Acid Effects on the Physical Properties of Different CAD/CAM Ceramic Materials: An in Vitro Analysis

Surface treatment, liquid, and aging effects on color and surface properties of monolithic ceramics

PURPOSE

The purpose of this study was to investigate the effects of surface treatments, liquids, and aging on color, translucency, and surface properties of monolithic ceramics.

MATERIALS AND METHODS

Lithium disilicate (LDS) and zirconia-reinforced lithium silicate (ZLS) ceramics (n = 135 each) were cut and divided into three groups [crystallization+glaze (single stage), crystallization-glaze (two stages), and crystallization-polish (two stages)]. One sample from each group was examined using scanning electron microscopy (SEM). Remaining samples were divided into four subgroups (distilled water, coffee, grape juice, and smoothie) (n = 11 each), stored for 12 d in the respective liquids, and thermally aged. One sample from each subgroup was analyzed using SEM. The color, gloss, and roughness values of the samples were analyzed after surface treatment (initial) and storage under different liquids+aging conditions. The initial data and both the aged data and data change values were analyzed using robust two- and three-way analyses of variance.

RESULTS

The glazed groups exhibited smoother surfaces. Ceramic type and ceramic-surface treatment interactions affected the initial translucency parameter (TP) (P < .001) and the initial and aged roughness values (P ≤ .001). Surface treatment type affected the color change (P < .001), and ceramic type affected the aged TP values (P < .001). Type of ceramic, surface treatment, and their interactions affected both the initial and aged gloss (P ≤ .001) and TP change values (P ≤ .015). Surface treatment type and ceramic-surface treatment interactions affected the gloss change values (P ≤ .001).

CONCLUSION

Although both ceramics and all surface treatments are clinically applicable, crystallization-glaze is recommended. When gloss and smoothness are important or when translucency is important, ZLS or LDS may be preferred, respectively.

Impact of various aging treatments on the microhardness and surface roughness of CAD-CAM monolithic restorative materials

PURPOSE

Dental ceramics deteriorate as a result of thermal aging and exposure to acidic solutions, which change their microhardness and surface roughness. This study assessed the resistance of several computer-aided design and computer-aided manufacturing (CAD-CAM) restorative dental materials in terms of surface roughness and microhardness following exposure to acidic solutions and thermal aging.

MATERIALS AND METHODS

Five different monolithic CAD-CAM restorative materials, two leucite-reinforced glass ceramics (G-Ceram and CEREC Blocs), a zirconia-infiltrated lithium silicate (Celtra Duo), a resin nanoceramic (Grandio), and monolithic zirconia (inCoris TZI), were used to create 2-mm-thick rectangular specimens (n = 100). After being immersed in either acidic saliva (pH = 4.0) (ST) or gastric juice (pH = 1.2) (GT), each material was subjected to 10,000 cycles of thermal aging. The Vickers microhardness and average surface roughness of the specimens were assessed at baseline, following thermal aging and exposure to either gastric juice or acidic saliva. The surface properties were examined using an atomic force microscope. The Mann‒Whitney U test with Bonferroni correction and the Wilcoxon signed-rank test was used for statistical analysis (a = 0.05).

RESULTS

The surface roughness of two leucite-reinforced glass ceramics (G-ceram and CEREC) significantly decreased with ST (p = 0.027 and p = 0.044). Only the CEREC was affected when the aging protocols were compared, and the ST group had a significant reduction in roughness (p = 0.009). The microhardness values significantly decreased after both aging protocols in all groups except for the ST subgroup of G-Ceram. Only inCoris was affected when the aging protocols were compared, and the GT group exhibited a significant reduction in microhardness (p = 0.002).

CONCLUSION

The surface roughness of the tested materials was not affected by the GT. Only leucite ceramics exhibited a decrease in surface roughness in the ST stage. Both aging processes produced a significant decrease in the microhardness of the tested ceramics. Leucite-reinforced glass-ceramic materials may be advantageous for patients with gastroesophageal reflux disease and those with a diet high in acidic foods due to their lower values for changes in microhardness and surface roughness compared to those of other CAD-CAM materials.

