Layered Double Hydroxide-Bismuth Molybdate Hybrids toward Water Remediation via Selective Adsorption of Anionic Species

The steady release of anthropogenic toxins into the biosphere is compromising water security globally. Herein, CoAl layered double hydroxide, a clay-like layered material with a cationic surface charge, was organically modified and used to template the growth of Bi₂MoO₆. The resulting nanohybrid selectively removed the anionic dye methyl orange from aqueous solution and showed an enhancement of greater than 300% in the maximum adsorptivity (1.95 mmol/g) compared to modified CoAl layered double hydroxide (0.42 mmol/g). Interestingly, the observed improvement in adsorption occurs without any significant increase in the surface area of the hybrids. Furthermore, these hybrids exhibit increased broadband visible light absorption, and their photoactivity is slightly improved compared to CoAl layered double hydroxide. This study demonstrates that composites of clay-like materials with Aurivillius oxides are promising sorbent materials for water decontamination and photocatalytic antifouling membranes and shows that the synthetic strategy that was first established with an anionic layered silicate nanoclay can be generalized to other ionic layered materials.

Synthesis of Titanium Dioxide via Surfactant-Assisted Microwave Method for Photocatalytic and Dye-Sensitized Solar Cells Applications

In this study, titania nanoparticles were obtained using the microwave-assisted technique. Moreover, different surfactants (PEG (Mn = 400), Pluronic P123 and Triton X−100) were used during the synthesis in order to determine their impact on the crystallinity and morphology of the final products. Subsequently, techniques such as XRD, SEM and TEM (performed in high contrast and high-resolution mode), diffuse reflectance spectroscopy (DRS), low temperature N2 sorption (BET model), FTIR and TGA were carried out. Based on the crystallinity analysis of the obtained materials, it was established that the addition of surfactants results in greater (PEG and Triton X−100) or smaller (Pluronic P123) average crystallite size. The main purpose of this study was to use the synthesized nanomaterials in the photodegradation process (in the UV light range) of the model organic pollutants – phenol (20 mg/L) and etodolac (15 mg/L). Furthermore, it was also pointed out that the dye-sensitized solar cells can be a second application for the synthesized titania nanomaterials. The photo-oxidation and photovoltaic tests have shown that the titanium dioxide obtained using the surfactant-assisted microwave method is characterized not only by better photodegradation efficiency of phenol and etodolac, but also by higher photocurrent density compared to the reference titania samples—the pristine TiO2 and commercial P25.