Effect of artificial aging on high translucent dental zirconia: simulation of early failure

Fatigue methods for evaluating translucent dental zirconia

OBJECTIVE

To investigate fatigue methods for the evaluation of translucent zirconia and to associate in vitro failures with clinically reported ones.

DATA

Studies published in English that used fatigue tests on dental translucent zirconia.

SOURCES

Two databases (MEDLINE/PubMed and Scopus) were electronically searched without any restriction on year of publication.

STUDY SELECTION

A total of 4555 studies were identified. After removal of duplicates (78) and irrelevant articles (4316) that did not meet the inclusion criteria, 161 articles were considered eligible based on their titles and abstracts. These articles were fully read, leading to the inclusion of 41 studies in the review.

RESULTS

The most widely used fatigue method for evaluation of translucent zirconia was step-stress (18 articles), followed by staircase (seven articles), and step-wise (two articles). Most studies had been conducted in a wet environment with the use of a stainless steel piston to apply load to cemented structures on a dentin-like substrate. Most fracture analyses indicated the fracture originated on the cementation or contact surface where the load was applied. Moreover, studies that utilized anatomical structures (dental crowns) reported fractures starting at the cervical margin of the crowns.

CONCLUSION

Most studies used the step-stress method. Only three studies reported failures similar to those found in clinical trials that used translucent zirconia restorations.

CLINICAL SIGNIFICANCE

The study findings can assist on correlating clinical failures to the ones observed in vitro.

How could mouthwashes affect the color stability and translucency of various types of monolithic zirconia? An in-vitro study

OBJECTIVES

This study aimed to evaluate the color stability and translucency of various types of monolithic zirconia after immersion in chlorhexidine and Listerine mouthwashes.

MATERIALS AND METHODS

This experimental study was performed on 36 disk-shaped specimens fabricated from low-translucent, high-translucent, and multilayered monolithic zirconia (n = 12 per group). Each group was equally divided and immersed in either 2% chlorhexidine (CHX) or Listerine mouthwash for 2 min daily over 7 days. Changes in color (ΔE) and the translucency parameter (ΔTP) were evaluated and compared. The data were analyzed with one-way ANOVA followed by Tukey's post-hoc tests (α = 0.05).

RESULTS

Chlorhexidine caused a significantly lower ΔE and a significantly higher ΔTP in multilayered zirconia compared to the low-translucency (ΔE: P = 0.0027, ΔTP: P<0.001) and the high-translucency zirconia group (ΔE: P<0.001, ΔTP: P = 0.022). Listerine caused a significantly higher ΔE in the high-translucency zirconia group compared to the multilayered zirconia group (P = 0.0165). It also resulted in a significantly higher mean ΔTP in the multilayered zirconia group compared to the low-translucency (P = 0.0003) and high-translucency zirconia groups (P = 0.019).

CONCLUSIONS

In both mouthwashes, multilayered monolithic zirconia exhibited the highest color stability among the tested materials; albeit with the most pronounced changes in translucency. Meanwhile, high-translucency monolithic zirconia was more prone to discoloration when exposed to both mouthwashes.

Thickness and yttria percentage influences the fracture resistance of laminate veneer zirconia restorations

OBJECTIVES

Mechanical properties are cardinal for the long-term clinical success of laminate veneer restorations but the selection of new restorative materials should ideally be based on clinical evidence, therefore, in vitro testing of dental materials is a good alternative to evaluate their properties and understand their behavior so this study aimed to compare and evaluate the effect of two different thicknesses and yttria percentage on the fracture resistance of laminate veneer zirconia restorations.

MATERIALS AND METHODS

Forty laminate veneer restoration prepared from partial sintering zirconia of 3Y (yttria), 5Y (yttria), combined 3Y&5Y (yttria), and lithium disilicate. Specimens were assigned into four main groups according to their percentage of yttria content (n = 10) and subgrouped into two thicknesses (0.5 mm thickness and 0.3 mm thickness) (n = 5) as follows: Group I, II, III, and IV (Group I for lithium disilicate (control), Group II for 3Y zirconia, Group III for 5Y zirconia, and Group IV for combined 3Y&5Y zirconia), each of them subdivided according to their thickness into two subgroups (n = 5 for each one) and resistance to fracture for each restoration was evaluated using a universal testing machine. Data were analyzed using a one-way analysis of variance and Duncan's tests at a 5% level of significance.

RESULTS

The thickness of laminate veneer restoration significantly affects the fracture resistance value of all type of laminate veneers restorations (fracture resistance mean value was highest for 0.5 mm thickness and lower for 0.3 mm thickness restorations) and yttria percentage significantly affect fracture resistance value of zirconia laminate veneer restorations (fracture resistance mean value was highest for 0.5 mm thickness of 3Y zirconia [865 N] and combined 3Y&5Y zirconia [846 N]).

CONCLUSIONS

Reducing the thickness of laminate zirconia veneer restorations to 0.3 mm reduces its fracture resistance and increasing yttria percentage had an adverse effect on fracture resistance of zirconia laminate veneer restorations.

Fractographic analysis of 35 clinically fractured bi-layered and monolithic zirconia crowns

OBJECTIVES

The aim of this retrieval study was to analyze the fracture features and identify the fracture origin of zirconia-based single crowns that failed during clinical use.

