Physico-chemical investigation of endodontic sealers exposed to simulated intracanal heat application: epoxy resins and zinc oxide-eugenols

Hydraulic (Single Cone) Versus Thermogenic (Warm Vertical Compaction) Obturation Techniques: A Systematic Review

Root canal treatment (RCT) involves cleaning and shaping of the root canal system before filling the canals with obturating materials, often gutta-percha (GP). The two primary obturation techniques are the thermogenic (warm vertical compaction, WVC) and hydraulic (single cone, SC) techniques. The objective of this study is to compare the clinical results and effectiveness of thermogenic and hydraulic obturation procedures in endodontic therapy to provide clinicians with evidence-based recommendations. Search strategies were conducted on February 01, 2024 and involved the databases Web of Science, PUBMED, Google Scholar, Scopus, Medline, Embase, NCBI, and Cochrane Library. The current systematic review included systematic reviews; meta-analyses; cohort studies; randomized controlled trial (RCT) studies; studies involving the comparison between single cone and warm compaction techniques; studies involving outcomes that include advantages, disadvantages, and complications associated with single cone or warm compaction techniques; and studies published within the last seven years. The selected studies were restricted to those with insufficient data, review articles without authentic references, publications in a language other than English, animal studies, and studies not involving SC or WVC. Out of 2300 studies registered, only 12 studies were included in the review. Both WVC and SC techniques showed satisfactory root canal fillings. However, five studies showed differences in the filling quality, four studies assessed the sealing ability and the dentinal tubule penetration of sealers, one study compared dentinal cracks, one study evaluated the amount of debris excluded apically, and one study compared the post-operative pain while using both techniques. The WVC and SC obturation techniques offer advantages and disadvantages in endodontic treatment. SC obturation is a simple and efficient procedure that is particularly suitable for situations with uncomplicated canal structures. The WVC obturation approach provides superior flexibility and sealing capability, especially in the complex root canal system. When choosing the method of treatment, it is important to take into account the patient's preferences, the clinician's experience, and unique considerations related to the situation. This systematic review highlights the important recommendations to healthcare professionals in selecting the most suitable obturation procedure based on the specific requirements of each clinical scenario. Research involving long-term follow-ups is required to get a better understanding of the outcomes of long-term goals. Clinical relevance: ability to educate clinicians regarding the best obturation technique between thermogenic and hydraulic. It directs the treatment decisions to maximize patient's comfort, minimize post-operative complications, and improve efficacy in endodontic practice.

Physicochemical Changes in Root-Canal Sealers under Thermal Challenge: A Comparative Analysis of Calcium Silicate- and Epoxy-Resin-Based Sealers

INTRODUCTION

We compared the effects of heat on the physicochemical properties of recently developed calcium silicate-based sealers (CSBSs), including BioRoot Flow, BioRoot RCS, and AH Plus Bioceramic sealer, with those of the epoxy-resin-based sealer (ERBS) AH Plus.

METHODS

The flow, film thickness, setting time, and solubility of sealers were evaluated at 37 °C and 100 °C using ISO 6876/2012. Furthermore, pH and calcium ion release were evaluated at these temperatures. In addition, the mass change in sealers at a high temperature was assessed via thermogravimetric analysis. Then, the chemical composition and components of the sealers were analyzed using a scanning electron microscope and Fourier-transform infrared spectroscopy (FTIR).

RESULTS

BioRoot Flow, AH Plus Bioceramic, and AH Plus complied with ISO standards in terms of flow and film thickness, both before and after heat application. However, BioRoot RCS exhibited significantly increased film thickness at 100 °C. The setting times of all sealers were significantly reduced at 100 °C. The solubility of CSBS was >3%, exceeding the ISO 6876/2012 standard, both before and after heat exposure. Conversely, the solubility of AH Plus complied with the standard, regardless of the thermal condition. For 4 weeks, CSBS showed a significantly higher pH than AH Plus at both 37 °C and 100 °C. After heat treatment, calcium release decreased in Bioroot RCS and BioRoot Flow, while AH Plus showed no significant differences before and after treatment. However, CSBS consistently exhibited significantly higher calcium release than AH Plus at both temperatures. An FTIR analysis revealed that the chemical composition of the sealers did not change at the high temperature, whereas a thermogravimetric analysis demonstrated a >5% weight reduction in CSBS and a 0.005% weight reduction in AH Plus at 100 °C.

