Scanning microradiographic study on the influence of diffusion in the external liquid on the rate of demineralization in hydroxyapatite aggregates

The effect of occlusal loading on cervical gap deformation: A 3D finite element analysis

OBJECTIVES

Secondary caries can be accelerated by hydrodynamic flow in a gap between the tooth and restorative material. This study investigated whether occlusal loading can lead to increased hydrodynamic flow by deforming a gap between tooth and restorative material.

METHODS

3D finite element analysis was employed to model a molar containing a restoration with an interfacial gap. The model was loaded using direct cusp-to-restoration contact and using a rubber tube model simulating a food bolus. The object exerting pressure was moved across the molar from buccal to lingual side. The applied forces were 50, 100, 200 and 400N. The elastic modulus of the restoration material was varied between 5, 10, 15.9 and 25GPa to resemble different kinds of composite. The primary outcome parameter was the volume of the gap under occlusal pressure.

RESULTS

Occlusal loading resulted in deformation of the gap area. Maximum deformation was seen when loading was applied in the middle of the restoration. Higher forces and lower restoration stiffness led to more deformation of the gap. Maximum deformation with a force of 100N and composite modulus of 15.9GPa was -0.0083mm³ (1.12%).

SIGNIFICANCE

Deformation of the gap between tooth and restorative material could lead to increased hydrodynamic flow and faster secondary caries lesion formation. The measured deformation is small. Further research needs to show whether gap compression through occlusal loading affects secondary caries formation to a clinically relevant degree.

Validation of a Real-Time ISE Methodology to Quantify the Influence of Inhibitors of Demineralization Kinetics in vitro Using a Hydroxyapatite Model System

The aim was to validate a novel protocol to measure the cariostatic efficacies of demineralization inhibitors by repeating previous SMR (scanning microradiography) studies investigating the dose response of Zn2+ and F- on demineralization kinetics in vitro using real-time Ca2+ ion selective electrodes (ISEs). In this study, Ca2+ release was used as a proxy for the extent of demineralization. Forty-eight hydroxyapatite (HAP) discs were allocated into 16 groups (n = 3) and adding either increasing [Zn2+], or [F-], similar to those used in the previous SMR studies. Each HAP disc was immersed in 50 mL, pH 4.0, buffered acetic acid for 1 h, and real-time ISE methodology was used to monitor the rate of increase in [Ca2+] in the demineralization solution. Next, either zinc acetate or sodium fluoride was added into each demineralization solution accordingly. Then after each [Zn2+] or [F-] addition, the HAP disc was further demineralized for 1 h, and ISE measurements were continued. The percentage reduction in the rate of calcium loss from hydroxyapatite (PRCLHAP) at each [Zn2+] or [F-] was calculated from the decrease in Ca2+ release rate, similar to that used in the previous SMR studies. A log-linear relationship between mean PRCLHAP and inhibitor concentration was found for both Zn2+ and F-, similar to that reported for each ion in the previous SMR studies. In conclusion, real-time Ca2+ ISE systems can be used to measure the cariostatic efficacies of demineralization inhibitors.

On the initial propagation of dental caries

A multi-dimensional model for dental caries is applied to study the shape of caries lesions in a realistic tooth geometry and to examine the rate of progress of caries. An upgraded model, taking into account the outer prismless enamel layer, is derived and solved. The model demonstrates the importance of this layer in delaying the onset of caries. The conclusions are discussed in light of experimental results.

Hydrodynamic Flow through Loading and in vitro Secondary Caries Development

This in vitro study investigated the effect of hydrodynamic flow through mechanical loading on development of secondary caries lesions. Forty-eight bovine tooth specimens (enamel and dentin; sizes 3.2 x 3.2 x 2.0 mm) were restored with resin-composite on polystyrene bars; 18 samples were bonded, and 30 were not bonded. Specimens were suspended in a lactic acid solution (pH = 5; 14 days) in a modified brushing machine, and artificial caries lesions were formed. During caries development, specimens were mechanically loaded at the surface of the polystyrene bar, bent so that the tooth- composite interfaces were subjected to opening forces (16x/min). Loads applied were either none (Control Bonded, CB, n = 6; and Control Non-bonded, CNB, n = 6), 200 gr (NB200, n = 12), or 350 gr (NB350 and B350, both n = 12). Before and after caries development, specimens were imaged with transverse wavelength-independent microradiography (T-WIM), and lesion depth (LD) and mineral loss (ML) were calculated at 4 different locations. An independent t test was used to compare the LD and ML at the 4 different locations. A statistically significant effect of the level of loading (comparing groups NB200 and NB350) and of bonding (comparing groups NB350 and B350) could be observed, with a higher load and absence of bonding leading to more advanced lesions.