The Effect of Light Exposure on Water Sorption and Solubility of Self-Adhesive Resin Cements

Limited Etching Time Increases Self-adhesive Resin Cement Adhesion to Enamel

AIM

To evaluate the influence of different enamel etching times on the bond strength of two self-adhesive resin cements (RCs) with and without thermocycling (TMC).

METHODS

One hundred twenty bovine teeth were used. Blocks of enamel (8×4×2mm) were obtained, polished, and randomly divided into two groups, according to the RC used: MaxCem Elite or RelyX U200. Groups were subdivided into four groups (n=16), according to the etching time: Control (0 seconds), 5 seconds, 10 seconds, and 20 seconds. Three RC cylinders (1-mm diameter) were built on each enamel block. The specimens were submitted to two storage conditions: 24 hours in distilled water or TMC (5000 cycles/5°C-55°C). Afterward, the specimens were submitted to the shear bond strength (SBS) test. The failure modes and adhesive interfaces were analyzed by scanning electron microscopy (SEM) and confocal laser scanning microscopy (CLSM). Data were analyzed with three-way analysis of variance (ANOVA) and Tukey test (α=0.05).

RESULTS

Etching increased the SBS for both the RCs,especially forthe groups etched for 5 and 10 seconds. TMC affected negatively the SBS of the control groups (p<0.05). No resin tags were observed in control groups, and the formation of tags was time dependent.

CONCLUSION

The 10 seconds etching time was more effective in increasing the enamel-resin bond strength. TMC negatively affected bond strength in specimens without acid etching.

Evaluation of microhardness and water sorption/solubility of dual-cure resin cement through monolithic zirconia in different shades

Aim:

The objective is to evaluate the effect of shades of monolithic zirconia on the microhardness and sorption/solubility of the underlying two dual-cured resin types of cement.

Materials and Methods:

Eighty samples of two dual-cured resin cement discs were polymerized under 60 monolithic zirconia discs in three shades and directly activated resin discs of cement were used as the control group (n = 10). After 24 h storage at 37°C in an incubator, Vickers microhardness and the sorption and solubility were measured.

Statistical Analysis Used:

Two-way ANOVA , one-way ANOVA, Independent t-test, Tukey's honestly significant difference, and Tamhane's T2 tests.

Results:

The mean microhardness of the Variolink N resin cements were significantly higher than Panavia SA ones (P < 0.001). Furthermore, Variolink N cements exhibited lower sorption/solubility than Panavia SA resin cements (both P < 0.05). The ceramic shade had a significant influence on the microhardness of both cements (P < 0.001) but had no significant effect on the sorption/solubility of resin cements (P > 0.05).

Conclusion:

Interposition of monolithic zirconia decreases the microhardness of resin cement especially Panavia SA. In Variolink N, by increasing the chroma saturation of ceramics, the microhardness decreased, however in Panavia SA, it was altered by the shades, but not in a specific pattern. For both cements, there were no statistical differences between the sorption/solubility of samples photo-cured under different shades. There was a reverse correlation between microhardness and water sorption/solubility of both cements.

The effect of curing mode of dual-cure resin cements on bonding performance of universal adhesives to enamel, dentin and various restorative materials

The effect of curing mode of dual-cure resin cements on the tensile bond strength (TBS) of universal adhesives to enamel, dentin, zirconia, lithium disilicate ceramics (LDS), feldspathic porcelain (FP), and a Pd-Au alloy was evaluated. The substrates were bonded using Tokuyama Universal Bond (TUB) or Scotchbond Universal Adhesive (SBU), followed by luting with Estecem II (ECII) or Rely-X Ultimate (RXU), respectively, which were used either in light-curing or self-curing mode. The TBS test was performed after 24 h or 5,000 thermal cycles. Light-curing significantly improved the 24-h TBS of TUB/ECII to enamel, dentin and FP, as well as the TBS of SBU/RXU to all substrates except LDS. After thermal cycling, light-curing significantly increased the TBS of both adhesives/cements to dentin, but significant differences between curing modes were seldom observed for other substrates. This suggested that light-curing is essential for the hydrophilic dentin, but self-curing might be sufficient for other substrates.

In Vivo Measurement of Root Canal Wall Temperature at Different Stages Prior to Fiber Post Cementation

Objective This study measured the in vivo temperature of prepared root canal walls during various stages of treatment prior to endodontic postcementation.

Materials and Methods One tooth each from five patients requiring endodontic treatment received conventional gutta-percha obturation. The coronal 4 mm of gutta-percha was removed by drilling and the canal wall temperature was measured. A sterile, saline rinse was applied, and another temperature value was recorded. Paper points were placed, and the wall temperature was recorded. A standardized period of 1.5 minute passed, simulating time needed to mix and place the resin cement and post (no resin was placed), after which the final wall temperature was obtained. The tooth was temporized and scheduled for prosthetic reconstruction. A one-way repeated measure analysis of variance (with Tukey's post hoc test) was performed among mean temperature values for each treatment stage (preset α 0.05).

Results Significant temperature differences were found among the treatment stages. Canal space drilling yielded the highest temperature (35.5 ± 0.8°C), while the lowest was obtained after saline rinsing (34.0 ± 0.9°C). The temperature of prepared root canal wall prior to postplacement (34.9 ± 1.2°C) and following paper point drying (34.8 ± 1.1°C) presented intermediate results, with no statistical difference between them.

Conclusions This study suggested that root canal wall temperature varied during various stages of preparation prior to endodontic post.

Influence of Curing Mode on the Surface Energy and Sorption/Solubility of Dental Self-Adhesive Resin Cements

This study investigated the influence of curing mode (dual- or self-cure) on the surface energy and sorption/solubility of four self-adhesive resin cements (SARCs) and one conventional resin cement. The degree of conversion (DC) and surface energy parameters including degree of hydrophilicity (DH) were determined using Fourier transform infrared spectroscopy and contact angle measurements, respectively (n = 5). Sorption and solubility were assessed by mass gain or loss after storage in distilled water or lactic acid for 60 days (n = 5). A linear regression model was used to correlate between the results (%DC vs. DH and %DC/DH vs. sorption/solubility). For all materials, the dual-curing consistently produced significantly higher %DC values than the self-curing (p < 0.05). Significant negative linear regressions were established between the %DC and DH in both curing modes (p < 0.05). Overall, the SARCs showed higher sorption/solubility values, in particular when immersed in lactic acid, than the conventional resin cement. Linear regression revealed that %DC and DH were negatively and positively correlated with the sorption/solubility values, respectively. Dual-curing of SARCs seems to lower the sorption and/or solubility in comparison with self-curing by increased %DC and occasionally decreased hydrophilicity.