Impact of a Core Ferrule Design on Fracture Resistance of Teeth Restored with Cast Post and Core

Can the Remaining Coronal Tooth Structure Influence the Mechanical Behavior of Nonpost Full Crowns?

OBJECTIVES

 This study investigated the impact of the remaining coronal tooth structure on the mechanical behavior of nonpost (NP) full crowns on endodontically treated maxillary central incisors.

MATERIALS AND METHODS

 Forty bovine incisors with NP and 2-mm of ferrule were divided into four groups based on the remaining structure: complete 2-mm ferrule (NP-2), absence of mesial and distal ferrule effect (NP-BL), absence of buccal and lingual ferrule effect (NP-MD), and no ferrule (NP-0). The specimens underwent a stepwise stress fatigue test until fracture occurred, and stress distribution was analyzed using in silico finite element analysis (FEA). Additionally, groups with endodontic posts (P) were simulated in the FEA.

RESULTS

 The results showed that the survival rates varied among the different groups under oblique loading. The NP-2 group exhibited the highest survival rate, with all samples enduring loads up to 200 N and some surviving up to 520 N. The NP-MD and NP-BL groups had lower survival rates, while the NP-0 group had the poorest survival rate. The predominant failure mode was a nonrepairable root fracture. FEA results indicated no significant difference between groups with and without posts. NP intraradicular restorations on nonweakened roots with a minimum height of 2mm and partial or total ferrule thickness of 1mm offer a promising treatment option.

CONCLUSION

 A complete 2-mm ferrule was found to be the most favorable configuration for NP full crowns. However, maintaining the remaining tissue is crucial, as both combinations with preserved ferrule effect exhibited superior behavior in terms of fatigue and fracture load compared to the group with no ferrule. These findings contribute to understanding the mechanical considerations for NP full crowns and provide insights into treatment planning and design choices in restorative dentistry.

In vitro fracture strength and modes of cast post and cores luted with self-adhesive resin-based cement

Aim: Cast post and core (CPC) is the main used post type; however, the biomechanical behavior of CPCs adhesively luted to the dentin is still unclear. Therefore, we aimed to evaluate the fracture resistance (FR) and fracture modes of teeth restored with CPCs luted with zinc-phosphate (ZP) or resin-based self-adhesive (SA) cements, as well as the influence of the coronal remnant. Methods: For that, 24 human premolars were divided into four groups according to the cement (ZP or SA) and coronal remnant (with or without 2mm). FR was tested in a universal machine and data analyzed by two-way ANOVA and Tukey HSD (α=.05). Fracture modes were classified according to the degree of dental destruction. Results: The results showed that there was no difference in FR (p=.352); however, teeth without ferrule presented more irreparable fractures, specially in the ZP group. Conclusion: All in all, self-adhesion of CPCs does not enhance fracture resistance, however it reduces the number of irreparable fractures, compared to ZP cement.

In vitro assessment of retention and resistance failure loads of complete coverage restorations made for anterior maxillary teeth restored with two different cast post and core designs

Background

The purpose of this in vitrostudy was to evaluate the retention and resistance form of complete coverage restorations supported by two different cast post and core designs.

Material and Methods

Forty extracted maxillary central incisors were randomly divided into four groups of 10 specimens each (namely A, B, C and D). All specimens were endodontically treated and a uniform post space of 9mm was created. All prepared teeth had a 360o chamfer ferrule of 2mm in axial height measured 0.5mm coronally from the cementoenamel junction (CEJ) and an axial wall thickness of 1.5 mm. Specimens in groups A and C received cast post and cores with the standardized core design, where the core ended at the coronal part of the ferrule, while specimens in groups B and D received cores that were encircling the ferrule. Cemented complete coverage restorations in groups A and B underwent tensile load stress, while the restorations in groups C and D underwent compressive load stress until failure.

Results

Teeth in group A exhibited a mean failure load of 326.14±83.67 N under tension, while teeth in group B exhibited a mean failure load of 332.79±80.38 N (p=0.858). Teeth in group C recorded a mean failure load of 1042.81±205.07 N, and in group D a mean failure load of 875.15±167.64 N (p=0.061) under compression was registered.

Conclusions

The standard cast post and core design with a 2 mm of ferrule height offers superior resistance, although not statistically significant (p=0.061), when compared to the core design encircling the axial wall ferrule. Both cast post and core designs offer equal retention. However, different failure modes of decementation were noted.

Key words:Endodontically treated teeth, Post-and-core technique, Endodontic-post, Decementation, Root fracture, Ferrule effect.