Quantitative analysis of allergenic ingredients in eluate extracted from used denture base resin

Elution characteristics of residual monomers in different light- and auto-curing resins

The aim of this in vitro study was to assess different auto-curing resins based on methylmethacrylate (MMA) and new light-curing resins based on urethane dimethacrylate (UDMA) regarding the residual monomers remaining in the resin and their elution over time. Specimens from three auto-curing and three light-curing resins were produced following the manufacturer's instructions. The concentration of residual MMA and UDMA monomers present in the resins as well as the quantity of the residual monomers released into artificial saliva solution after immersion times of 1, 3, and 7 days were analyzed by high-performance liquid chromatography (HPLC). Data were statistically analyzed using ANOVA and the post hoc Student-Newman-Keuls test. The highest and lowest amounts of residual monomers were found in the group of light-curing resins (p<0.05). The light-curing resins Triad Trans Sheet (0.06 wt%) and Primosplint (0.06 wt%) released over the entire immersion time of 7 days the smallest (p<0.05) quantity of UDMA. These two light-curing resins based on UDMA exhibited lower elution of residual monomers than auto-curing resins (MMA). The elution characteristics of the residual monomers do not seem to correlate with the residual monomer concentration in resins. These observations demonstrate that the quantitative determination of residual monomers alone - as required by the ISO specification 20795-1 - does not seem to be sufficient for an assessment of the biological properties of different resins. Instead, the evaluation of elution characteristics appears to be of higher clinical relevance.

Identification and quantification of leachable substances from polymer-based orthodontic base-plate materials

The aim of this study was to analyse leachable monomers, additives, and degradation products from polymer-based orthodontic base-plate materials. One heat-cured resin (Orthocryl), one light-cured (Triad VLC), and three thermoplastic materials (Biocryl C, Essix A+, and Essix Embrace) were investigated. Elution was performed in water at 37°C for 10 days. The extract medium was changed and analysed daily. Chromatographic methods were used to identify and quantify the leachables. In addition, the content of residual methyl methacrylate (MMA) was quantified in the poly(methyl methacrylate) (PMMA)-based materials. Statistical analysis of the quantitative results was performed using a t-test for comparison of two independent samples. Monomers and additives leached from the materials polymerized in situ and from the thermoplastic PMMA-based material. No leachable substances were found in the extracts from the other thermoplastic materials. Accumulated over 10 days, a larger amount of MMA leached from the powder-and-liquid material, Orthocryl (42 μg/cm(2)), than from the thermoplastic material, Biocryl C (0.49 μg/cm(2)). The accumulated amounts of monomers leached from Triad VLC were 91 μg/cm(2) of urethane dimethacrylate and 2.2 μg/cm(2) of 2-hydroxyethyl methacrylate. Formaldehyde was found to leach from methacrylate-based materials: 3.2 μg/cm(2) from Orthocryl and 0.16 μg/cm(2) from Triad VLC. However, formaldehyde was not detectable in extracts from Biocryl C. Residual MMA was 5.4 wt % in Orthocryl and 0.4 wt % in Biocryl C. No phthalates were detected in the tested materials. In this in vitro study, minimal leaching was found from the thermoplastic materials, while leaching of methacrylates and formaldehyde was observed from the powder-and-liquid type and the paste material. Within the limitations of this study, the results suggest that prefabricated thermoplastic plates should be preferred for patients with an allergy to methacrylates.