Tomographic Evaluation of the Internal Adaptation for Recent Calcium Silicate-Based Pulp Capping Materials in Primary Teeth

Shear bond strength of calcium silicate-based cements to glass ionomers

BACKGROUND

A shear bond strength between the biomaterial and restorative material is crucial for minimizing bacterial microleakage and ensuring a favorable long-term prognosis for vital pulp therapy. This study aimed to conduct a comparative evaluation of the shear bond strength between calcium silicate-based biomaterials utilized in vital pulp treatment and various glass ionomer cement materials, both with and without the application of adhesive agents.

METHODS

A total of 270 acrylic blocks, each featuring cavities measuring 4 mm in diameter and 2 mm in depth, were prepared. Calcium silicate-containing biomaterials (ProRoot MTA, Medcem Pure Portland Cement, and Medcem MTA), following manufacturers' instructions, were placed within the voids in the acrylic blocks and allowed to set for the recommended durations. The biomaterial samples were randomly categorized into three groups based on the restorative material to be applied: conventional glass ionomer cement, resin-modified glass ionomer cement, and bioactive restorative material. Using cylindrical molds with a diameter of 3.2 mm and a height of 3 mm, restorative materials were applied to the biomaterials in two different methods, contingent on whether adhesive was administered. After all samples were incubated in an oven at 37 °C for 24 h, shear bond strength values were measured utilizing a universal testing device. The obtained data were statistically evaluated using ANOVA and post-hoc Tukey tests.

RESULTS

The highest shear bond strength value was noted in the Medcem MTA + ACTIVA bioactive restorative material group with adhesive application, while the lowest shear bond strength value was observed in the ProRoot MTA White + Equia Forte HT Fil group without adhesive application (P < 0.05).

CONCLUSION

Activa Bioactive Restorative may be considered a suitable restorative material in combination with calcium silicate-based biomaterials for vital pulp treatment. The application of adhesives to calcium silicate-based biomaterials can effectively address the technical limitations.

The assessment of internal adaptation and fracture resistance of glass ionomer and resin-based restorative materials applied after different caries removal techniques in primary teeth: an in-vitro study

Background

The aim of this study was to evaluate the 3-dimensional (3D) internal adaptation (IA) and fracture resistance (FR) of compomer and glass ionomers applied after conventional caries removal to sound dentin (CCRSD) and selective caries removal to firm dentin (SCRFD) in in-vitro.

Methods

Thirty extracted primary molars were randomly assigned to three main groups (n = 10) as glass hybrid restorative (GHR) (Equia Forte® HT), conventional glass ionomer (CGIR) (Voco Ionofil Molar) and compomer (Dyract XP). Each group was randomly divided into two subgroups according to caries removal technique as CCRSD (n = 5) and SCRFD (n = 5). The restoration procedures were completed after caries removal (CCRSD or SCRFD) in all samples. Then, specimens were subjected to IA and FR tests. Data were analyzed with Student’s t, one-way ANOVA, and Kruskal Wallis-H tests. The correlation between IA and FR results was analyzed with a Pearson test. The statistical significance level was considered as 5%.

Results

While CCRSD showed superior IA results than SCRFD for all restorative materials (p < 0.05), no statistical difference was found between CCRSD and SCRFD in FR assessment (p > 0.05). In CCRSD, compomer showed superior results for IA and FR than glass ionomers (p < 0.05). In SCRFD, it was found no significant difference between the restoratives for IA (p > 0.05). However, compomer showed superior FR results than glass ionomers (p < 0.05). There was moderate negative correlation between internal voids and FR without statistically significant difference (r = −0.333, p = 0.072).

Conclusions

Despite the advantages of SCRFD, it was found to be less superior than CCRSD in IA assessment. Therefore, when SCRFD is preferred, a peripheral seal should be provided for ideal restorative treatment. On the other hand, compomer mostly showed superior results compared to others.

Clinical Efficacy of Biomimetic Bioactive Biomaterials for Dental Pulp Capping: A Systematic Review and Meta-Analysis

Recently, biomimetic bioactive biomaterials have been introduced to the market for dental pulp capping. This systematic review and meta-analysis aimed to determine any variation between the effect of using TheraCal LC and other bioactive biomaterials for pulp capping is different, as measured by dentin increment and clinical success. The risk of bias was assessed using the Risk of Bias 2 and Newcastle−Ottawa tools for randomized clinical trials and observational studies. A search for relevant articles was performed on five databases. Additionally, the quality of the included studies was assessed using the Grading of Recommendations Assessment, Development, and Evaluation (GRADE) criteria. A summary of individual studies and a meta-analysis were performed. The odds ratio of data from clinical success was combined using a random-effects meta-analysis. The meta-analysis results showed homogeneity between the studies (I2 = 0%). They revealed that the clinical success showed no differences between the patients who received TheraCal LC, light-cured calcium silicate-based biomimetic biomaterial, for dental pulp capping or the comparator biomaterials (p > 0.5). However, the certainty of the evidence was low to moderate due to the risk of bias in the included studies.

The Effect of Thermocycling on Interfacial Bonding Stability of Self-Etch Adhesives: OCT Study

Objective

The aim of this study was to monitor the behavior of interfacial gaps formed under different bonded polymeric restorations before and after thermocycling (TC), using swept-source optical coherence tomography (SS-OCT) and confirming the obtained findings with confocal laser scanning microscopy (CLSM).

Materials and Methods

Cylindrical class I cavities were prepared in twenty noncarious human premolar teeth (1.5 mm depth × 3.5 mm diameter) and divided randomly into two groups: TS and SN, according to the adhesive system (n = 10). In the TS group, one-step self-etch adhesive Clearfil Tri-S Bond Plus (Kuraray Noritake Dental, Japan) was used, followed by composite restoration using Estelite Sigma Quick (Tokuyama Dental, Japan). In the SN group, the cavities were restored with the two-step self-etch/composite silorane-based resin restoration system (3M ESPE, USA). All specimens were restored in bulk filling technique and cured in accordance with the manufacturers' instructions. Both groups were imaged under SS-OCT after 24 h and recorded as controls. Then, each group was subjected to thermal challenge using the TC machine (5–55°C) and B-scans were recorded at different TC intervals (2600, 5200, and 10000). In order to confirm the SS-OCT findings, additional specimens were prepared, scanned, and sectioned for CLSM observation.

Results

B-scans demonstrated white clusters at the tooth-resin interface that corresponded to the gap location on CLSM images. The TS group showed significantly less gap formation than the SN group before and after TC (p < 0.001).

Conclusions

An optimal composite adaptation can be achieved when the bonded restoration comprises a combination of an adhesive containing 10-MDP monomer and a considerable highly filled composite.