Color stability of mineral trioxide aggregate and calcium enriched mixture cement

Mineral trioxide aggregate and other bioactive endodontic cements: an updated overview - part II: other clinical applications and complications

Mineral trioxide aggregate (MTA) is a dental material used extensively for vital pulp therapies (VPT), protecting scaffolds during regenerative endodontic procedures, apical barriers in teeth with necrotic pulps and open apices, perforation repairs as well as root canal filling and root-end filling during surgical endodontics. A number of bioactive endodontic cements (BECs) have recently been introduced to the market. Most of these materials have calcium and silicate in their compositions; however, bioactivity is a common property of these cements. These materials include the following: BioAggregate, Biodentine, BioRoot RCS, calcium-enriched mixture cement, Endo-CPM, Endocem, EndoSequence, EndoBinder, EndoSeal MTA, iRoot, MicroMega MTA, MTA Bio, MTA Fillapex, MTA Plus, Neo MTA Plus, Ortho MTA, Quick-Set, Retro MTA, Tech Biosealer, and TheraCal LC. It has been claimed that these materials have properties similar to those of MTA but without the drawbacks. In Part I of this review, the available information on the chemical composition of the materials listed above was reviewed and their applications for VPT was discussed. In this article, the clinical applications of MTA and other BECs will be reviewed for apexification, regenerative endodontics, perforation repair, root canal filling, root-end filling, restorative procedures, periodontal defects and treatment of vertical and horizontal root fractures. In addition, the literature regarding the possible drawbacks of these materials following their clinical applications is reviewed. These drawbacks include their discolouration potential, systemic effects and retreatability following use as a root filling material. Based on selected keywords, all publications were searched regarding the use of MTA as well as BECs for the relevant clinical applications. Numerous publications were found regarding the use of BECs for various endodontic applications. The majority of these investigations compared BECs with MTA. Despite promising results for some materials, the number of publications using BECs for various clinical applications was limited. Furthermore, most studies had several methodological shortcomings and low levels of evidence.

Comparison of Tooth Discoloration Induced by Calcium-Enriched Mixture and Mineral Trioxide Aggregate

Introduction:

The aim of this in vitro study was to evaluate the tooth discoloration induced by calcium-enriched mixture (CEM) cement and mineral trioxide aggregate (MTA).

Methods and Materials:

Forty five endodontically treated human maxillary central incisors were selected and divided into three groups (n=15) after removing the coronal 3 mm of the obturating materials. In the MTA group, white MTA plug was placed in pulp chamber and coronal zone of the root canal. In CEM cement group, CEM plug was placed in the tooth in the same manner. In both groups, a wet cotton pellet was placed in the access cavity and the teeth were temporarily sealed. After 24 h the teeth were restored with resin composite. In the negative control group the teeth were also restored with resin composite. The color change in the cervical third of teeth was measured with a colorimeter and was repeated 3 times for each specimen. The teeth were kept in artificial saliva for 6 months. After this period, the color change was measured again. Data were collected by Commission International de I'Eclairage's L*a*b color values, and corresponding ΔE values were calculated. The results were analyzed using the one-way ANOVA and post-hoc Tukey’s test with the significance level defined as 0.05.

Results:

There was no significant differences between CEM group and control group in mean discoloration. The mean tooth discoloration in MTA group was significantly greater than CEM and control groups (P<0.05).

Conclusion:

According to the result of the present study CEM cement did not induce tooth discoloration after six months. Therefore it can be used in vital pulp therapy of esthetically sensitive teeth.

Effect of Calcium Hydroxide on the Push-out Bond Strength of Endodontic Biomaterials in Simulated Furcation Perforations

Introduction:

The aim of this in vitro study was to evaluate the effect of calcium hydroxide (CH) on push-out bond strength of white mineral trioxide aggregate (WMTA) and calcium-enriched mixture (CEM) cement in simulated furcation perforations.

Methods and Materials:

Furcation perforations, measuring 1.3 mm in diameter and 2 mm in height, were created in 80 human mandibular first molars. The teeth were then divided into 4 groups (n=20). In groups 1 and 3 CH was placed in the perforation for one week, before placement of WMTA and CEM. In groups 2 and 4 perforations were repaired without placement of CH. In groups 1 and 2 the perforation sites were repaired with WMTA and CEM cement was used in groups 3 and 4. After 7 days, the push-out test was carried out using a universal testing machine. Data were analyzed with two-way ANOVA. The level of significance was set at 0.05.

Results:

The maximum and minimum bond strength values were recorded in the WMTA/CH (13.08±1.8 MPa) and CEM cement groups (8.03±0.98 MPa), respectively. There were significant differences in resistance to dislodgement between the WMTA/CH and other groups (P<0.05).

Conclusion:

Placement of CH before placement of WMTA in furcation perforation improves the push-out bond strength of this material.