Staining and bleaching susceptibility of zirconia-reinforced lithium silicate glass-ceramics with different thicknesses, translucencies, and fabrication methods

STATEMENT OF PROBLEM

The influence of different thicknesses, translucencies, and fabrication methods on the spectrophotometric and topographical properties of zirconia-reinforced lithium silicate glass-ceramics (ZLSs) for dental restorations remains unclear.

PURPOSE

The purpose of this in vitro study was to investigate the effect of thicknesses, translucencies, and fabrication methods on the color stability, translucency parameter, opalescence parameter, whiteness stability, transmitted irradiance, light transmittance, opacity, gloss, and roughness of ZLSs exposed to coffee staining and bleaching treatments.

MATERIAL AND METHODS

Two pressable ZLSs (VITA AMBRIA, VA and Celtra Press, CP) and 2 machinable ZLSs (VITA Suprinity, VS and Celtra Duo, CD) were examined at high translucency (HT) and low translucency (LT) levels in 2 thicknesses (n=160). The specimens were evaluated at baseline, after coffee staining, and after bleaching. The color stability (ΔE2000), translucency parameter (TP), opalescence parameter (OP), whiteness index (WID), and whiteness stability (ΔWID) were measured with a spectrophotometer. Transmitted irradiance (It), light transmission (T), and opacity (O) were obtained from a light-polymerizing unit and a polymerization light collection device. Roughness stability (ΔSa%) was determined with an optical profilometer, and gloss stability (ΔGU%) was recorded with a gloss meter. Data of ΔCIE2000, ΔWID, ΔSa%, and ΔGU% were analyzed by 4-way ANOVA, and data of the TP, OP, WID, It, T, and O were analyzed by repeated 4-way ANOVA (α=.05).

RESULTS

VS-HT exceeded the ΔCIE2000 acceptability threshold after coffee staining and bleaching protocols. Pressable ZLSs exhibited greater color stability than machinable ZLSs. The 1-mm-thick VA, CP, and CD materials exceeded the ΔWID perceptibility threshold after bleaching. The highest TP and OP was displayed by the 1-mm-thick CP after bleaching. ΔGU increased after water storage and decreased after coffee staining and bleaching. ΔSa% significantly increased after bleaching (P<.05).

CONCLUSIONS

The color stability and other spectrophotometric properties of ZLSs depended on material thickness. The effects of ZLS fabrication methods and translucency levels on their measured properties were inconsistent. Subjecting 1-mm-thick ZLS materials to acidic media adversely impacted their stainability and surface texture.

Evaluation of the Mechanical and Adhesion Characteristics of Indirect Restorations Manufactured with Three-Dimensional Printing

The aim of this study was to investigate the marginal fit and bond strength characteristics of onlay restorations manufactured by three-dimensional printing (Varseo XS, Bego GmbH, Bremen, Germany) and CAD/CAM (CAMcube, Montreal, QC, Canada) systems. Class II onlay cavities on sixty mandibular molars were prepared in cavities and restored in three separate groups using different fabrication methods. Digital and conventional impressions were taken to design the restorations in the CAD system (DWOS, Straumann GmbH, Freiburg, Germany). To evaluate the marginal fit and void volumes, all specimens were scanned with microcomputed tomography. A microshear test was performed to compare the bond strength of the restorations to the tooth surface. The marginal fit values measured for the 3D-printed and CAD/CAM onlay restorations were found to be at clinically acceptable levels (<120 µm), and no significant difference could be observed between the three different fabrication methods (p > 0.05). According to the microshear test results, the CAD/CAM group had the highest bond strength values before (34.82 MPa) and after (26.87 MPa) thermal cycling (p < 0.05), while the 3D-printed and conventionally produced onlays had similar results (p < 0.05). 3D printing technology is a promising option for indirect restorations; however, the post-production phase is as crucial as the printing and cementation phases.

Vertical Edgeless Preparation: Periodontal Dominance in Prosthetic Crown Preparation

This article aims to describe Vertical Edgeless Preparation (VEP), a full-crown vertical preparation technique initially introduced by the Porta Mascarella Group in the 1980s. The method is defined as “periodontally driven” because its main indication is teeth with a loss of periodontal attachment, and it aims to obtain healthier periodontal tissues. This work describes the step-by-step procedure for performing this prosthetic technique and its indications, contraindications, impression phases, temporary crown management, and biological concepts.