CONCLUSIONS

BioRoot Flow, AH Plus Bioceramic, and AH Plus possess favorable physicochemical properties, which make them suitable for application under thermal conditions. At a high temperature, BioRoot RCS did not exhibit changes in its chemical composition. However, its film thickness was increased, and pH and solubility were reduced. Therefore, caution is needed when it is applied at high temperatures, such as during the warm obturation technique.

Heat-Induced Changes in the Physical Properties of a New Premixed Calcium Silicate-Containing Root Canal Sealer: An In Vitro Study

This study aimed to examine how heating affects the physical properties of a newly developed premixed calcium silicate-containing sealer (AH Plus Bioceramic Sealer; AHB), in comparison with EndoSequence BC Sealer (ES), AH Plus Jet (AH), and Pulp Canal Sealer. The setting time, flow, and film thickness were tested with or without heating at 100 °C for 30 or 60 s, in accordance with ISO6876:2012 standards. Ultrastructural and elemental analyses were performed with scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS). Data were analyzed using one-way analysis of variance (ANOVA) with a Tukey post hoc test (α = 0.05). All sealers exhibited significantly shorter setting time and flow after heating at 100 °C for 30 and 60 s (p < 0.05). After heating, AHB showed a significantly higher film thickness compared to that of the other materials (p < 0.05). None of the tested properties of heat-applied AHB and ES met ISO standards, except the setting time in ES. The SEM/EDS results for AHB and ES were not affected by heating. The detected changes in physical properties can negatively impact the performance of premixed calcium silicate-containing sealers, particularly AHB, when warm vertical compaction is employed.

Effect of heat application on the physicochemical properties of new endodontic sealers: an in vitro and SEM study

Understanding the properties of endodontic sealers is vital for treatment planning. Calcium silicate-based sealers are important in modern endodontics. This study investigates the effect of heat on the physicochemical properties of new calcium silicate sealers, addressing concerns raised by clinicians seeking to combine their benefits with the gutta-percha obturation technique. Five endodontic sealers (AH Plus Bioceramic®, Total Fill® BC®, One-fil® Bioceramic, K-Biocer, Any-seal®) were evaluated. Each sealer (n = 16/group) was either kept at 37 °C or subjected to heat at 60 or 200 °C for 30 s. ISO 6876-2012 standards were used to measure setting time, flow, film thickness, and dimensional changes over time. SEM and EDS were utilized for surface and chemical analysis. Data analysis employed IBM SPSS Statistics version 26 with a 5% significance level for two-sided tests. The sealers' setting times were shortened by heat, except for Total Fill® BC with extended setting time. All sealers had significantly longer setting times than manufacturer specifications. Film thickness increased with temperature, while flow values decreased. K-Biocer sealer showed the highest flow (16.89 ± 0.57 mm) at 200 °C, while Total Fill® sealer had the lowest (15.32 ± 0.62 mm). Shrinkage was significant at 60 °C and 200 °C, with greater shrinkage at 200 °C. Heat caused surface deformations in all sealers. The 200 °C groups exhibited more voids in AH Plus Bioceramic®, Any-seal®, and One-fil® sealers, and higher void area in Total Fill®, One-fil®, and K-Biocer sealers (p value < 0.001). EDX analysis confirmed heat-induced chemical and elemental changes in all tested sealers. Elevated temperature affects the physicochemical properties and structure of the tested endodontic sealers. The consideration of endodontic sealer compatibility is essential when warm gutta-percha obturation techniques are used.

Comparative Evaluation of Push-out Bond Strength of Three Different Root Canal Sealers: An In Vitro Study

AIM

The aim of this present study was to compare the dislodgement resistance of calcium silicate-based sealer, zinc oxide sealer, and a new sealer combining both zinc oxide and calcium silicate-based sealer in vitro.

MATERIALS AND METHODS

60 single-rooted human teeth were instrumented with F3 Protaper Gold. All endodontic canals were filled using gutta percha cones using the cold lateral condensation technique in combination using one of the mentioned sealers (n = 20 per group). The teeth were divided into three groups: group A consisted of Sealite® Ultra, group B consisted of K-Sealer®, and group C consisted of BioRoot® RC. After 2 months of incubation (37°C, 100% humidity) and after cutting out 2 mm from the most apical portion of the root apex, six slices of 1 mm thickness were generated. Mechanical dislodgement resistance was examined using a universal pressure-testing machine and the push-out bond strength (POBS) was calculated. Specimens were examined under 20× magnification to define the bond failure mode. Statistical analysis was executed using ANOVA, post hoc Turkey test for pairwise comparisons and Kruskal-Wallis tests.

