The Influence of Dentine on the pH of Calcium Hydroxide, Chlorhexidine Gel, and Experimental Bioactive Glass-Based Root Canal Medicament

New and Efficient Bioactive Glass Compositions for Controlling Endodontic Pathogens

Endodontic treatment aims to conserve teeth through removing infected tissue, disinfecting, and filling/sealing the root canal. One of the most important treatment steps is the removal of microorganisms to avoid reinfection and consequent tooth loss. Due to increased resistance to intracanal medications, new alternative procedures are needed. Thus, an intracanal medication is suggested using three bioactive glass (BG) compositions (BG1, BG2, and BG3) produced by the sol–gel method, with different molar contents of bactericidal oxides. The BGs were morphologically and physically characterized. Their ability to inhibit the growth of two oral pathogens responsible for the failure of endodontic treatments (E. faecalis and C. albicans) was also studied. The results suggest that BG2 and BG3 can inhibit the growth of E. faecalis after 48 h of incubation, and all BG samples have a significant effect on C. albicans survival.

Bioactivity and properties of an adhesive system functionalized with an experimental niobium-based glass

OBJECTIVE

This study evaluated the incorporation of niobophosphate bioactive glass (NbG) fillers into a commercial adhesive resin.

MATERIALS AND METHODS

The silanized (NbGs) or non-silanized (NbG) NbG was added to the commercial adhesive system One Step (OS) at 30% by weight; unfilled adhesive served as control. The bioactivity of adhesives was analyzed by SEM and FTIR/ATR after 28 days in PBS. The adhesives were evaluated as regards microtensile bond strength immediately and after six months (n = 6); degree of conversion (n = 3), microhardness (n = 5); and radiopacity (n = 3). Data from each test were submitted to ANOVA and Tukey tests (P <0.05).

RESULTS

FTIR/ATR analysis showed phosphate and carbonate precipitates on the NbG adhesive specimen surface. Statistical analysis of microtensile bond strength values showed that material x time interaction was not significant, but NbG group values were similar to those of unfilled adhesive (p <0.05). Addition of NbG did not alter the degree of conversion, but did increase microhardness and radiopacity values of the adhesive systems compared with those of the control group (OS). Incorporation of NbG into the adhesive system did not compromise the properties of the adhesive.

CONCLUSION

A smart adhesive system with bioactive properties, high radiopacity, microhardness, and similar bond strength and degree of conversion was obtained by incorporating 30% by weight of NbG.