018 (updated September 2021). In vitro studies that compared the bond strength assessed by push-out tests following at least two dentine chemical treatments prior to fiber post cementation were included. Risk of bias was evaluated. A random-effects Bayesian-mixed treatment comparison model was used to compare push-out bond strength of different chemical pretreatments. SUCRA (surface area under the cumulative ranking) analysis was performed to rank the pretreatments. After removing duplicates and screening titles and abstracts, 61 studies remained. SUCRA analysis showed that the best bond strength values for self-etch, etch-and-rinse, and self-adhesive cements were ethyl acetate (SUCRA: 99.8%), low concentration NaOCl (SUCRA: 83.4%), and grape seed extract (SUCRA: 97.6%), respectively. According to the SUCRA rankings, ethanol was in a good position for all adhesive strategies (SUCRA: 78.6%). The use of chemical pretreatments in intraradicular dentine of endodontically treated teeth depends on the adhesive and cementation strategy. The pretreatment generally associated with the highest bond strength was ethanol.

Post-Space Treatment Influences the Bond Strength In Endodontically Treated Teeth: A Systematic Review and Meta-Analysis of In Vitro Studies

OBJECTIVES

This systematic review of in vitro studies investigated the influence of the post-space treatment used to remove the smear layer on the bond strength of the post to root canal dentin.

METHODS AND MATERIALS

In vitro studies included in this study were identified from PubMed/MEDLINE, Lilacs, and Scopus databases up until March 2019, without limits on publication year or language. Two reviewers independently selected the studies based on the inclusion and exclusion criteria, extracted the data, and evaluated the risk of bias of all studies. A random effects model was used for pairwise meta-analyses (control vs. post-space preparation groups) at a significance level of p<0.05.

RESULTS

Of the 2,832 potentially eligible studies, 453 studies were selected for full-text analysis, and 75 were included in this systematic review. Only one study was considered to have a low risk of bias. Overall, post-space treatment significantly improves the bond strength to root canal dentin (p<0.00001).

CONCLUSION

Post-space treatment has a positive influence on the bond strength of the post to root canal dentin. In this review, the post-space treatments that improve the adhesive resistance of the post were ethanol, sodium hypochlorite, and ethylene diamine tetra-acetic acid (NaOCl + EDTA), NaOCl + EDTA + ultrasound, erbium-doped yttrium aluminium garnet laser (Er:YAG laser), neodymium-doped yttrium aluminium garnet laser (Nd:YAG laser), and diode laser.

Effect of zirconia surface modification using dopamine polymerisation on the shear bond strength of resin cement

This study evaluated the influence of polydopamine treatment on the surface properties and bond strength of yttria-stabilised tetragonal zirconia polycrystal (Y-TZP). Sixty-three zirconia blocks (10 × 10 × 2 mm) were randomly divided into three groups defined by surface treatment: (i) control group (C), (ii) grit-blasted with 110 μm alumina particles (GB), and (iii) polydopamine (PDA) coating. The surfaces of specimens subjected to different treatments were investigated by X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and water contact angle measurements. After the surface treatments, the specimens were cemented to resin composite cylinders. After bonding, the shear bond strength of the ceramic to the resin was measured, and the failure mode of each specimen was analysed using a stereomicroscope. The results indicated that the shear bond strength is highest for the GB treatment and lowest for the controls. However, the difference between groups GB and PDA was not statistically significant. In the control group, adhesive failure was predominant, whereas in the treatment groups, mixed mode failure was predominant. The pre-treatment of Y-TZP ceramic with the polydopamine coating might improve the bond strength of the resin cement to the zirconia ceramic.

Postspace pretreatment with 17% ethylenediamine tetraacetic acid, 7% maleic acid, and 1% phytic acid on bond strength of fiber posts luted with a self-adhesive resin cement

Context:

Pretreatment of radicular dentin with chelating agents improves the bond strength of fiber-posts luted with a self-adhesive resin cement.

Aims:

The aim of this study was to assess the effects of the three chelating agents as final rinse of the postspace on bond strength of fiber posts luted with a self-adhesive resin cement.

Settings and Design:

This is an in vitro laboratory study.

Materials and Methods:

Forty-five mandibular premolars were prepared using MTwo rotary system and irrigation was done with 2.5% sodium hypochlorite. Three groups of teeth samples were considered for postspace preparation and irrigated with different solutions: Group 1: 17% ethylenediamine tetraacetic acid (EDTA); Group 2: 7% Maleic acid; Group 3: 1% Phytic acid. This was followed by the luting the posts with RelyX U200. After a week, from each sample, 2 mm thick slices were obtained from each third of the root and subjected to push-out bond strength testing.

Statistical Analysis Used:

One-way analysis of variance and Bonferroni's Post hoc analysis was used for assessing the results. The statistical significance level was set at P < 0.05.

Results:

Bond strength values were improved with maleic acid and phytic acid pretreatment with slight or no significant difference between these groups. A final rinse of postspace with EDTA significantly reduced the bond strength.

Conclusions:

Maleic acid (7%) pretreatment of postspace improved the adhesion of fiber posts luted with a self-adhesive resin cement.

Influence of the Chelating Solutions in the Resistance of Glass Fiber Posts to the Root Dentin

Objective  This study aimed to evaluate the influence of chelating agents (EDTA, citric acid and Tetraclean) on glass fiber posts adhesion to root dentin.

Materials and Methods  Forty mandibular premolars single canals, with complete apical root, straight, circular cross sections were selected, accessed and had the cervical third prepared with Gates-Glidden drills, then included in resin, instrumented with ProTaper Universal and the root canal obturation was carried out. After, the samples were randomly divided into 4 groups (n = 10) to test the final irrigation solutions: G1:17% EDTA; G2:10% citric acid; G3: Tetraclean and G4: saline solution (control). After 30 days of storage (36.5° C and 100% humidity), the post preparation was performed leaving 4 mm of apical endodontic filling. Then, a fiber-glass post previously selected was coated with ED Primer adhesive system and resin sealer Panavia, installed and stored for 24 hours at 37°C. The samples were subjected to a tensile test with a constant speed of 1 mm/min with 2000 Kgf. The results were analyzed with the ANOVA test.

Results  The statistical analyzes indicated no significant differences between the groups (p > 0.05).

Conclusion  The type of chelating agent used in the final irrigation of the endodontic treatment did not influence the tensile strength of the fixation system used to sealer the glass fiber posts to the intracanal dentin.