Dentinal tubules driven wetting of dentin: Cassie-Baxter modelling

Bonding Performance of Universal Adhesives Applied to Nano-Hydroxyapatite Desensitized Dentin Using Etch-and-Rinse or Self-Etch Mode

The study assessed the bonding performance of three universal adhesives on desensitized dentin with etch-and-rinse mode or self-etch mode after nano-hydroxyapatite (nHAp)-based desensitizers application. Simulated sensitive dentin specimens were prepared and separated into four groups: no treatment as the negative control, groups desensitized by Biorepair toothpaste, Dontodent toothpaste, or nHAp paste. Three universal adhesives of All-Bond Universal, Single Bond Universal, and Clearfil Universal Bond with etch-and-rinse or self-etch mode were bonded to the desensitized dentin specimens separately, followed by resin composite build-ups. Micro-tensile bond strength was measured using a micro-tensile tester. The wettability of desensitized dentin was evaluated by the contact angle of the adhesives. Resin infiltration was observed by confocal laser scanning microscopy. Dentin tubular occlusion and nanoleakage were observed by scanning electron microscope. The results showed that the etch-and-rinse or self-etch mode of each adhesive showed similar bond strength when bonding to nHAp-based desensitized dentin. The dentin surface was partially covered by desensitizers after desensitization. Compared with the self-etch mode, stronger demineralization and more reopened dentin tubules were observed in the etch-and-rinse mode after acid etching; longer resin tags and more nanoleakage in the resin-dentin interface were observed when using the etch-and-rinse mode. When bonding to nHAp-based desensitized dentin with universal adhesives, no significant difference in bond strength was found between self-etch mode or etch-and-rinse mode; while the latter produced more nanoleakage in the resin-dentin interfaces.

Microtensile Bond Strength of Etch-and-Rinse Adhesives in Different Hydroabrasion Conditionings

The aim of the present study was to in vitro evaluate the effect of dentin conditioning with hydroabrasion on the microtensile bond strengths of three adhesive systems, compared to the standard etch-and-rinse technique. Sixty extracted human third molars were collected, and their midcoronal occlusal dentin was used for the microtensile bond strength test. Teeth were randomly assigned to three groups according to the adhesive system used: ExciTE F DSC, ENA Bond, and Scotchbond Universal. Specimens from each group were further divided into four subgroups: control specimens were treated with standard adhesive procedures; hydroabraded (HA) specimens were subjected to preventive hydroabrasion with three different intensity levels. After bonding procedures, composite crowns were incrementally built up. After thermocycling, specimens were subsequently sectioned into 1 × 1 mm sticks, and microtensile bond strengths were measured. Data were statistically analyzed. Failure mode analysis was performed. There were no significant differences in terms of bond strength between standard adhesion protocols and adhesion with HA preconditionings. On the other hand, the type of adhesive used had a significant effect on the tensile bond strength. Subgroups treated with hydroabrasion at higher intensity showed a slightly increased frequency of cohesive fractures. In conclusion, hydroabrasion can be used for dentin cavity preparation or finishing, since it does not seem to affect the bonding effectiveness.

Caries removal with Er:YAG laser followed by dentin biomodification with carbodiimide and chitosan: Wettability and surface morphology analysis

This study aimed to investigate dentin wettability and surface morphology after selective removal of carious lesion by erbium-doped yttrium aluminum garnet (Er:YAG) laser, followed by dentin biomodification with carbodiimide (EDC) and chitosan (CHI). Seventy-eight bovine dentin specimens were submitted to caries induction. Specimens were distributed according to methods of carious removal (n = 39): bur at low-speed (40,000 rpm) or Er:YAG laser (noncontact mode, 250 mJ/pulse and 4Hz). All specimens were etched with 35% phosphoric acid, and subdivided according to dentin biomodification (n = 13): Control (no biomodification), EDC or CHI. The contact angle (n = 10) between adhesive system (3M ESPE) and dentin surface was measured by a goniometer. Eighteen specimens (n = 3) were analyzed by scanning electron microscopy. Data were analyzed by two-way ANOVA and Tukey's test (α = .05). The method used to remove carious lesion did not influence the wettability of dentinal surface (p = .748). The angles produced on the remaining dentin after biomodification were influenced (p = .007). CHI promoted higher contact angles (p = .007) and EDC did not differ from the control group (p = .586). In the bur-treated group, most tubules were open, regardless of which biomodifier was used. Laser modified the organic matrix layer. CHI promoted partially closed tubules in some areas while EDC exposed dentinal tubules. Regardless of which method was used for selective removal of carious lesion, biomodification with EDC did not affect the dentin wettability, whereas CHI changed the wettability of remaining dentin. Both biomodifiers promoted a slight change on dentin morphology.

