Evaluation of enamel surface modification using PS-OCT after laser treatment to increase resistance to demineralization

Combined effects of a topical fluoride treatment and 445 nm laser irradiation of enamel against a demineralization challenge: A light and electron microscopic ex vivo study

This study investigated the caries-preventive effect of 445 nm laser radiation in combination with fluoride on the prevention of white spot lesions. Previously, several studies have indicated the ability of 488 nm argon ion laser irradiation to reduce early enamel demineralization. A diode laser (445 nm) could be an alternative technology for possible caries-preventive potential. Each sample of a group of seventeen caries-free bovine teeth was treated in four different ways on four different zones of the labial surface: control/no treatment (C), laser irradiation only (L) (0.3 W, 60 s and applied dose of 90 J/cm²), amine fluoride application only (10,000 ppm and pH 3.9) (F), and amine fluoride application followed by laser irradiation (FL). After treatment, the teeth were subjected to a demineralization solution (pH 4.3 for 48 h at 37 °C) to induce subsurface lesions. After sectioning, the teeth were examined by light microscopy. Three teeth were analyzed by scanning electron microscopy (SEM). The depths of the subsurface lesions in the C, L, F, and FL groups were 103.01 (± 13.04), 96.99 (± 14.51), 42.59 (± 17.13), and 24.35 (± 11.38) μm, respectively. The pairwise group comparison showed the following results: p < 0.001 for FL versus C, FL versus L, F versus C, and F versus L, p = 0.019 for FL versus F and p = 0.930 for L versus C. The SEM micrographs support the light-microscopic examination. The results of the current study have shown that using relatively low irradiation settings of 445 nm laser on fluoridated enamel may be effective for prevention of white spot lesions.

Laser-assisted prevention of enamel caries: a 10-year review of the literature

Since the invention of lasers in dentistry, investigations in caries prevention by the use of laser radiation have been proposed. There are several mechanisms stated for this purpose such as photothermal and/or photochemical interaction processes with the enamel. Alone or in conjugation with topical fluoride application, this treatment modality may improve enamel acid resistance in high-caries-risk populations. Data collection was done by searching the keywords caries, prevention, and laser in PubMed, Embase, Web of Science, Cochrane Library, and Google Scholar. Lasing protocols of the collected literature and their effectiveness as well as examination methods used to verify treatment outcomes have been evaluated. One hundred eighteen publications were found for the last 10 years. The wavelengths investigated for caries prevention are mainly located in the near and the mid-infrared spectral range. In the evaluated period of time, investigations using CO₂; Er:YAG; Er,Cr:YSGG; Er:YLF; fundamental, second, and third harmonic generations of Nd:YAG; diodes; and argon ion lasers were found in the databases. Accounting for 39% of the literature, CO₂ laser was the most examined system for this purpose. Reviewing the literature in this narrative review showed that all laser systems presented a positive effect in varying degrees. Laser irradiation could be an alternative or synergistic to topical fluoridation for enamel caries prevention with longer lasting effect. Further research should be focused on selecting proper laser settings to avoid damage to enamel and developing effective evidence-based clinical protocols.

Influence of CO2 Laser Irradiation and CPPACP Paste Application on Demineralized Enamel Microhardness

Introduction: It has been suggested that the application of casein phosphopeptide-amorphous calcium phosphate paste (CPP-ACP) and CO2 laser irradiation on enamel could increase the resistance of enamel to caries and acid attacks. The aim of the current study was to compare the influence of CPP-ACP paste application and irradiation of CO2 laser on microhardness of demineralized enamel. Methods: Thirty sound maxillary extracted premolars were selected. The crowns were cut at the cervical line and were split into facial and palatal halves. Specimens were mounted in selfcure acrylic blocks in such way that the enamel surface was exposed to 4×4 mm. After a pH cycling of the specimens, they were randomly divided into 4 groups (n=15), as follows: CG: Control group, LAS: CO2 laser, CP: CPP-ACP and LASCP: laser combined CPP-ACP treatment. The Vickers microhardness of the specimens was measured (500 g load, 5 seconds, 3 points). Data were analyzed using one-way ANOVA and post hoc Tukey tests (α =0.05). Results: The lowest mean Vickers microhardness value was observed in CG group (192.57±50.87 kg/mm2 ) and the highest in LASCP group (361.86±22.22 kg/mm² ). There were significant differences between groups (P<0.001). The pairwise comparison of the groups revealed that there were significant differences between these groups: CG versus LAS, CP, LASCP (P<0.05) and LASCP versus LAS and CP (P<0.05). No significant difference between LAS group versus CP group (P>0.05) was observed. Conclusion: The results of the current study revealed that CO2 laser and CCP-ACP were effective for improvement of enamel hardness value after demineralization. Incorporation of CO2 laser irradiation and CCP-ACP paste application provides additional remineralizing potential for demineralized enamel.

Synergistic effect of fluoride and laser irradiation for the inhibition of the demineralization of dental enamel

Both laser irradiation and fluoride treatment alone are known to provide increased resistance to acid dissolution. CO₂ lasers tuned to a wavelength of 9.3 μm can be used to efficiently convert the carbonated hydroxyapatite of enamel to a much more acid resistant purer phase hydroxyapatite (HAP). Further studies have shown that fluoride application to HAP yields fluoroapatite (FAP) which is even more resistant against acid dissolution. Previous studies show that CO₂ lasers and fluoride treatments interact synergistically to provide significantly higher protection than either method alone, but the mechanism of interaction has not been elucidated. We recently observed the formation of microcracks or a "crazed" zone in the irradiated region that is resistant to demineralization using high-resolution microscopy. The microcracks are formed due to the slight contraction of enamel due to transformation of carbonated hydroxyapatite to the more acid resistant pure phase hydroxyapatite (HAP) that has a smaller lattice. In this study, we test the hypothesis that these small cracks will provide greater adhesion for topical fluoride for greater protection against acid demineralization.