RESULTS

The POBS of BioRoot® was significantly higher than the POBS of the two other sealers with a mean of 10.54 MPa ± 2.10 and 5.73 MPa ± 2.34, respectively (p < 0.001). Sealite® and K-Sealer® showed similar results in the median and coronal part. K-Sealer® revealed highest POBS compared with Sealite® in the apical part (p < 0.05).

CONCLUSION

The POBS of the zinc oxide and calcium silicate-based sealer was significantly lower compared with calcium silicate. Sealite® and K-Sealer® exhibited almost same results. BioRoot showed the highest POBS of all sealers.

CLINICAL SIGNIFICANCE

The current study was needed to evaluate the bond strength of three different cements to dentinal walls, by evaluating their respective POBS in vitro. The findings of this study may provide guidance for the clinician in the selection of an adequate endodontic sealer that guarantees an enhanced adhesive seal between the Gutta-percha and the dentinal canal walls. How to cite this article: Makhlouf MP, El Helou JD, Zogheib CE, et al. Comparative Evaluation of Push-out Bond Strength of Three Different Root Canal Sealers: An In Vitro Study. J Contemp Dent Pract 2024;25(1):15-19.

Impact of Heating Exposure on the Micro-Push-Out Bond Strength of Bioceramic Sealers

Introduction

The aim of this study was to evaluate the effect of heating of bioceramic and epoxy resin-based sealers on their micro-push-out bond strength (BS) to root canal dentin.

Methods

After criterial selection, 30 human teeth were decoronated and 1-mm thick slices (n = 60) were obtained perpendicularly along tooth axis, from cervical and middle root thirds, with a diamond disc attached to a cutting machine. In each slice, three 1.0-mm diameter orifices were made. After rinsing with 17% EDTA and 2.5% NaOCl, each orifice was filled with Bio-C Sealer or BioRoot RCS or AH Plus, according to the manufacturers' instructions. After filling, half of the slices (n = 30) were heated at 100°C for 1 min, and the other half were kept at room temperature. After 7 days-controlled storage, micro-push-out test was performed in a Universal Testing Machine. Failures were analyzed using a stereomicroscope. Statistical analysis was performed with One-Way ANOVA and post hoc Tukey (α = 5%) tests.

Results

AH Plus demonstrated higher BS values after heating (p=0.001) when compared to nonheated. The other sealers did not show a statistically significant difference (p > 0.05). When heated, the average BS values for AH Plus were higher than for BioRoot RCS and Bio-C Sealer (p < 0.001). Cohesive failure mode was the most frequent, followed by adhesive and mixed ones.

Conclusion

Heating provided a higher push-out BS to root dentin for AH Plus and did not influence BioRoot RCS or Bio-C sealer.

Thermal, chemical and physical analysis of VDW.1Seal, Fill Root ST, and ADseal root canal sealers

This study aimed to evaluate the thermal, chemical, and physical properties of VDW.1Seal, Fill Root ST, and ADseal sealers. Thermal properties were analyzed using Thermogravimetric analysis (TGA) and Differential thermal analysis (DTA). Attenuated total reflection Fourier Transform Infrared Spectroscopy (ATR-FTIR) analysis was performed as a complementary test to confirm TGA/DTA analysis. The chemical composition of the set sealer material was identified using an X-ray powder diffraction (XRD) system. Other physical properties of each sealer were investigated; ten specimens were used to measure the solubility (at 24 h and 28 days), and another ten specimens were used to assess pH changes and calcium ion release (after 7 and 14 days). Film thickness was done according to ISO 6876 specs. The data were analyzed using the two-way ANOVA test. Results showed that for all sealers, TGA analysis revealed a direct relationship between sealer mass loss and temperature rise. In addition, the decomposition of the tested sealers started at 145 °C, 135 °C and 91 °C for VDW.1Seal, ADseal sealer, and Fill Root ST, respectively. XRD analysis revealed a higher degree of crystallinity for VDW.1Seal and ADseal. ADseal showed the least solubility; VDW.1Seal exhibited the highest alkalinity, calcium ion release, and the lowest film thickness.

