Application of Chitosan-Based Molecularly Imprinted Polymer in Development of Electrochemical Sensor for p-Aminophenol Determination

Molecularly Imprinted Polymers (MIPs) have specific recognition capabilities and have been widely used for electrochemical sensors with high selectivity. In this study, an electrochemical sensor was developed for the determination of p-aminophenol (p-AP) by modifying the screen-printed carbon electrode (SPCE) with chitosan-based MIP. The MIP was made from p-AP as a template, chitosan (CH) as a base polymer, and glutaraldehyde and sodium tripolyphosphate as the crosslinkers. MIP characterization was conducted based on membrane surface morphology, FT-IR spectrum, and electrochemical properties of the modified SPCE. The results showed that the MIP was able to selectively accumulate analytes on the electrode surface, in which MIP with glutaraldehyde as a crosslinker was able to increase the signal. Under optimum conditions, the anodic peak current from the sensor increased linearly in the range of 0.5-35 µM p-AP concentration, with sensitivity of (3.6 ± 0.1) µA/µM, detection limit (S/N = 3) of (2.1 ± 0.1) µM, and quantification limit of (7.5 ± 0.1) µM. In addition, the developed sensor exhibited high selectivity with an accuracy of (94.11 ± 0.01)%.

Synergistic Bonding of Poly(N-isopropylacrylamide)-Based Hybrid Microgels and Gold Nanoparticles Used for Temperature-Responsive Controllable Catalysis of p-Nitrophenol Reduction

Stimuli-responsive hybrid nanoparticles used for controllable catalysis have been attracting increasing attention. This study aims to prepare hybrid microgels with excellent temperature-sensitive colorimetric and catalytic properties through combining the surface plasmon resonance properties of gold nanoparticles (AuNPs) with the temperature-sensitive properties of poly(N-isopropylacrylamide) (PNIPAM)-based microgels. Microgels with hydroxy groups (MG-OH) were prepared by soap-free emulsion polymerization, using N-isopropylacrylamide as the main monomer, hydroxyethyl methylacrylate as the functional monomer, N,N'-methylene bisacrylamide as the crosslinker, and 2,2'-azobis(2-methylpropionamidine) dihydrochloride as an initiator to ensure the microgels are positively charged. Furthermore, chemical modification on the surface of MG-OH was carried out by 3-mercaptopropyltriethoxysilane to obtain thiolated microgels (MG-SH). Two kinds of hybrid nanoparticles, AuNPs@MG-OH and AuNPs@MG-SH, were self-assembled, through electrostatic interaction between positive MG-OH and negative citrate-stabilized AuNPs as well as through synergistic bonding of electrostatic interaction and Au-S bonding between positive MG-SH and negative AuNPs. The morphology, stability, temperature-sensitive colorimetric properties, and catalytic properties of hybrid microgels were systematically investigated. Results showed that although both AuNPs@MG-OH and AuNPs@MG-SH exhibit good temperature-sensitive colorimetric properties and controllable catalytic properties for the reduction reaction of p-nitrophenol, AuNPs@MG-SH with synergistic bonding has better stability and higher catalytic performance than AuNPs@MG-OH. This work has good competitiveness against known PNIPAM-based materials and may provide an effective method for preparing smart catalysts by self-assembly with stimuli-responsive polymers, which has a great potential application for catalyzing a variety of reactions.