Clinical outcomes of single full-coverage lithium disilicate restorations: A systematic review

Introduction

Lithium disilicate glass-ceramic (LDC) restorations exhibit microorganism infiltration, recurrent caries, pulpal lesions, periodontal inflammation, and cement exposure to the oral environment over time. All these factors lead to restoration failure. This systematic review aimed to investigate the clinical outcomes of LDC full-coverage crowns (FCC) in permanent teeth compared with those of other full-coverage restoration materials.

Materials & Methods

Search strategies were developed for four databases: Web of Science, OVID, PubMed, and Scopus. Data extraction and quality appraisals were performed by two independent reviewers. Data on the presence of caries, post-operative sensitivity, and periodontal changes were extracted from the included clinical studies. In addition to the outcome measures, data on the sample size, study groups, method of restoration fabrication, type of impression, and type of abutment were recorded.

Results

We retrieved 3989 records for the title and abstract screening. Of these, 19 clinical studies met the inclusion criteria. The overall quality of the included studies indicates a low risk of bias. Most studies reported no pulpal involvement, recurrent caries, or post-operative sensitivity and presented a favorable periodontal response after the cementation of LDC-FCC during different follow-up periods.

Conclusion

Based on the endodontic and periodontic clinical responses of natural tooth abutments and their supporting periodontium, LDC-FCC can be considered a clinically successful restorative option.

Flexural Strength Properties of Five Different Monolithic Computer-Aided Design/Computer-Aided Manufacturing Ceramic Materials: An In Vitro Study

Objective

The purpose of this in vitro study is to compare the flexural strength and Weibull modulus of 5 different monolithic computer-aided design/computer-aided manufacturing (CAD/CAM) ceramics.

Methods

A total of 50 specimens were fabricated, 10 from each of the following materials: lithium disilicate-based ceramic (IPS e.max CAD), zirconia -reinforced lithium-silicate ceramic (Vita Suprinity), leucite-based glass ceramic (IPS Empress CAD), and two zirconia-based ceramics (Zenostar and CopraSmile). The specimens were 4 mm wide, 2 mm thick, and 16 mm long. Flexural strength test was executed using a universal testing machine (Model 5980, Instron Industrial Products, Norwood, MA, USA). The two-parameter Weibull distribution function was used to analyze the variability of flexural strength values. Statistical analysis was performed on SPSS Version 23 (IBM Corp., Armonk, NY, USA) using one-way analysis of variance (ANOVA) and post-hoc Tukey’s test.

Results

Suprinity had the highest Weibull modulus value, while Empress CAD displayed the lowest value. One-way ANOVA showed significant difference in the flexural strength between the different materials tested (p<0.05). Post-hoc analysis revealed significant differences among all the test groups in terms of flexural strength. Zenostar presented the highest mean flexural strength value (1033.90 MPa), while Empress CAD had the lowest value.

Conclusion

High-translucency zirconia had superior flexural properties than translucent zirconia, lithium disilicate ceramics, zirconia-reinforced lithium silicate ceramics, and leucite-based glass ceramics.

Impact of thermocycling on surface roughness, microhardness and optical properties of three different lithium disilicate ceramics

Objectives

This investigation was carried out to examine the influence of thermocycling aging on the surface roughness (R_a, µm), color parameters (L*, a*, b*), lightness change (ΔL*), chroma change (ΔC*_ab), color change (ΔE), and microhardness (VH) of three lithium disilicate ceramics.

Materials and methods

Forty-five specimens were prepared from three lithium disilicate materials (n = 15)—e.max CAD (EC), e.max Press (EP), and GC Initial LiSi Press (LP) ceramics—with dimensions of 6.0 × 1.2 × 16.0 ± 0.2 mm following the manufacturers’ instructions. All specimens were exposed to 5000 thermal cycles with bath temperatures ranging between 5 °C and 55 °C. Data of surface roughness, color parameters, and microhardness were obtained using an optical profiler, a spectrophotometer, and a Vickers hardness tester, respectively. One-way ANOVA, a post-hoc Tukey’s test, and a paired sample t-test were implemented for statistical analysis (p ≤ 0.05).