Comparison of physico-chemical properties of zinc oxide eugenol cement and a bioceramic sealer

The aim of the present study was to compare the physico-chemical properties of EssenSeal with AH PLUS bioceramic and Pulp Canal Sealer EWT. Flow, solubility, film thickness, radiopacity and setting time were evaluated according to ISO 6876 (2012) specifications. External and cross-section surface characteristics were analysed under a scanning electron microscope. Statistical analysis was performed using Shapiro-Wilk's test, one-way ANOVA and the Tukey HSD test. All the sealers conformed to the ISO 6876 (2012) standards, except for the setting time for AH plus bioceramic, which exceeded more than 10% of the time indicated by the manufacturer. Statistically significant differences were found between the three study sealers regarding the physico-chemical properties tested (p < 0.05). EssenSeal demonstrated characteristics respecting the ISO 6876 (2012) standards and can be considered a predictable alternative in root canal sealing.

Comparison of obturation quality in natural and replica teeth root-filled using different sealers and techniques

OBJECTIVES

This study aims to assess the obturation efficacy of sealers placed with different techniques using microcomputed tomography (µCT) and assess the influence of µCT testing parameters on the obturation data obtained.

MATERIALS AND METHODS

Incisors and mesial roots of lower molars with standardized root length were scanned using µCT, and one tooth of each type was 3D printed in acrylic. Two obturation techniques (warm vertical and single cone) and 4 sealer types (AH Plus, BioRoot RCS, Totalfill BC, and Bio-C Sealers) were assessed following storage in Hank's balanced salt solution for 3 and 6 months by assessing gap and void volume percentages on both natural and replica incisor and molar roots. The storage solution was analysed to assess calcium ion leaching. The influence of temperature, tooth positioning, and moisture content of the teeth while µCT scanning was also investigated.

RESULTS

The obturation quality in the incisor group was the same using both natural teeth and replicas (p > 0.05). No changes in void volume were identified when comparing the same sealer using different obturation techniques. The premixed sealers used in single-cone obturation exhibited high void volume in the 3D printed replicas in the long term. The temperature, positioning, and moisture content of the teeth did not affect the outcome of µCT testing.

CONCLUSIONS

BioRoot RCS, Totalfill BC, and Bio-C Sealers are suitable for obturation of both complex and simple root canal systems using different obturation techniques with BioRoot RCS exhibiting the highest calcium ion release. 3D printed acrylic teeth can be used to assess the obturation quality in uncomplicated root canal systems. µCT parameters had no significant effect on the µCT measurement.

CLINICAL RELEVANCE

The single-cone obturation technique with hydraulic sealer is a simple technique that can be used for obturation of all root canal systems.

Analysis of physicochemical properties of endodontic sealers containing rhodamine B

The use of fluorescent dyes in microscopy studies is frequent. Therefore, it is important to investigate whether these compounds may alter the physicochemical properties of materials in which they are incorporated to avoid methodological biases. This study evaluated the physicochemical properties of two endodontic sealers containing dry or diluted rhodamine B. Six groups were evaluated: AH Plus and MTA Fillapex in their original composition and mixed with 0.1% dry or diluted rhodamine. Push-out test was applied to assess the bond strength to root dentin. ANSI-ADA No. 57 and ISO No. 6876:2012 specifications were followed to evaluate flowability, setting time, and solubility of the sealers. pH changes were assessed after 24 h, 7, and 30 days. Intergroup comparisons were analyzed by ANOVA complemented by Tukey's post-hoc test; comparisons among periods were analyzed by Wilcoxon and Friedman tests. The incorporation of dry rhodamine decreased the bond strength and prolonged the setting time of AH Plus. The incorporation of diluted rhodamine decreased the setting time and increased the flowability of MTA Fillapex. Diluted rhodamine promoted pH reduction of AH Plus after 24 h and dry rhodamine after 7 days. Rhodamine incorporation promoted pH reduction after 30 days for MTA Fillapex. Solubility was not affected. In conclusion, the incorporation of diluted rhodamine changed the properties of MTA Fillapex, and the incorporation of dry rhodamine changed the properties of AH Plus. Previous dilution of rhodamine did not severely compromise the physicochemical properties of AH Plus and may be suggested to assess its penetrability.

