Evaluation of Different Techniques and Materials for Filling in 3-dimensional Printed Teeth Replicas with Perforating Internal Resorption by Means of Micro-Computed Tomography

INTRODUCTION

The aim of this study was to evaluate the filling ability of 2 obturation techniques in 3-dimensional (3D) printed teeth with perforating internal resorption (PIR).

METHODS

A maxillary central incisor was instrumented and scanned by micro-computed tomographic (micro-CT) imaging. The 3D model was exported in the stereolithographic format and, with the aid of OrtogOnBlender software (Cícero Moraes, Sinop, SP, Brazil), a PIR in the middle third of the root canal was designed. Thirty-two replicas were printed in surgical resin and distributed into 4 groups (n = 8) according to the obturation technique and the material used: 2 groups used the hybrid technique, 1 with Bio-C Sealer (BCS; Angelus, Londrina, PR, Brazil)/gutta-percha (GP; VDW GmbH, Munich, Germany) + Bio-C Repair (BCR; Angelus, Londrina, PR, Brazil) and the other with BioRoot (BR; Septodont, Saint Maur des Fosses, France)/gutta-percha (GP) + Biodentine (BD; Septodont, Saint Maur des Fosses, France), and 2 groups used the incremental technique, 1 with BCR and the other with BD. Postobturation micro-CT imaging was performed to measure the percentage volume of voids and laser confocal microscopy to measure the surface roughness (μm) of the repair cements. Data were compared using analysis of variance and Kruskal-Wallis tests.

RESULTS

Regarding the filling volume in the apical third, the BCS/GP + BCR (89.70 ± 5.15), BR/GP + BD (87.70 ± 8.43), and BCR (84.20 ± 9.00) groups showed the highest percentages compared with the BD group (69.70 ± 6.88) (P < .05). In the area of internal resorption, the BCS/GP + BCR (96.00 ± 2.64) and BCR (95.30 ± 2.93) groups showed the highest percentages compared with the BR/GP + BD group (91.50 ± 1.35) (P < .05). The BD group showed intermediate values that were sometimes similar to the BCS/GP + BCR and BCR groups and similar to the BR/GP + BD group (P > .05). Regarding the quality of the filling in the perforation area, the BCR group showed better results compared with the BD group (P < .001). Regarding roughness, the BCR group (1.66 ± 0.65) showed lower surface roughness compared with the BD group (2.51 ± 0.89) (P < .05).

CONCLUSIONS

The capacity and quality of the filling in teeth with PIR were superior with the incremental technique with BCR and the hybrid technique with BCS/GP + BCR.

Mineral Trioxide Aggregate Applications in Endodontics: A Review

A current topic in dentistry concerns the biocompatibility of the materials, and in particular, conservative dentistry and endodontics ones. The mineral trioxide aggregate (MTA) is a dental material with biocompatibility properties to oral and dental tissues. MTA was developed for dental root repair in endodontic treatment and it is formulated from commercial Portland cement, combined with bismuth oxide powder for radiopacity. MTA is used for creating apical plugs during apexification, repairing root perforations during root canal therapy, treating internal root resorption, and pulp capping. The objective of this article is to investigate MTA features from a clinical point of view, even compared with other biomaterials. All the clinical data regarding this dental material will be evaluated in this review article. Data obtained from the analysis of the past 10 years' literature highlighted 19 articles in which the MTA clinical aspects could be recorded. The results obtained in this article are an important step to demonstrate the safety and predictability of oral rehabilitations with these biomaterials and to promote a line to improve their properties in the future.