Influence of dentin pretreatment on bond strength of universal adhesives

Objective: The purpose of the present study was to compare bond strength of different universal adhesives under three different testing conditions: when no pretreatment was applied, after 37% phosphoric acid etching and after glycine application. Materials and methods: One hundred and fifty bovine permanent mandibular incisors were used as a substitute for human teeth. Five different universal adhesives were tested: Futurabond M+, Scotchbond Universal, Clearfil Universal Bond, G-Premio BOND, Peak Universal Bond. The adhesive systems were applied following each manufacturer's instructions. The teeth were randomly assigned to three different dentin surface pretreatments: no pretreatment agent (control), 37% phosphoric acid etching, glycine pretreatment. The specimens were placed in a universal testing machine in order to measure and compare bond strength values. Results: The Kruskal-Wallis analysis of variance and the Mann-Whitney test were applied to assess significant differences among the groups. Dentin pretreatments provided different bond strength values for the adhesives tested, while similar values were registered in groups without dentin pretreatment. Conclusions: In the present report, dentin surface pretreatment did not provide significant differences in shear bond strength values of almost all groups. Acid pretreatment lowered bond strength values of Futurabond and Peak Universal Adhesives, whereas glycine pretreatment increased bond strength values of G Praemio Bond adhesive system.

Influence of air abrasion and sonic technique on microtensile bond strength of one-step self-etch adhesive on human dentin

The purpose of this in vitro study was to evaluate the microtensile bond strength of one-step self-etch adhesive to human dentin surface modified with air abrasion and sonic technique and to assess the morphological characteristics of the pretreated dentin surface. The occlusal enamel was removed to obtain a flat dentin surface for thirty-six human molar teeth. The teeth were randomly divided into three experimental groups (n = 12 per group), according to the pretreatment of the dentin: (1) control group, (2) air abrasion group, and (3) sonic preparation group. Microtensile bond strength test was performed on a universal testing machine. Two specimens from each experimental group were subjected to SEM examination. There was no statistically significant difference in bond strength between the three experimental groups (P > 0.05). Mean microtensile bond strength (MPa) values were 35.3 ± 12.8 for control group, 35.8 ± 13.5 for air abrasion group, and 37.7 ± 12.0 for sonic preparation group. The use of air abrasion and sonic preparation with one-step self-etch adhesive does not appear to enhance or impair microtensile bond strength in dentin.

Solvent composition of one-step self-etch adhesives and dentine wettability

OBJECTIVES

Our aim was to determine the wettability of dentine by four commercial self-etch adhesives and evaluate their spreading rate on the dentine surface. Any correlation with chemical composition was sought, particularly with the amount of solvent or HEMA present in the adhesive. The adhesives used were AdheSE One, Optibond All.In.One, Adper Easy Bond and XenoV.

METHODS

Chemical compositions were determined by proton nuclear magnetic resonance (NMR) spectroscopy of the adhesives dissolved in dimethylsulfoxide. Apparent contact angles for sessile drops of adhesives were measured on dentine slices as a function of time for up to 180s. The water contact angles were determined for fully polymerised adhesives.

RESULTS

All adhesives were water-based with total solvent contents ranging from 27% to 73% for HEMA-free adhesives, and averaging 45% for HEMA containing adhesives. The contents in hydrophobic groups decreased as water contents increased. No differences were found in the adhesive contact angles after 180s even though the spreading rates were different for the products tested.

CONCLUSION

Water contact angles differed significantly but were not correlated with HEMA or solvent presence. Manufacturers use different approaches to stabilise acid co-monomer ingredients in self-etch adhesives. Co-solvents, HEMA, or acrylamides without co-solvents are used to simultaneously etch and infiltrate dentine. A large proportion of water is necessary for decalcification action.