Morphological and Chemical Analysis of Different Types of Calcium Silicate-Based Cements

Dentine Remineralisation Induced by "Bioactive" Materials through Mineral Deposition: An In Vitro Study

This study aimed to assess the ability of modern resin-based "bioactive" materials (RBMs) to induce dentine remineralisation via mineral deposition and compare the results to those obtained with calcium silicate cements (CSMs). The following materials were employed for restoration of dentine cavities: CSMs: ProRoot MTA (Dentsply Sirona), MTA Angelus (Angelus), Biodentine (Septodont), and TheraCal LC (Bisco); RBMs: ACTIVA BioACTIVE Base/Liner (Pulpdent), ACTIVA Presto (Pulpdent), and Predicta Bioactive Bulk (Parkell). The evaluation of the mineral deposition was performed through scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX) on the material and dentine surfaces, as well as at the dentine-material interface after immersion in simulated body fluid. Additionally, the Ca/P ratios were also calculated in all the tested groups. The specimens were analysed after setting (baseline) and at 24 h, 7, 14, and 28 days. ProRoot MTA, MTA Angelus, Biodentine, and TheraCal LC showed significant surface precipitation, which filled the gap between the material and the dentine. Conversely, the three RBMs showed only a slight ability to induce mineral precipitation, although none of them was able to remineralise the dentine-material interface. In conclusion, in terms of mineral precipitation, modern "bioactive" RBMs are not as effective as CSMs in inducing dentine remineralisation; these latter represent the only option to induce a possible reparative process at the dentin-material interface.

Investigating the Effect of Selenium Nanoparticles on Mineral Trioxide Aggregates as a Promising Novel Dental Material

Aim

To enhance mineral trioxide aggregate high plasticity (MTA HP), a commonly used dental calcium silicate cement, by incorporating selenium nanoparticles (SeNPs) known for their antioxidant and anti-inflammatory properties. The objectives included investigating the impact of SeNPs on the setting time and chemical properties of MTA HP.

Materials and Methods

We performed a comprehensive study to formulate and profile SeNPs integrated into MTA HP. Diverse concentrations of SeNPs were introduced into MTA HP, and the commencement and culmination of the setting process were gauged employing a Gillmore needle cabinet. The chemical composition was validated using Fourier transform infrared spectroscopy with attenuated total reflectance and X-ray diffraction analysis.

Results

The incorporation of SeNPs led to remarkable improvements. Notably, SeNPs positively affected the setting time of MTA HP, with faster setting times corresponding to higher SeNPs concentrations. Chemical analyses confirmed the successful integration of SeNPs with MTA HP. These enhancements make the material may be suitable for dental applications, especially due to its accelerated setting time.

Conclusions

MTA HP incorporated with SeNPs represents a significant advancement in dental materials. Its faster setting time, combined with the antioxidant and anti-inflammatory properties of selenium, provides dental professionals with an efficient and time-saving option for complex treatments. This novel nanomaterial holds promise for improving dental procedures and patient outcomes.

Effect of incorporation of nano-graphene oxide on physicochemical, mechanical, and biological properties of tricalcium silicate cement

OBJECTIVE

Evaluation of setting time, compressive strength, pH, calcium ion release, and antibacterial activity of mineral trioxide aggregate (MTA) after modification with three different concentrations of nano-graphene oxide (GO) powder compared to unmodified Biodentine as a commercial control.

METHODS

GO powder, unhydrated and hydrated cements were characterized using Environmental Scanning Electron Microscope (ESEM) with Energy Dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), Raman Spectroscopy, and Fourier Transform Infrared spectroscopy (FTIR). GO was also analyzed using Scanning Transmission Electron Microscope (STEM) to determine average lateral dimensions. Specimens were prepared and grouped according to the concentration of GO added to Rootdent MTA (control, 1, 3, and 5 wt%) and the material used (MTA and unmodified Biodentine) into five groups. Setting time was evaluated using Gillmore penetrometer (n = 5). Compressive strength was evaluated using universal testing machine (n = 7). pH and calcium ion release were assessed using pH meter and Induced Coupled Plasma-Optical Emission Spectroscopy (ICP-OES) at 1, 7, 14, and 28 days (n = 7). Antibacterial activity was evaluated against Streptococcus mutans using direct contact test (n = 7). One-way and repeated measures ANOVA followed by Tukey's post hoc test were used for data analysis with significance level set at p ≤ 0.05.

RESULTS

Addition of GO to MTA reduced both initial and final setting time. GO modified MTA groups and unmodified Biodentine showed significantly increased calcium ion release at 14 and 28 days. All cements showed alkaline pH of the storage media at all tested time intervals. 1 wt% GO recorded the highest compressive strength values in MTA modified groups. The increased concentration of GO from 1 to 5 wt% successively increased antibacterial activity of MTA, with Biodentine showing the lowest significant value.

CONCLUSION

Addition of 1 wt% GO can significantly improve the tested properties of tricalcium silicate-based cements without compromising their compressive strength.

CLINICAL SIGNIFICANCE

GO is a promising modification for tricalcium silicate cements to improve setting time, compressive strength, and antibacterial activity to provide a variety of materials for different clinical situations. This in turn can reduce the risk of reinfection and allow placement of the final restoration in a single visit.

Micro-CT analysis and leakage of bioceramic retrofillings after ultrasonic and Er:YAG laser cavity preparations: an in vitro study

The purpose of the study was to determine the influence of preparation techniques on marginal adaptation and sealing of Biodentine™ and TotalFill® RRM bioceramic retrograde fillings. Fifty-two single-root teeth extracted for periodontal reasons were used. Root canals were instrumented using Reciproc Blue #25 and obturated using a single cone technique with an AH Plus® root canal sealer. Retrograde cavities were prepared with Piezomed device (Piezo), Er:YAG laser in short-pulse(SP) and quantum square pulse(QSP) modes and filled with Biodentine™ (BD) or TotalFill® RRM (TF). There were 6 groups (n=8): (1) Piezo BD, (2) Piezo TF, (3) SP BD, (4) SP TF, (5) QSP BD, and (6) QSP TF, and positive and negative controls (n=2). Micro-CT analysis was performed on two samples from each group. Percentage volumes of internal and external voids in apical 1.5 mm were determined. Rhodamine B dye leakage was done on six samples. The samples were cut longitudinally and examined under a stereomicroscope. Digital recordings were analyzed in ImageJ software. The deepest penetration of color in mm was recorded. The data were statistically analyzed using ANOVA and Duncan's test at the level of significance α=0.05. TotalFill® RRM performed significantly better than Biodentine™ in terms of sealing (p<0.05) and marginal adaptation, as evaluated by micro-CT. Sealing was significantly better in SP compared to QSP mode preparations (p<0.05). Differences between Piezomed and laser modes were not significantly different (p>0.05). Sealing was statistically significantly better with TotalFill® RRM compared to Biodentine™ and in Er:YAG SP preparations compared to Er:YAG QSP.