Effects of bond primers on bending strength and bonding of glass fibers in fiber-embedded maxillofacial silicone prostheses

Using Peek as a Framework Material for Maxillofacial Silicone Prosthesis: An In Vitro Study

There are often bonding problems between acrylic resins and silicone. PEEK (polyetheretherketone), which is a high-performance polymer, has great potential for the implant, and fixed or removable prosthodontics. The aim of this study was to evaluate the effect of different surface treatments on PEEK to be bonded to maxillofacial silicone elastomers. A total of 48 specimens were fabricated from either PEEK or PMMA (Polymethylmethacrylate) (n = 8). PMMA specimens acted as a positive control group. PEEK specimens were divided into five study groups as surface treatments as control PEEK, silica-coating, plasma etching, grinding, or nano-second fiber laser. Surface topographies were evaluated by scanning electron microscopy (SEM). A platinum-primer was used on top of all specimens including control groups prior to silicone polymerization. The peel bond strength of the specimens to a platinum-type silicone elastomer was tested at a cross-head speed of 5 mm/min. The data were statistically analyzed (α = 0.05). The control PEEK group showed the highest bond strength (p < 0.05) among the groups. No statistical difference was found between control PEEK, grinding, or plasma etching groups (p > 0.05). The lowest bond strength was seen in the laser group, which was not statistically different from silica-coating (p > 0.05), and statistically different from control PEEK, grinding, or plasma groups (p < 0.05). Positive control PMMA specimens had statistically lower bond strength than either control PEEK or plasma etching groups (p < 0.05). All specimens exhibited adhesive failure after a peel test. The study results indicate that PEEK could serve as a potential alternative substructure for implant-retained silicone prostheses.

Comparison and Impact of Different Fiber Debond Techniques on Fiber Reinforced Flexible Composites

The focus of this paper is the realization and verification of a modified fiber bundle pull-out test setup to estimate the adhesion properties between threads and elastic matrix materials with a more realistic failure mode than single fiber debond techniques. This testing device including a modified specimen holder provides the basis for an adequate estimation of the interlaminar adhesion of fiber bundles including the opportunity of a faster, easier, and more economic handling compared to single fiber tests. The verification was done with the single-fiber and microbond test. Overall, the modified test setup showed the typical pull-out behavior, and the relative comparability between different test scales is given.

An overview of development and status of fiber-reinforced composites as dental and medical biomaterials

Fibr-reinforced composites (FRC) have been used successfully for decades in many fields of science and engineering applications. Benefits of FRCs relate to physical properties of FRCs and versatile production methods, which can be utilized. Conventional hand lamination of prefabricated FRC prepregs is utilized still most commonly in fabrication of dental FRC devices but CAD-CAM systems are to be come for use in certain production steps of dental constructions and medical FRC implants. Although metals, ceramics and particulate filler resin composites have successfully been used as dental and medical biomaterials for decades, devices made out of these materials do not meet all clinical requirements. Only little attention has been paid to FRCs as dental materials and majority of the research in dental field has been focusing on particulate filler resin composites and in medical biomaterial research to biodegradable polymers. This is paradoxical because FRCs can potentially resolve many of the problems related to traditional isotropic dental and medical materials. This overview reviews the rationale and status of using biostable glass FRC in applications from restorative and prosthetic dentistry to cranial surgery. The overview highlights also the critical material based factors and clinical requirement for the succesfull use of FRCs in dental reconstructions.

Effect of light aging on silicone-resin bond strength in maxillofacial prostheses

PURPOSE

The aim of this study was to investigate the effect of accelerated light aging on bond strength of a silicone elastomer to three types of denture resin.

MATERIALS AND METHODS

A total of 60 single lap joint specimens were fabricated with auto-, heat-, and photopolymerized (n = 20) resins. An addition-type silicone elastomer (Episil-E) was bonded to resins treated with the same primer (A330-G). Thirty specimens served as controls and were tested after 24 hours, and the remaining were aged under accelerated exposure to daylight for 546 hours (irradiance 765 W/m(2) ). Lap shear joint tests were performed to evaluate bond strength at 50 mm/min crosshead speed. Two-way ANOVA and Tukey's test were carried out to detect statistical significance (p < 0.05).

RESULTS

ANOVA showed that the main effect of light aging was the most important factor determining the shear bond strength. The mean bond strength values ranged from 0.096 to 0.136 MPa. The highest values were recorded for auto- (0.131 MPa) and photopolymerized (0.136 MPa) resins after aging.

CONCLUSIONS

Accelerated light aging for 546 hours affects the bond strength of an addition-type silicone elastomer to three different denture resins. The bond strength significantly increased after aging for photo- and autopolymerized resins. All the bonds failed adhesively.