Multiple Cuspal-Coverage Direct Composite Restorations: Functional and Esthetic Guidelines

Fatigue performance of endodontically treated premolars restored with direct and indirect cuspal coverage restorations utilizing fiber-reinforced cores

Objectives

The aim of this in vitro study was to investigate the fatigue survival and fracture behavior of endodontically treated (ET) premolars restored with different types of post-core and cuspal coverage restorations.

Materials and methods

MOD cavities were prepared on 108 extracted maxillary premolars. During the endodontic treatment, all teeth were instrumented with rotary files (ProTaper Universal) to the same apical enlargement (F2) and were obturated with a matched single cone obturation. After the endodontic procedure, the cavities were restored with different post-core and overlay restorations (n = 12/group). Three groups (A1–A3) were restored with either conventional composite core (PFC; control) or flowable short-fiber-reinforced composite (SFRC) core with/without custom-made fiber posts and without overlays. Six groups had similar post-core foundations as described above but with either direct PFC (B1–B3) or indirect CAD/CAM (C1–C3) overlays. Fatigue survival was tested for all restorations using a cyclic loading machine until fracture occurred or 50,000 cycles were completed. Kaplan-Meyer survival analysis was conducted, followed by pairwise post hoc comparisons.

Results

None of the restored teeth survived all 50,000. Application of flowable SFRC as luting-core material with fiber post and CAD/CAD overlays (Group C3) showed superior performance regarding fatigue survival (p < 0.05) to all the other groups. Flowable SFRC with fiber post and direct overlay (Group B3) showed superior survival compared to all other direct techniques (p < 0.05), except for the same post-core foundation but without cuspal coverage (Group A3).

Conclusions

Custom-made fiber post and SFRC as post luting core material with or without cuspal coverage performed well in terms of fatigue resistance and survival when used for the restoration of ET premolars.

Clinical relevance

The fatigue survival of direct and indirect cuspal coverage restorations in ET MOD premolars is highly dependent on whether the core build-up is fiber-reinforced or not. The combination of short and long fibers in the form of individualized post-cores seems to offer a favorable solution in this situation.

Evaluation of the Bond Strength and Cytotoxicity of Alkasite Restorative Material

Cention N (CN; Ivoclar Vivadent, Schaan, Liechtenstein), advertised as an alkasite, is a bioactive bulk-fill resin-based composite (BF-RBC) with alkaline fillers. This study evaluated the resin-dentin micro-tensile bond strength (μTBS) and cytotoxicity of CN. Methods: Flat dentin surfaces were obtained, bonded with a universal adhesive, and randomly distributed into two groups. CN (group I) and a flowable BF-RBC, namely, Tetric N-Flow Bulk Fill, Ivoclar Vivadent, Schaan, Liechtenstein (group II), were used. After thermocycling, bonded samples were sectioned into micro-beams for μTBS evaluation. Resin-based composite (RBC) discs with a thickness of 2 and 4 mm were tested on human gingival fibroblast cells (HGFCs). Cytotoxicity was assessed by cell viability and growth using AlamarBlue® (Biosource, Camarillo, CA, USA) over a seven-day period. Independent t-test was utilized to statistically analyze μTBS data, while one- and two-way analysis of variance (ANOVA) and Tukey’s post-hoc tests were utilized to analyze the cell viability data. Results: There was no statistically significant difference (p > 0.05) in the μTBS between the flowable BF-RBC and CN. For both materials, the HGFCs were viable, with constant growing over the seven-day period. Conclusion: CN provided a resin-dentin μTBS that was comparable to that provided by the flowable BF-RBC. Both materials showed acceptable cytotoxicity over the seven-day period at a thickness of both 2 and 4 mm.

Fracture resistance of root filled premolar teeth restored with direct composite resin with or without cusp coverage

AIM

To evaluate the fracture resistance and fracture patterns of root filled maxillary first premolar teeth (with mesio-occlusal cavity preparation) restored with several composite restoration designs.

METHODOLOGY

One hundred extracted sound human maxillary first premolars were randomly divided into five groups. Group 1 remained untreated (negative control). Conventional root canal treatment with additional mesial-occlusal cavity preparation was carried out on teeth in groups 2-5. In group 2, the teeth were restored intra-coronally with direct composite resin (positive control). In group 3, the palatal cusps of the teeth were reduced, and the cavities were restored with composite resin covering the palatal cusp (partial coverage). In group 4, the buccal and palatal cusps along with the distal marginal ridges were reduced; the cavities and cusps were restored with composite resin (conventional full coverage). In group 5, the buccal and palatal cusps were reduced but the distal marginal ridges were conserved. The cavities and the cusps were restored with composite resin (modified full coverage). All teeth were subjected to a progressive compressive loading parallel to their longitudinal axis until fracture. Fracture resistance was analysed using the one-way ANOVA and Fisher's LSD test. Fracture patterns were analyzed with chi-square test. The significance level was set at 0.05.

RESULTS

The fracture resistance (mean ± SD) of groups 1-5 was 1131 ± 207N, 904 ± 184N, 927 ± 224N, 1095 ± 289N and 1085 ± 243N, respectively (groups 1, 4, 5 > groups 2, 3; P = 0.004). Cusp fractures were recorded as the fracture pattern in 20 (100%), 19 (95%), 16 (80%), 8 (40%) and 12 (60%) premolars in groups 1-5, respectively (groups 1, 2 > groups 4, 5; group 3 > group 4; P < 0.001).

CONCLUSIONS

When direct composite resin was used to restore root filled maxillary first premolar teeth involving a proximal surface, those restored with full-coverage designs had greater fracture resistance.