Interleukin-6, tumor necrosis factor-α, and CD5 immunolabeling of new experimental endodontic sealer and repair material

The aim of this study was to evaluate the biocompatibility and immunoinflammatory response of the Sealepox and Sealepox-RP, based on interleukin (IL)-6, tumor necrosis factor (TNF)-α, and CD5 immunolabelling. The ProRoot MTA (PRMTA) was used for comparison. Polyethylene tubes (1.0-mm internal, 1.6-mm external diameter, and 10.0-mm length; ISO 10993) with or without (control) materials were randomly implanted in the dorsum of 35 rats (4 per rat). After 7, 15, 30, 60, and 90 days (n = 7), the tubes were removed for histological and immunohistochemical analysis. The Kruskal-Wallis and Dunn's test for non-parametric data and, ANOVA and Tukey test for parametric data were used (P < 0.05). Hematoxylin and eosin staining revealed that the concentration of inflammatory cells decreased over time with no differences between groups in all periods (P > 0.05). Regarding IL-6 immunostaining, there was no difference at 7 days (P > 0.05); all groups decreased over time, being faster for the PRMTA group and also, with no differences between groups in the last period (P > 0.05). For TNF-α, at 7 days there was no difference between groups (P > 0.05); there was an increase at 15 days for PRMTA and, at 30 and 60 days, for PRMTA and Sealepox compared to the control (P < 0.05). At 90 days, Sealepox RP showed the lowest immunostaining being similar to the control (P > 0.05). Regarding CD5 cells, at 7 days, there was high immunostaining for PRMTA compared to the control (P < 0.05); and significant reduction over time with difference for all groups at 30 and 60 days. (P < 0.05); Sealepox was similar to the control in all periods (P > 0.05). Sealepox RP showed the highest immunostaining at 15 days, being different from the control and PRMTA (P < 0.05); in the other periods it was similar to the control (P > 0.05). It can be concluded that Sealepox and Sealepox-RP were biocompatible and demonstrated similar immunoinflammatory response regarding IL-6, TNF-α, and CD5 compared to PRMTA.

Short and Long-Term Solubility, Alkalizing Effect, and Thermal Persistence of Premixed Calcium Silicate-Based Sealers: AH Plus Bioceramic Sealer vs. Total Fill BC Sealer

This study aimed to investigate the short- and long-term solubility, alkalizing potential, and suitability for warm-vertical compaction of AH Plus Bioceramic Sealer (AHBC), and Total Fill BC Sealer (TFBC) compared to the epoxy-resin sealer AH Plus (AHP). A solubility test was performed according to ISO specification 6876 and further similar to ISO requirements over a period of 1 month in distilled water (AD) and 4 months in phosphate-buffered saline (PBS). The pH of the immersion solution was determined weekly. Sealers were exposed to thermal treatment at 37, 57, 67, and 97 °C for 30 s. Furthermore, heat treatment at 97 °C was performed for 180 s to simulate inappropriate implementation of warm vertical filling techniques. Physical properties (setting time, flow, film thickness according to ISO 6876) and chemical properties (Fourier transformed infrared spectroscopy) were assessed. AHBC and TFBC were associated with significantly higher solubility than AHP over 1 month in AD and 4 months in PBS (p < 0.05). AHBC and TFBC both reached high initial alkaline pH, while TFBC was associated with a longer-lasting alkaline potential than AHBC. Initial pH of AHBC and TFBC was higher in AD than in PBS. None of the sealers were compromised by thermal treatment.

Hydration Characterization of Two Generations of MTA-Based Root Canal Sealers

Since the setting characterization of a root canal sealer has an impact on its biological behavior of final obturation, this study evaluated the setting characterization of mineral trioxide aggregate MTA-Fillapex versus MTA-Bioseal compared with epoxy resin (Adseal) root canal sealers. Freshly mixed sealer was inserted into the mold (n = 10). The initial and final setting times were evaluated using a Vicat needle and were then statistically analyzed by one-way ANOVA at p < 0.05. The raw pastes and the stages of the setting reaction were analyzed using Fourier Transform Infrared (FTIR) Spectroscopy. The phase compositions were evaluated using X-ray diffraction (XRD). A significant and fast setting time was recorded by Adseal (4.7 ± 0.46 h) followed by MTA-Bioseal (11.4 ± 1.34 h) at p < 0.001. The MTA-Fillapex did not set completely in three months. The FTIR and XRD of both MTA-Bioseal and Adseal detected bands of the polymerized phases, while those of MTA-Fillapex detected partial polymerization with a low percentage of polymerized silica. MTA-Bioseal and Adseal met the ISO standards for setting times. However, MTA-Fillapex did not fulfill the ideal requirement for the sealer. Although the raw pastes of both MTA-sealers had nearly similar compositions, they behaved differently during the hydration reaction. MTA-Bioseal set completely, while MTA-Fillapex was not completely set.

