Effects of prepolymerized particle size and polymerization kinetics on volumetric shrinkage of dental modeling resins

Effects of various beverages on characteristics of provisional restoration materials

OBJECTIVE

To investigate the effect of common beverages on four currently used provisional restoration materials: Protemp®4, Integrity®, polymethyl methacrylate (PMMA) block, and acrylic resin. Flowable resin composite is included as a control group.

MATERIALS AND METHODS

Each material was formed into disks of 10-mm diameter and 4-mm thickness (N = 40) by loading the material into acrylic molds. The exposed surface in the mold was covered using a glass slide to prevent an oxygen inhibition layer, and polymerization then proceeded. The solidified disks were placed in distilled water for 24 h. These samples (n = 8) were then immersed for 14 days in one of four different beverages: water, orange juice, cola, and coffee. Changes in color dimension, hardness, and roughness were observed and then analyzed using two-way repeated analysis of variance.

RESULTS

The provisional materials had more obvious changes in all three color dimensions than the flowable resin composite. Integrity showed the biggest changes, followed by acrylic resin and PMMA block, whereas Protemp had the smallest changes. The hardness of all the materials significantly decreased after immersion in any of the beverages for 14 days. There were no changes in surface roughness when the materials were immersed in distilled water. The surface roughness of the PMMA block significantly decreased in orange juice whereas that of Integrity and acrylic resin significantly increased in cola.

CONCLUSION

Different kinds of provisional materials had different degrees of staining due to their composition. Moisture had a significant influence on the hardness of materials, and the acidity of cola significantly roughened the surface of the provisional materials.

A Comparative Study of the Mechanical Properties of Selected Dental Composites with a Dual-Curing System with Light-Curing Composites

Dual-curing composites have a wide spectrum of use in practice (rebuilding, reconstruction, and luting). The characterization of this type of material and comparative study of selected mechanical properties with light-cured materials were carried out for this paper. In this study, we used six materials with a dual-cure system—Bulk EZ, Fill-Up!, StarFill 2B, Rebilda DC, MultiCore Flow, Activa Bioactive-Restorative—and three light-cured materials—Filtek Bulk Fill Posterior, Charisma Classic, and G-aenial Universal Flo. The materials were conditioned for 24 h in water at 37 °C before testing. Selected material properties were determined: three-point bending flexural strength, diametral tensile strength, hardness, microhardness, and shrinkage stress. The highest three-point bending flexural strength (TPB) was 137.0 MPa (G-aenial Universal Flo), while the lowest amounted to 86.5 MPa (Activa Bioactive). The diametral tensile strength (DTS) values were in a range from 39.2 MPa (Rebilda DC) to 54.1 MPa (Charisma Classic). The lowest hardness (HV) value of 26 was obtained by the Activa Bioactive material, while the highest values were recorded for Filtek Bulk Fill Posterior and Charisma Classic-53. The shrinkage stress of the tested materials ranged from 6.3 MPa (Charisma Classic) to 13.2 MPa (G-aenial Universal Flo). Dual-curing composites were found to have similar properties to light-cured composites.

Bonding and Thermal Cycling Performances of Two (Poly)Aryl-Ether-Ketone (PAEKs) Materials to an Acrylic Denture Base Resin

Poly(aryl–ether–ketone) materials (PAEKs) are gaining interest in everyday dental practices because of their natural properties. This study aims to analyze the bonding performance of PAEKs to a denture acrylic. Testing materials were pretreated by grinding, sandblasting, and priming prior to polymerization with the denture acrylic. The surface morphologies were observed using a scanning electron microscope and the surface roughness was measured using atomic force microscopy. The shear bond strength (SBS) values were determined after 0 and 2500 thermal cycles. The obtained data were analyzed using a paired samples t-test and Tukey’s honestly significant difference (HSD) test (α = 0.05). The surface characteristics of testing materials after different surface pretreatments showed obvious differences. PAEKs showed lower surface roughness values (0.02–0.03 MPa) than Co-Cr (0.16 MPa) and zirconia (0.22 MPa) after priming and sandblasting treatments (p < 0.05). The SBS values of PAEKs (7.60–8.38 MPa) met the clinical requirements suggested by ISO 10477 (5 MPa). Moreover, PAEKs showed significantly lower SBS reductions (p < 0.05) after thermal cycling fatigue testing compared to Co-Cr and zirconia. Bonding performance is essential for denture materials, and our results demonstrated that PAEKs possess good resistance to thermal cycling fatigue, which is an advantage in clinical applications. The results imply that PAEKs are potential alternative materials for the removable of prosthetic frameworks.