The effect of surface pre-reacted glass-ionomer filler eluate on dental pulp cells and mineral deposition on dentin: In vitro study

Effect of borate, fluoride and strontium ions on biomimetic nucleation of calcium phosphate studied using solid-state nuclear magnetic resonance and X-ray diffraction

OBJECTIVES

Apatite minerals can have various anions and cations in their crystal structure in addition to phosphate ion (PO₄³⁻) and calcium ion (Ca2+). The aim of this study is to investigate effects of the borate, fluoride and strontium ions on biomimetic nucleation of calcium phosphate.

METHODS

Nano-crystalline hydroxyapatite (H-Ap) was obtained from a supersaturated buffered solution containing 4.12 mM HPO42- and 5.88 mM Ca2+ (H-Ap). Four additives were used in solid solution methods: (i) 0.588 mM F- (F-Ap), (ii) 5.88 mM Sr2+ (Sr-Ap), (iii) 4.12 mM BO33- (BO3-Ap), and (iv) a surface pre-reacted glass ionomer (S-PRG) filler eluate that contained 0.17 mM Sr2+, 0.588 mM F-, 11.1 mM BO33-- (SPRG-Ap). Apatite crystallization was investigated using a solid-state magic-angle spinning NMR spectroscopy and X-ray diffraction (XRD) with the Rietveld analysis.

RESULTS

A 2D 1H-31P heteronuclear-correlation NMR showed F- ion incorporation in the apatite structure of the F-Ap and SPRG-Ap. The peaks on the 31P axis of the F-Ap, Sr-Ap, and BO3-Ap were different from that of the H-Ap, and the full width at half maximum increased in the following order: H-Ap∼F-Ap∼BO3-Ap< SPRG-Ap< Sr-Ap, suggesting the incorporation of the F-, Sr2+ and BO33-. The incorporation of F and BO3 was further confirmed by 19F and 11B NMR. The XRD revealed that Sr2+ was preferentially incorporated into the CaII site.

SIGNIFICANCE

The F-, Sr2+ and BO33-ions might be involved in modifying the crystallization of apatite precipitation, producing a variety of apatite. S-PRG filler that release these ions may have an effect on remineralization, i.e., the reformation of apatite lost due to caries.

Influence of surface pre-reacted glass-ionomer (S-PRG) filler eluate on collagen morphology, remineralization, and ultimate tensile strength of demineralized dentin

OBJECTIVE

To evaluate the effect of ions released from surface pre-reacted glass-ionomer (S-PRG) filler on collagen morphology, remineralization, and ultimate tensile strength (UTS) of demineralized dentin.

MATERIALS AND METHODS

Bovine incisor root dentins were demineralized with EDTA and divided into three treatment groups: 1) water (control); 2) S-PRG filler eluate; 3) 125 ppm sodium fluoride (NaF). After a 3-min treatment, the specimens were stored in simulated body fluid (SBF) for 3 months. Collagen morphology and remineralization were assessed using transmission electron microscopy (TEM), scanning electron microscopy (SEM), and Fourier-transform infrared spectroscopy (FTIR). Additionally, ultimate tensile strength (UTS) was measured.

RESULTS

TEM and SEM demonstrated that S-PRG induced more effective remineralization compared to NaF, while the control group exhibited faint mineral deposition with collagen degradation. S-PRG displayed the most homogenous mineral deposition in collagen fibrils, along with closure of interfibrillar spaces. Extensive mineral precipitation was observed within dentinal tubules in the S-PRG group. In addition, S-PRG filler eluate demonstrated significantly higher phosphate-to-amide ratio and UTS compared to NaF and control groups (p < 0.05).

CONCLUSIONS

Ion released from S-PRG filler positively influenced collagen morphology, remineralization, and ultimate tensile strength of demineralized dentin.

CLINICAL SIGNIFICANCE

S-PRG filler enhances remineralization and improve the biomechanics of demineralized dentin.

An In Vitro Evaluation of Selenium Nanoparticles on Osteoblastic Differentiation and Antimicrobial Properties against Porphyromonas gingivalis

Despite numerous treatment methods, there is no gold standard for the treatment of peri-implantitis—an infectious peri-implant disease. Here, we examined selenium nanoparticles (SeNPs) at a wide range of concentrations to investigate their cytotoxicity, regulation of osteoblastic differentiation, and assessed the antibacterial effect against Porphyromonas gingivalis. SeNPs (mean size: 70 nm; shape: near-spherical; concentration: 0–2048 ppm) were tested against the MC3T3-E1 osteoblast precursor cell line and P. gingivalis red complex pathogen. Reverse transcriptase quantitative polymerase chain reaction (RT-qPCR) analysis was used to evaluate the bone morphogenetic protein 2 (BMP-2) signaling pathway. SeNPs at concentrations of 2–16 ppm showed no obvious cytotoxicity and promoted good mineralization and calcification. SeNPs at concentrations 64 ppm and below influenced gene expression promoting osteoblastic differentiation, whereas at high concentrations inhibited the expression of Runt-related transcription factor 2 (Runx2). The growth of P. gingivalis was significantly inhibited at SeNP concentrations of more than 4 ppm. SeNPs at low concentrations promoted osteoblastic differentiation while strongly inhibiting peri-implantitis pathogen growth. This study represents one of the few in vitro assessments of SeNPs against a red complex pathogen and the regulatory effect on osteoblastic differentiation. The findings demonstrate SeNPs could potentially be used for future application on implant coating.