Results

For surface roughness, insignificant differences were reported between the materials either before or after thermocycling (p > 0.05) while each material displayed a significant increase after being subjected to thermocycling (p < 0.05). For color parameters, LP showed significantly lower L* and b* after thermocycling while EC presented a significant reduction in a* in comparison with other materials (p < 0.05). EP showed a significant decrease in ΔL*, ΔC*_ab and ΔE compared with other materials (p < 0.05). Regarding microhardness, LP showed significantly increase value in comparison with other materials (p < 0.05).

Conclusions

Thermocycling had a major impact on the surface roughness, microhardness and optical characteristics of the tested materials. E.max Press displayed less changes in (ΔL*), (ΔC*_ab) and (ΔE), while GC LiSi Press had better behavior in terms of microhardness.

Effect of erosive media on microhardness and fracture toughness of CAD-CAM dental materials

Background

Erosive acids might create surface flaws and deteriorate the mechanical properties of CAD-CAM materials. This invitro study aimed to investigate the effect of simulated gastric HCl and extrinsic erosive acids on surface microhardness and fracture toughness of CAD-CAM materials.

Methods

400 bar-shaped specimens (17×4×2 mm³) were prepared from 4 different CAD-CAM dental materials (n = 100/group); monolithic zirconia (Ceramill Zolid HT+, Amanngirbach, Austria), lithium disilicate ceramic (IPS e.max CAD, Ivoclar Vivadent, Liechtenstein), nanohybrid resin composite (Grandio Blocs, VOCO) and polymer-infiltrated glass network (Vita Enamic, VITA Zahnfabrik). Specimens from each material type were further subdivided into 5 groups (n = 20) according to the erosive media applied (simulated gastric HCl, white wine, Coca-Cola®, orange juice, and artificial saliva that served as a control). Specimens were immersed for 24 h in an incubator at 37 ℃, then ultrasonically cleaned in distilled water and air-dried. Half of the specimens were tested for Vickers microhardness (VHN) at parameters of 500 gf for 10 s, while the rest of the specimens underwent 3-point flexure till fracture. Fractured surfaces were examined under a scanning electron microscope (SEM) for fracture toughness (K_IC) calculation using the quantitative fractographic analysis method. Data collected were statistically analyzed using two-way analysis of variance (α = 0.05) after verification of data normality and homogeneity of variances.

Results

Erosive media created surface flaws that lowered the surface microhardness of the material and initiated the fracture pattern under different loads according to material type. The material type was a more predominant factor than erosive media that affected either the microhardness or the fracture toughness of CAD-CAM dental materials. The highest VHN and K_IC values were found among Ceramill Zolid HT+ groups followed by IPS e.max CAD and Grandio Blocs regardless of the erosive media employed. Erosive media significantly reduced the VHN and K_IC in Vita Enamic specimens compared to the rest of the material types.

Conclusion

All CAD-CAM materials used, except Vita Enamic, showed high resistance against the erosive acids indicating higher longevity of the material in patients frequently exposed to either extrinsic or intrinsic acid.

The Effects of a coffee beverage and whitening systems on surface roughness and gloss of CAD/CAM lithium disilicate glass ceramics

OBJECTIVES

To investigate the effects of a coffee beverage and two whitening systems on the surface roughness and gloss of glazed Lithium Disilicate Glass-Ceramics (LDGC) for computer-aided design/computer-aided manufacturing (CAD/CAM) systems.

METHODS

Sixty-eight LDGC disks (12 × 10 × 2 mm) were prepared from blocks of CAD/CAM systems (IPS e.max CAD ceramic). Baseline measurements for surface roughness (Ra) and gloss (GU) were taken using a 3-D optical profilometer and a glossmeter, respectively; then specimens were randomized into four groups (n = 17). All specimens were immersed in a coffee solution (24 h × 12 days) then subjected to two whitening systems. G1-negative control (kept moist × 7 days); G2-positive control (brushed with distilled water, 200 g/load, 2 min twice daily × 7 days); G3-whitening toothpaste (Colgate optic white; relative dentin abrasivity (RDA) = 100, 200 g/load, 2 min twice daily × 7 days); and G4-simulated at-home bleaching protocol (Opalescence,15% carbamide peroxide (CP), 6 h/day × 7 days). The study outcomes were measured at baseline and after the treatments. Data were analyzed using paired T-test and one-way ANOVA (α = 0.05).