Minimal Dentinal Tubule Penetration of Endodontic Sealers in Warm Vertical Compaction by Direct Detection via SEM Analysis

Sealer staining using rhodamine B dye to investigate the penetration depth of endodontic sealers was proven unsuitable for this purpose. This study aimed to investigate the sealer penetration depth into dentinal tubules by scanning electron microscopy (SEM). Root canals of 52 human upper central incisors were instrumented using the ProTaper Gold NiTi system (Dentsply Sirona, York, PA, USA) up to size F3. After irrigation with sodium hypochlorite and citric acid combined with ultrasonic activation, the root canals were either filled using the epoxy resin sealer AH Plus (Dentsply Sirona) or the calcium silicate-based sealer Total Fill BC Sealer HiFlow (TFHF, FKG Dentaire, La Chaux-de-Fonds, Switzerland) by warm vertical compaction. Root slices of 1 mm thickness were obtained at 2 to 3, 5 to 6 and 8 to 9 mm from the apex. The root slices were investigated for sealer penetration into the dentinal tubules using SEM according to four root quadrants (buccal, mesial, oral, distal). Statistical analysis was performed by the Kruskal-Wallis test (p = 0.05) as data were not normally distributed according to the Shapiro-Wilk test. AH Plus penetrated significantly deeper into the dentinal tubules compared to TFHF at each root level (p < 0.05). Dentinal sealer penetration was deeper in the bucco-oral direction compared to the mesio-distal direction. AH Plus penetrated deeper into dentinal tubules than TFHF. Warm vertical compaction exerting high pressure on the root canal filling material is not able to press sealers deep into dentinal tubules as penetration depth values did not exceed a mean of 110 µm in SEM.

The Structural, Physical, and In Vitro Biological Performance of Freshly Mixed and Set Endodontic Sealers

Objective:

The objective of this study was to evaluate the in vitro performance of endodontic sealers in their freshly mixed and set forms.

Methods:

The commercially used endodontic sealers (AH Plus, Dia-ProSeal, GuttaFlow 2, and Pulpdent Root Canal Sealer) were investigated and the chemical structure of freshly mixed and set sealers were assessed with Fourier transform infrared spectroscopy (FTIR). The surface morphology and elemental analysis were assessed with a scanning electron microscope (SEM) equipped with energy-dispersive X-ray spectroscopy. The pH and solubility analysis were performed and the cytotoxicity was done on extracts of freshly mixed and set materials using Alamar blue assay. One way ANOVA and Post Hoc Tukey analysis was used to do multiple comparison analysis of the mean values and standard deviation results through SPSS version 20 (IBM Software, NY, USA) for pH, solubility, and cytotoxicity analysis.

Results:

FTIR analysis revealed the structural pattern and the difference in freshly mixed and set samples was observed with the change in intensities of the peaks. The morphological pattern revealed the presence of micro/nano-particles with pores distributed throughout their structure. The sealer with the least solubility was AH Plus (0.10±0.01) followed by Dia-ProSeal (0.77±0.25), GuttaFlow 2 (1.88±0.82) and Pulpdent Root Canal Sealer (3.03±0.18). The solubility of AH plus was significantly lower (P<0.05) in comparison to GuttaFlow 2 and Pulpdent Root Canal Sealer. The highest pH (10.09±0.034) in the freshly mixed state and highest cytotoxicity in the freshly mixed (70.08±5.852) and set sealers (83.87±5.409) (P<0.05) at day 7 was observed in Dia-ProSeal. GuttaFlow 2 was the most biocompatible sealer in the set state and AH Plus was the most biocompatible sealer in the freshly mixed state at day 7.

