Design, Synthesis, and Characterization of a Novel Blue-Green Long Afterglow BaYAl3O7:Eu2+, Nd3+ Phosphor and Its Anti-Counterfeiting Application

Herein, a series of novel long afterglow nanophosphors BaYAl3O7:Eu2+, Nd3+ was synthesized by the combustion method. The investigation encompassed the characterization of X-ray diffraction, morphology, chemical valence, elemental composition, and photoluminescence behavior of BaYAl3O7:Eu2+ and BaYAl3O7:Eu2+, Nd3+ nanoparticles. Under 365 nm excitation, BaYAl3O7:Eu2+ and BaYAl3O7:Eu2+, Nd3+ show emission bands centered at 497 nm and 492 nm, which are attributed to the 4f65d→4f7 transition of Eu2+ ions. The optimal samples of BaYAl3O7:0.03Eu2+ and BaYAl3O7:0.03Eu2+, 0.02Nd3+ have average fluorescence lifetimes of 850 ns and 1149 ns, respectively. The co-doping of Nd3+ ions as the trap centers produced long afterglow luminescence properties, and the afterglow time could reach up to 8 min. Furthermore, the fluorescent powder can be mixed with polyacrylic acid to prepare anti-counterfeiting inks; a clover pattern and snowflake pattern have been successfully printed using screen printing technology, proving its potential application in the field of anti-counterfeiting.

Identification of Nano-Metal Oxides That Can Be Synthesized by Precipitation-Calcination Method Reacting Their Chloride Solutions with NaOH Solution and Their Application for Carbon Dioxide Capture from Air-A Thermodynamic Analysis

Several metal oxide nanoparticles (NPs) were already obtained by mixing NaOH solution with chloride solution of the corresponding metal to form metal hydroxide or oxide precipitates and wash-dry-calcine the latter. However, the complete list of metal oxide NPs is missing with which this technology works well. The aim of this study was to fill this knowledge gap and to provide a full list of possible metals for which this technology probably works well. Our methodology was chemical thermodynamics, analyzing solubilities of metal chlorides, metal oxides and metal hydroxides in water and also standard molar Gibbs energy changes accompanying the following: (i) the reaction between metal chlorides and NaOH; (ii) the dissociation reaction of metal hydroxides into metal oxide and water vapor and (iii) the reaction between metal oxides and gaseous carbon dioxide to form metal carbonates. The major result of this paper is that the following metal-oxide NPs can be produced by the above technology from the corresponding metal chlorides: Al₂O₃, BeO, CaO, CdO, CoO, CuO, FeO, Fe₂O₃, In₂O₃, La₂O₃, MgO, MnO, Nd₂O₃, NiO, Pr₂O₃, Sb₂O₃, Sm₂O₃, SnO, Y₂O₃ and ZnO. From the analysis of the literature, the following nine nano-oxides have been already obtained experimentally with this technology: CaO, CdO, Co₃O₄, CuO, Fe₂O₃, NiO, MgO, SnO₂ and ZnO (note: Co₃O₄ and SnO₂ were obtained under oxidizing conditions during calcination in air). Thus, it is predicted here that the following nano-oxides can be potentially synthesized with this technology in the future: Al₂O₃, BeO, In₂O₃, La₂O₃, MnO, Nd₂O₃, Pr₂O₃, Sb₂O₃, Sm₂O₃ and Y₂O₃. The secondary result is that among the above 20 nano-oxides, the following five nano-oxides are able to capture carbon dioxide from air at least down to 42 ppm residual CO₂-content, i.e., decreasing the current level of 420 ppm of CO₂ in the Earth's atmosphere at least tenfold: CaO, MnO, MgO, CdO, CoO. The tertiary result is that by mixing the AuCl₃ solution with NaOH solution, Au nano-particles will precipitate without forming Au-oxide NPs. The results are significant for the synthesis of metal nano-oxide particles and for capturing carbon dioxide from air.

A New Approach for the Synthesis of Powder Zinc Oxide and Zinc Borates with Desired Properties

Zinc borates are widely used in industry due to their thermal stability as a flame retardant in the production of plastics, rubber, and other polymer compositions. We have developed a simple and effective approach for the synthesis of zinc borate powders with desired properties, including desired particle size, low bulk density, high reactivity, etc. Zinc borates were prepared by the thermal treatment of a concentrated water–carbohydrate solution of a zinc salt until finely dispersed ZnO was formed, followed by its hydrothermal treatment at 90–300 °C as part of a suspension based on a hot aqueous solution of H3BO3. According to X-ray powder diffraction, IR spectroscopy, and TG–DSC data, depending on the temperature of hydrothermal treatment, a decrease in the water content in the structure of synthesized zinc borate particles is observed. TEM and SEM data indicate the formation of isometrically shaped zinc borate particles in the nanometer range during hydrothermal treatment above 250 °C. Varying the temperature of the hydrothermal treatment affects the average size and fineness of the structure of the zinc borate particles.