Laboratory simulation of longitudinally cracked teeth using the step-stress cyclic loading method

Biomechanics, Bioactive and Biomimetic philosophy in restorative dentistry ̶ Quo vadis?

INTRODUCTION

In recent years, restorative dentistry has embraced various techniques, including direct, semi-direct, and indirect restorations, to address the replacement of lost tooth tissue. The focus has been on integrating the principles of Biomechanics, Bioactivity, and Biomimicry (3-Bio) as key drivers behind these innovations.

METHODS

The aim of this article is to provide a concise overview of three important aspects of restorative dental materials: biomechanics, bioactivity and biomimetics. Further, the aim is to provide readers with relevant information on the 3-Bio concept, offering insights in to the innovative approaches shaping modern restorative dentistry.

RESULTS

Developing restorative materials with interactive properties aligned with the 3-Bio concept poses a significant challenge. Currently, dentistry lacks a comprehensive system in this regard. The development of dental materials based on the 3-Bio concept could potentially elicit positive mechanical and biological responses in targeted tooth tissues.

CONCLUSION

Assessing several parameters through a battery of in vitro and in silico assays could help in tailoring the different aspects of the 3-Bio concept, spanning from bioactivity to biomimetics via biomechanics. This approach could allow the prediction and translation of the clinical performance of the assessed restorative materials.

CLINICAL SIGNIFICANCE

The findings of this opinion article highlight that the development of restorative materials aligned with the 3-Bio concept could enhance the management of dental defects and extend the longevity of bonded restorations, thereby improving patient care through tissue preservation. More collective efforts between clinicians, researchers, and even industrial partners are required to fully understand the correlation between bioactive behavior, biomechanical limitations, and biomimetics to provide suitable restorative materials for specific clinical applications.

A critical analysis of research methods and experimental models to study the load capacity and clinical behavior of the root filled teeth

The prognosis of root‐filled teeth depends not only on a successful root canal treatment but also on the restorative prognosis. This critical review discusses the advantages and limitations of various methodologies used to assess the load capacity or clinical survivability of root‐filled teeth and restorations. These methods include static loading, cyclic loading, finite element analysis and randomized clinical trials. In vitro research is valuable for preclinical screening of new dental materials or restorative modalities. It also can assist investigators or industry to decide whether further clinical trials are justified. It is important that these models present high precision and accuracy, be reproducible, and present adequate outcomes. Although in vitro models can reduce confounding by controlling important variables, the lack of clinical validation (accuracy) is a downside that has not been properly addressed. Most importantly, many in vitro studies did not explore the mechanisms of failure and their results are limited to rank different materials or treatment modalities according to the maximum load capacity. An extensive number of randomized clinical trials have also been published in the last years. These trials have provided valuable insight on the survivability of the root‐filled tooth answering numerous clinical questions. However, trials can also be affected by the selected outcome and by intrinsic and extrinsic biases. For example, selection bias, loss to follow‐up and confounding. In the clinical scenario, hypothesis‐based studies are preferred over observational and retrospective studies. It is recommended that hypothesis‐based studies minimize error and bias during the design phase.

Fatigue analysis of restored teeth longitudinally cracked under cyclic loading

OBJECTIVE

To investigate the fatigue behavior of restored teeth, in particular the mechanisms of longitudinal dentinal cracking under cyclic mechanical loading, using finite element analysis (FEA) and the stress-life (S-N) approach.

METHODS

Ten root-filled premolars restored with resin composites were subjected to step-stress cyclic loading to produce longitudinal cracks. Fracture loads and number of cycles completed at each load level were recorded. FEA was used to predict the stress amplitude of each component under the global cyclic load. Both intact and debonded conditions were considered for the dentin-composite interface in the FEA. The predicted stress concentrations were compared with the fracture patterns to help elucidate the failure mechanisms. The S-N approach was further used to predict the lifetimes of the different components in the restored teeth. Cumulative fatigue damage was represented by the sum of the fractions of life spent under the different stress amplitudes.

RESULTS

Longitudinal cracks were seen in ~50% of the samples with a mean fracture load of 770 ± 45 N and a mean number of cycles to failure of 32,297 ± 12,624. The longitudinal dentinal cracks seemed to start near the line angle of the cavity, and propagated longitudinally towards the root. The sum of fractions of life spent for the dentin-composite interface exceeded 1 after ~7000 cycles when that for dentin was much lower than 1, indicating that interfacial debonding would occur prior to dentin fracture. This was supported by micro-CT images showing widened interfacial space in the cracked samples. In the debonded tooth, FEA showed dentinal stress concentrations at the gingival wall of the cavity, which coincided with the longitudinal cracks found in the cyclic loading test. The sum of fractions of life spent for dentin was close to 1 at ~30,000 cycles, similar to the experimental value.

SIGNIFICANCE

Debonding of the dentin-composite interface may occur prior to longitudinal cracking of dentin in root-filled teeth under cyclic loading. The approximate time of occurrence for these events could be estimated using fatigue analysis with stresses provided by FEA. This methodology can therefore be used to evaluate the longevity of restoration designs for root-filled teeth.