Conclusion:

Clinically, the sealer is applied in fresh state, whereby this study signifies that which material is more biocompatible in fresh state and provides insight information to clinicians. AH Plus showed least solubility and cytocompatibility in fresh state compared to other groups.

Physico-Chemical Investigation of Endodontic Sealers Exposed to Simulated Intracanal Heat Application: Hydraulic Calcium Silicate-Based Sealers

The aim of this study was to gain information about the effect of thermal treatment of calcium silicate-based sealers. BioRoot RCS (BR), Total Fill BC Sealer (TFBC), and Total Fill BC Sealer HiFlow (TFHF) were exposed to thermal treatment at 37 °C, 47 °C, 57 °C, 67 °C, 77 °C, 87 °C and 97 °C for 30 s. Heat treatment at 97 °C was performed for 60 and 180 s to simulate inappropriate application of warm obturation techniques. Thereafter, specimens were cooled to 37 °C and physical properties (setting time/flow/film thickness according to ISO 6876) were evaluated. Chemical properties (Fourier-transform infrared spectroscopy) were assessed after incubation of the specimens in an incubator at 37 °C and 100% humidity for 8 weeks. Statistical analysis of physical properties was performed using the Kruskal-Wallis-Test (P = 0.05). The setting time, flow, and film thickness of TFBC and TFHF were not relevantly influenced by thermal treatment. Setting time of BR decreased slightly when temperature of heat application increased from 37 °C to 77 °C (P < 0.05). Further heat treatment of BR above 77 °C led to an immediate setting. FT-IR spectroscopy did not reveal any chemical changes for either sealers. Thermal treatment did not lead to any substantial chemical changes at all temperature levels, while physical properties of BR were compromised by heating. TFBC and TFHF can be considered suitable for warm obturation techniques.

Effects of heating on the physical properties of premixed calcium silicate-based root canal sealers

The purpose of this study was to examine the effect of heating on the physical properties of four types of premixed calcium silicate-based root canal sealers. Endoseal MTA, Well-Root ST, EndoSequence BC Sealer, EndoSequence BC Sealer HiFlow, and AH Plus (epoxy resin root canal sealer) were heated at 100°C for 1 min, and changes in setting time, flow, and film thickness were evaluated in accordance with ISO 6876:2012 standards. In addition, pH measurement and scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) analyses of the set materials were performed. All root canal sealers heated at 100°C showed significant decreases in setting time and flow, particularly Endoseal MTA. In addition, the film thickness of Endoseal MTA increased significantly after heating at 100°C. The pH and SEM/EDS results were not affected by heating. Heating calcium silicate-based root canal sealers accelerated setting time, decreased flow, and increased film thickness. However, the degree of these changes varied among the products. The present findings indicate that heat-induced changes in the physical properties of calcium silicate-based root canal sealers could adversely affect the quality of warm vertical condensation technique.

Filling Ability and Flow of Root Canal Sealers: A Micro-Computed Tomographic Study

This study evaluated by micro-computed tomography (μCT) the filling ability in curved root canals, besides the flow of AH Plus (AHP) and Neo MTA Plus (NMTAP) sealers using different methodologies. Mandibular molars mesial roots with two root canals and degree of curvature between 20° and 40° were selected. The specimens were prepared with the ProDesign R system up to size 35.05 and were filled with the sealers by a continuous wave of condensation technique, Thermo Pack II (n=12). The teeth were scanned using μCT after root canal preparation and obturation. The volumetric percentage of filling material and voids were calculated. Flow was evaluated based on ISO 6876/2012 (n=10). Flow and filling were also evaluated in μCT using a glass plate with a central cavity and four grooves from the central cavity (n=6). Flow was linearly calculated into the grooves. The central cavity filling (CCF) and lateral cavity filling (LCF) were calculated in mm³. Data were submitted to non-paired t test with a significance threshold at 5%. The percentage of filling and voids between the root canals filled with AHP or NMTAP was similar (p>0.05). NMTAP presented the lowest flow in conventional test (p<0.05). Using μCT, sealers had similar CCF, LCF and linear flow (p>0.05). In conclusion, NMTAP and AHP had similar filling ability in curved mesial root canals of mandibular molars without presence of isthmus. Although AHP presented better flow than NMTAP using ISO methodology, there was no difference between these materials regarding volumetric filling when evaluated by μCT.