METHODS

Thirty-five fractured single crowns were retrieved from dental practices (bi-layered, n=15; monolithic, n=20). These were analyzed according to fractographic procedures by optical and scanning electron microscopy to identify fracture patterns and fracture origins. The fracture origins were closely examined. The crown margin thickness and axial wall height were measured.

RESULTS

Three types of failure modes were observed: total fractures, marginal semilunar fractures, and incisal chippings. Most of the crowns (23) had fracture origins at the crown margin and seven of them had defects in the fracture origin area. The exact fracture origin was not possible to identify due to missing parts in four crowns. The crown wall thickness was 20% thinner and wall height 30% shorter in the fracture origin area compared to the opposite side.

CONCLUSIONS

The findings in this study show that fractography can reveal fracture origins and fracture modes of both monolithic and bi-layered dental zirconia. The findings indicate that the crown margin on the shortest axial wall is the most common fracture origin site.

CLINICAL SIGNIFICANCE

Crown design factors such as material thickness at the margin, axial wall height and preparation type affects the risk of fracture. It is important to ensure that the crown margins are even and flawless.

The Effect of Translucency and Surface Treatment on the Flexural Strength of Aged Monolithic Zirconia

Aims

This in vitro study aimed to evaluate the effect of the degrees of translucency in different types of monolithic zirconia as well as the aging and surface treatment with airborne particle abrasion on the flexural strength of monolithic zirconia.

Materials and Methods

Sixty bar-shaped specimens were fabricated from three different types of presintered monolithic zirconia (n = 20 per group) including low translucent (LT) (DD Bio ZW iso, high strength zirconia, Dental Direkt, Germany), high translucent (HT) (DD Bio ZX² 98, high translucent zirconia, Dental Direkt, Germany), and multilayered system (ML) (DD cubeX2®ML, multilayer, cubic zirconia system, Dental Direkt, Germany). Each monolithic zirconia group was equally subdivided according to be either air-abraded with 110 µm aluminium oxide particles or left untreated (control). After thermocycling, the flexural strength was measured by using a universal testing machine. Two-way ANOVA followed by Tukey's post hoc and independent samples t-test were used for the statistical analyses (P < 0.05).

Results

Surface treatment and types of zirconia were found to have a significant interaction (P = 0.010). Having controlled the effect of surface treatment, the flexural strength of HT and LT zirconia was found to be significantly higher than the ML zirconia system (P ≤ 0.001). Airborne particle abrasion could significantly decrease the flexural strength of monolithic zirconia only in ML zirconia (P = 0.002).

Conclusions

Multilayered zirconia system had the lowest flexural strength among all groups. Moreover, the flexural strength of this system was attenuated by surface treatment with airborne particles abrasion.

Monolithic zirconia crowns: effect of thickness reduction on fatigue behavior and failure load

PURPOSE

The objective of this study was to evaluate the effect of thickness reduction and fatigue on the failure load of monolithic zirconia crowns.

MATERIALS AND METHODS

140 CAD-CAM fabricated crowns (3Y-TZP, inCorisTZI, Dentsply-Sirona) with different ceramic thicknesses (2.0, 1.5, 1.0, 0.8, 0.5 mm, respectively, named G2, G1.5, G1, G0.8, and G0.5) were investigated. Dies of a mandibular first molar were made of composite resin. The zirconia crowns were luted with a resin composite cement (RelyX Unicem 2 Automix, 3M ESPE). Half of the specimens (n = 14 per group) were mouth-motion-fatigued (1.2 million cycles, 1.6 Hz, 200 N/ 5 – 55℃, groups named G2-F, G1.5-F, G1-F, G0.8-F, and G0.5-F). Single-load to failure was performed using a universal testing-machine. Fracture modes were analyzed. Data were statistically analyzed using a Weibull 2-parameter distribution (90% CI) to determine the characteristic strength and Weibull modulus differences among the groups.

RESULTS

Three crowns (21%) of G0.8 and five crowns (36%) of G0.5 showed cracks after fatigue. Characteristic strength was the highest for G2, followed by G1.5. Intermediate values were observed for G1 and G1-F, followed by significantly lower values for G0.8, G0.8-F, and G0.5, and the lowest for G0.5-F. Weibull modulus was the lowest for G0.8, intermediate for G0.8-F and G0.5, and significantly higher for the remaining groups. Fatigue only affected G0.5-F.

CONCLUSION

Reduced crown thickness lead to reduced characteristic strength, even under failure loads that exceed physiological chewing forces. Fatigue significantly reduced the failure load of 0.5 mm monolithic 3Y-TZP crowns.

A REVIEW OF MECHANICAL BEHAVIOR OF DENTAL CERAMIC RESTORATIONS

Dental ceramics are well known for restoring the function and aesthetic of lost or damaged teeth. Understanding these materials’ mechanical and aesthetic properties can make a suitable choice for those materials. The longevity of dental ceramics depends on several factors, including manufacturing method, clinical process, and the oral cavity’s aqueous environment. Failure mechanisms in restorative ceramics are complex and a combination of several factors. Different microstructures in the crystalline phase will involve the propagation of cracks and eventually the fatigue of ceramic materials. Large grains reduce mechanical performance compared to small grain sizes. Aesthetic materials used for veneering are weaker than the core materials and fail when even subjected to small loads. The soft bonding in the core–veneer interface and possible residual stresses created during the veneering method are drawbacks of these systems. Studies on the mechanical behavior of these materials have grown significantly in recent years and provide helpful information about static and fatigue experimentation and the failure behavior of various materials used in dental crowns.