Improving the 3D Printability and Mechanical Performance of Biorenewable Soybean Oil-Based Photocurable Resins

The general requirement of replacing petroleum-derived plastics with renewable resources is particularly challenging for new technologies such as the additive manufacturing of photocurable resins. In this work, the influence of mono- and bifunctional reactive diluents on the printability and performance of resins based on acrylated epoxidized soybean oil (AESO) was explored. Polyethylene glycol di(meth)acrylates of different molecular weights were selected as diluents based on the viscosity and mechanical properties of their binary mixtures with AESO. Ternary mixtures containing 60% AESO, polyethylene glycol diacrylate (PEGDA) and polyethyleneglycol dimethacrylate (PEG200DMA) further improved the mechanical properties, water resistance and printability of the resin. Specifically, the terpolymer AESO/PEG575/PEG200DMA 60/20/20 (wt.%) improved the modulus (16% increase), tensile strength (63% increase) and %deformation at the break (21% increase), with respect to pure AESO. The enhancement of the printability provided by the reactive diluents was proven by Jacobs working curves and the improved accuracy of printed patterns. The proposed formulation, with a biorenewable carbon content of 67%, can be used as the matrix of innovative resins with unrestricted applicability in the electronics and biomedical fields. However, much effort must be done to increase the array of bio-based raw materials.

New Materials Based on Polyvinylpyrrolidone-Containing Copolymers with Ferromagnetic Fillers

The article investigates the peculiarities of the effect of ferromagnetic fillers (FMFs) of various natures (Ni, Co, Fe, FeCo, SmCo₅) on the formation of the structure and properties of 2-hydroxyethylmethacrylate (HEMA) with polyvinylpyrrolidone (PVP) copolymers. The composites were characterized using FTIR-spectroscopy, SEM, DMTA, magnetometry of vibrating samples, specific electrical resistivity studies, and mechanical and thermophysical studies. The formation of a grafted spatially crosslinked copolymer (pHEMA-gr-PVP) was confirmed and it was established that the FMF introduction of only 10 wt.% into the copolymer formulation increased the degree of crosslinking of the polymer network by three times. The surface hardness of composites increased by 20–25%. However, the water content decreased by 16–18% and lay within 42–43 wt.%, which is a relatively high number. The heat resistance of dry composites was characterized by Vicat softening temperature, which was 39–42 °C higher compared to the unfilled material. It was established that the obtained composites were characterized by a coercive force of 200 kA × m⁻¹ and induction of a magnetic field at the poles of 4–5 mT and 10–15 mT, respectively. The introduction of FMF particles into pHEMA-gr-PVP copolymers, which, in the dry state, are dielectrics, provides them with electrical conductivity, which was evaluated by the specific volume resistance. Depending on the FMF nature and content, as well as their orientation in the magnetic field, the resistance of filled materials could be regulated within 10²–10⁶ Ohm·m. Therefore, the modification of HEMA with PVP copolymers by ferromagnetic fillers of various natures provides the possibility of obtaining materials with unique predicted properties and expands the fields of their use, for instance as magnetic sorbents for various applications, as well as the possibilities associated with their being electrically conductive materials that can respond by changing of electrical conductivity, depending on various factors.

Physicochemical Principles of Synthesis and Modification of Unsaturated Polyester-Polyvinyl Chloride Composites and the Properties of Materials Derived from Them

The influence of the polymeric modifier of polyvinyl chloride on the structuring of unsaturated polyester resins has been investigated. It is established that the introduction of 2–5 parts by weight of polyvinyl chloride into a polyester composite accelerates the process of gelation and shortens the time of microgelation of the polyester. The influence of polyvinyl chloride on the structure coefficient, surface hardness, and strength of adhesive bonds and technological shrinkage of modified polyester composites has been revealed.