RESULTS

The mean surface roughness significantly increased (p ⩽ 0.002) for all groups after the designated treatment protocols. Among groups, the mean surface roughness of G2 and G3 were significantly higher (p ⩽ 0.001) (Ra: 0.51 and 0.57 μm, respectively) compared to the control group (Ra: 0.23 μm), and were not significantly different from G4 (Ra: 0.46 μm). Surface gloss decreased with no significant change within or among groups after treatment.

CONCLUSION

All glazed LDGC had a significant increase in surface roughness after being subjected to simulated 1 year of coffee drinking and whitening systems (15% CP and whitening toothpaste), and the greatest change was associated with brushing (simulating 8 months). However, coffee beverages and whitening systems had no significant effect on the surface gloss.

Comparative Study of the Effectiveness of Laboratory-Formulated Polishing Pastes for Two CAD/CAM Ceramic Restorative Materials

PURPOSE

To evaluate the effect of different polishing pastes with different particle sizes on the surface finish of two different CAD/CAM ceramics.

MATERIALS AND METHODS

A total of 128 specimens were prepared of two CAD/CAM ceramics: lithium disilicate (12.4 × 14.5 × 2 mm) and monolithic zirconia (17.5 × 12.5 × 2.5 mm). They were divided randomly into 8 groups according to surface treatment (n = 8). Group 1 (control) was left as received after crystallization or sintering with no further surface treatment; Group 2 (glazed); Group 3 (positive control), where specimens were polished using standardized surface treatment (medium grit silicon carbide discs, rubber cup and pumice slurry, then rubber cup and toothpaste). For groups 4 to 8, in addition to silicon carbide and pumice slurry polishing, specimens were further polished using a diamond paste (DP), and polishing pastes of microzirconia (MZ), nanosilica (NS), nanodiamond (ND), and nanozirconia (NZ), respectively. Surface roughness (R_a ) was measured using noncontact profilometer. The mean values were compared using ANOVA and Post Hoc Tukey's test (α = 0.05). Specimens' surfaces were studied using a scanning electron microscope (SEM).

RESULTS

Positive control group and MZ exhibited significant R_a of lithium disilicate compared to control (p ˂ 0.001), glazed (p = 0.001), DPs (p = 0.002), NS (p ˂ 0.001), ND (p ˂ 0.001), and NZ (p = 0.002). In the case of zirconia, positive control showed a significantly higher R_a compared to all other groups (p ˂ 0.001). No statistical difference was found between all other polishing techniques (positive control, glazed, DPs, NS, ND, MZ, and NZ) (p > 0.05).

CONCLUSION

Polishing with ND, NZ, and NS lab-formulated pastes produced surfaces with comparable smoothness to control and glazed specimens for lithium disilicate and zirconia ceramic materials.

Mechanical Characterization of Two Dental Restorative Materials after Acidic Challenge

The aim of this study was to determine the effect of acidic beverages on the mechanical characteristics of a nanofilled composite resin and of a glass ionomer. Thirty specimens of each restorative material were produced and were evaluated at three different time points: before immersion (T0), after a 7 day immersion (T1) and after a 14 day immersion (T2) in water, beer and a soft drink. The studied parameters were microhardness and surface roughness. At T2, composite resin and glass ionomer specimens immersed in water, beer and the soft drink showed a statistically significant decrease in microhardness compared to T0 results. The surface roughness of composite resin specimens decreased between T0 and T1/T2 after immersion in beer and soft drink. A statistically significant increase was found between the roughness of glass ionomer specimens immersed in each one of the beverages at T0 and T1/T2. It is essential that clinicians are aware not only of available restorative materials, its characteristics and best handling techniques but also of the importance of performing an adequate assessment of patients’ dietary habits, thus making it possible to offer patients quality treatments with a predictable prognosis and longevity.