The Kinetics of the Redox Reaction of Platinum(IV) Ions with Ascorbic Acid in the Presence of Oxygen

In this work, the kinetics of the redox reaction between platinum(IV) chloride complex ions and ascorbic acid is studied. The reduction process of Pt(IV) to Pt(II) ions was carried out at different reagent concentrations and environmental conditions, i.e., pH (2.2-5.1), temperature (20-40 °C), ionic strength (I = 0.00-0.40 M) and concentrations of chloride ions (0.00-0.40 M). The kinetic traces during the reduction process were registered using stopped-flow spectrophotometry. Based on the kinetic traces, the rate constants were determined, and the kinetic equations were proposed. It was shown that in the mild acidic medium (pH = 2.5), the reduction process of Pt(IV) to Pt(II) ions is more complex in the presence of oxygen dissolved in the aqueous solutions. For these processes, the values of the enthalpy and entropy of activation were determined. Moreover, the mechanism of the reduction of Pt(IV) to Pt(II) ions was proposed. The presented results give an overview of the process of the synthesis of platinum nanoparticles in the solution containing oxygen, in which the reduction process of Pt(IV) to Pt(II) ions is the first step.

CTAB Reverse Micelles as Catalysts for the Oxidation of Ascorbic Acid by K3[Fe(CN)6]

The oxidation of ascorbic acid by K3[Fe(CN)6] was studied in reverse micellar systems composed of CTAB (Cetyltrimethylammonium bromide), and it was found  the observed first order  (k1(aq) = 5.2×10−5 s−1, k1(rev) = 61.4×10−4 s−1) rate constant in reverse micellar medium is around forty times higher compared to aqueous medium under identical conditions. The rate enhancement (k2(aq) = 0.9×10−5 mole−1.dm3.sec−1, k2(rev) = 1.75×10−3 mole−1.dm3.sec−1)  is attributed to the large concentration effect and lower dielectric constant in the reverse micelles. The rate of the reaction increases with increase in W = {[H2O]/[surfactant]} which is explained in terms of ionic strength of the water pool. The effect of surfactant concentration on rate was explained on the basis of Berezin pseudo phase model. Copyright © 2021 by Authors, Published by BCREC Group. This is an open access article under the CC BY-SA License (https://creativecommons.org/licenses/by-sa/4.0). 

Sulforaphane-assisted preparation of tellurium flower-like nanoparticles

A new method for the fabrication of flower-like tellurium nanoparticles is reported. It is based on the reduction of tellurite precursor by products generated during decomposition of sulforaphane at elevated temperature in aqueous medium. These species and other organic molecules present in the reaction mixture are being adsorbed on the surface of tellurium nuclei and govern further tellurium growth in the form of nanoflowers. The obtained particles have been characterized by a range of physicochemical techniques. It was shown that the average size of the nanoflower particles is ca. 112 nm, and they are composed of smaller domains which are ca. 30 nm in diameter. The domains are crystalline and consist of trigonal tellurium as shown by x-ray diffraction, Raman spectroscopy and high resolution transmission electron microscopy. The tellurium nanoflowers were examined from the perspective of their potential anticancer activity. The in vitro cell viability studies were conducted on breast cancer (MDA-MB-231, MCF-7) and normal cell lines (MCF-10A) employing MTT and CVS assays. It was shown, that the nanoflowers exhibit considerable cytotoxicity against cancer cells which is ca. 3-7 times higher than that observed for reference normal cells. The preliminary in vivo investigations on rats revealed that the nanoflowers accumulate predominantly in pancreas after intraperitoneal administration, without observable negative behavioral effects.

Stabilisation of copper(i) polypyridyl complexes toward aerobic oxidation by zinc(ii) in combination with acetate anions: a facile approach and its application in ascorbic acid sensing in aqueous solution

A new approach to stabilise Cu(i) complexes in aqueous solution using Zn(ii) acetate was demonstrated.

A self-supporting bimetallic Au@Pt core-shell nanoparticle electrocatalyst for the synergistic enhancement of methanol oxidation

The morphology of Pt−Au bimetal nanostructures plays an important role in enhancing the catalytic capability, catalytic stability and utilization efficiency of the platinum. We designed and successfully prepared Au@Pt nanoparticles (NPs) through an economical, surfactant-free and efficient method of seed-mediated growth. The Au@Pt NPs displayed electrochemical performances superior to those of commercial Pt/C catalysts because their agglomeration was prevented and exhibited better long-term stability with respect to methanol oxidation in acidic media by efficiently removing intermediates. Among the obtained Au@Pt NPs, Au₉₀@Pt₁₀ NPs exhibited the most significantly enhanced catalytic performance for the methanol oxidation reaction (MOR). Their mass and electrochemically active surface area (ECSA)-normalized current densities are approximately 3.9 and 4.6 times higher than those of commercial Pt/C catalysts, respectively. The oxidation current densities of the Au₉₀@Pt₁₀ NPs are approximately 1.8 times higher than those of commercial Pt/C catalysts after 4000 s of continuous measurement because the small Pt NPs grown on the surface of the Au₉₀@Pt₁₀ NPs were effectively stabilized by the Au metal support. This approach may be a facile method for the synthesis of self-supported bimetallic nanostructures, which is of great significance for the development of high performance electrocatalysts and sensors.