Different Undercut Depths Influence on Fatigue Behavior and Retentive Force of Removable Partial Denture Clasp Materials: A Systematic Review

Retention and fatigue performance of modified polyetheretherketone clasps for removable prosthesis

PURPOSE

Polyetheretherketone (PEEK) is considered as an alternative to metal material for removable partial denture (RPD). However, the retentive force is not strong as a metal RPD. This study investigated the retention and fatigue performance of PEEK clasps with different proportions of clasp arm engaging the undercut to verify a new strategy to improve their clinical performance.

METHODS

Three groups (n = 10/group) of PEEK clasps with their terminal 1/3, 2/3 and the whole of retentive arms engaging the undercut were fabricated along with a group (n = 10) of conventional cobalt-chrome (CoCr) clasps as control group. Retentive forces were measured by universal testing machine initially and at an interval of 1500 cycles for a total of 15,000 fatigue cycles. The fatigue cycles were conducted by repeated insertion and removal of the clasp using fatigue testing machine. Each clasp was scanned by Trios3 scanner before and after fatigue test to obtain digital models. The deformation of the clasp was evaluated by root mean square (RMS) through aligning the two models in Geomagic wrap (2021). Scanning electron microscopy (SEM) and finite element analysis were carried out to observe the abrasion and the von Mises stress of the clasp arm. Kruskal-Wallis H test was used to compare the retentive forces and the RMSs of the studied groups followed by Bonferroni multiple comparisons.

RESULTS

The whole of PEEK clasp arm engaging the undercut provided higher mean retentive forces (7.99 ± 2.02 N) than other PEEK clasp groups (P < 0.001) and was closer to CoCr clasps (11.88 ± 2.05 N). The RMSs of PEEK clasps were lower than CoCr clasps (P < 0.05) while the differences among PEEK clasps were of no statistical significance (P > 0.05). SEM showed that evidences of surface abrasion were observed on the section that engaged the undercut for all groups of clasps. The stress concentration mainly occurred on the initial part of the retentive arm. The maximum von Mises stress of each group was below the compressive strength of PEEK.

CONCLUSIONS

Proportions of PEEK clasp arm engaging the undercut positively influenced the retentive force and the fatigue resistance of PEEK clasps was superior than CoCr clasps. It is a feasible method to improve the retention of PEEK clasps by increasing the proportion of clasp arm engaging the undercut. Clinical trials are needed to further verify this innovation.

Clinical Applications of Polyetheretherketone in Removable Dental Prostheses: Accuracy, Characteristics, and Performance

The high-performance thermoplastic polyetheretherketone (PEEK) has excellent mechanical properties, biocompatibility, chemical stability, and radiolucency. The present article comprehensively reviews various applications of PEEK in removable dental prostheses, including in removable partial dentures (RPDs) (frameworks and clasps), double-crown RPDs, and obturators. The clinical performance of PEEK in removable dental prostheses is shown to be satisfactory and promising based on the short-term clinical evidence and technical complications are scarce. Moreover, the accuracy of RPDs is a vital factor for their long-term success rate. PEEK in removable dental prostheses is fabricated using the conventional lost-wax technique and CAD/CAM milling, which produces a good fit. Furthermore, fused deposition modeling is considered to be one of the most practical additive techniques. PEEK in removable prostheses produced by this technique exhibits good results in terms of the framework fit. However, in light of the paucity of evidence regarding other additive techniques, these manufacturers cannot yet be endorsed. Surface roughness, bacterial retention, color stability, and wear resistance should also be considered when attempting to increase the survival rates of PEEK removable prostheses. In addition, pastes represent an effective method for PEEK polishing to obtain a reduced surface roughness, which facilitates lower bacterial retention. As compared to other composite materials, PEEK is less likely to become discolored or deteriorate due to wear abrasion.

Fatigue behavior of removable partial denture cast and laser-sintered cobalt-chromium (CoCr) and polyetheretherketone (PEEK) clasp materials

OBJECTIVE

To investigate the fatigue behavior of cast and laser-sintered cobalt-chromium (CoCr) and polyetheretherketone (PEEK) material for a removable partial denture (RPD) clasps.

METHODS

Dumbbell-shaped specimens were digitally designed with the center part of the dumbbell being a half-round shape at the cross-sectional dimension of 1.25 mm to simulate a typical clasp design and dimensions. A fatigue machine with an offset axis rotation system simulated a typical undercut depth of 0.25, 0.50, and 0.75 mm. Each group was subjected to 30,000 fatigue cycles (simulating 21 years) or till specimen failure. Before testing, the stress value at each undercut depth for each specimen was established in a universal testing machine and SN curves were plotted for each group. Data were statistically analyzed using Kruskal-Wallis and post hoc tests. The fractured surfaces were analyzed using SEM.

RESULTS

The average fatigue cycles with 0.25, 0.50, and 0.75 mm undercuts were 27,155 ± 6277, 9298 ± 4033, 5642 ± 8785 for cast CoCr and 26,765 ± 6150, 11,318 ± 7931, 2861 ± 4803, for laser-sintered CoCr, respectively. Apart from three specimens, the PEEK groups did not fail during the simulation period. Clasps with 0.25 mm deflection showed significantly higher fatigue resistance than other groups (p < .001). There was no significant difference in fatigue behavior between the cast and laser-sintered CoCr. Microporosities at the fractured site along with irregular crack propagation were observed for cast and laser-sintered CoCr specimens. Fatigue-induced broken polymer crosslinking chains were observed in PEEK specimens.

CONCLUSION

PEEK material exhibited the highest fatigue resistance and significantly lower deflection resistance. Cast and laser-sintered CoCr showed similar fatigue resistance and behavior.