The subsurface lesion in erosive tooth wear

OBJECTIVES

This study compared the surface change on natural and polished enamel exposed to a joint mechanical and chemical wear regimen.

METHODS

Human enamel samples were randomly assigned to natural (n = 30) or polished (n = 30) groups, subjected to erosion (n = 10, 0.3% citric acid, 5 min), abrasion (n = 10, 30 s), or a combination (n = 10). Wear in the form of step height was measured with a non-contact profilometer, and surface changes were inspected with SEM on selected sections. Data was normalised and underwent repeated measures MANOVA, accounting for substrate and erosive challenge as independent variables, with Bonferroni correction for significant post hoc interactions.

RESULTS

After four cycles, polished samples had mean step heights of 3.08 (0.40) μm after erosion and 4.08 (0.37) μm after erosion/abrasion. For natural samples, these measurements were 1.52 (0.22) μm and 3.62 (0.39) μm, respectively. Natural surfaces displayed less wear than polished surfaces under erosion-only conditions (p<0.0001), but the difference disappeared with added abrasion. SEM revealed a shallow subsurface layer for polished surfaces and natural ones undergoing only erosion. However, natural surfaces exposed to both erosion and abrasion showed deeper subsurface changes up to 50 µm.

CONCLUSION

Natural enamel, when exposed to erosion alone, showed less wear and minimal subsurface alterations. But with added abrasion, natural enamel surfaces saw increased wear and notable subsurface changes compared to polished ones.

CLINICAL SIGNIFICANCE

The pronounced subsurface lesions observed on eroded/abraded natural enamel surfaces highlight how combined wear challenges may accelerate tooth tissue loss.

Quantitative analysis of the degree of demineralization for bleached enamel by optical coherence tomography

BACKGROUND

Tooth bleaching imparts whitening effects along with adverse effects such as increased tooth sensitivity and enamel surface changes. Herein, we employed optical coherence tomography (OCT), a nondestructive optical detection technique, for evaluation of tooth enamel after treatment with peroxide-based bleaching agents.

METHODS

Fifteen enamel samples were bleached using 38% acidic hydrogen peroxide-based bleach, subjected to OCT scanning, and then cross-sectioned and imaged under polarized light microscopy (PLM) and transverse microradiography (TMR). OCT cross-sectional images were compared with PLM and TMR. The depth and severity of demineralization produced in the bleached enamel were measured by OCT, PLM, and TMR. Comparison between the three techniques was performed using Kruskal-Wallis H non-parametric test and Pearson correlation.

RESULTS

In comparison with PLM and TMR, OCT clearly detected the changes in the enamel surface after hydrogen peroxide bleaching. Significant correlations (p<0.05) were observed in lesion depth between OCT and PLM (r=0.820), OCT and TMR (r=0.822), and TMR and PLM (r=0.861). There was no statistically significant difference in demineralization depth values measured by OCT, PLM, and TMR (p>0.05).

CONCLUSION

OCT can allow real-time, non-invasive imaging of artificially bleached tooth models and automatically measure the early changes in the enamel lesion structure upon exposure to hydrogen peroxide-based bleaching agents.

In vitro remineralization assessment of enamel subsurface lesions using different percentages of surface reaction-type pre-reacted glass-ionomer containing gum-based material

OBJECTIVE

To identify the remineralization activity of enamel subsurface lesions using different percentages of surface pre-reacted glass-ionomer (S-PRG) filler containing gum-base material.

METHODS

Gum extracts from gum-base materials containing 0wt%, 5wt%, and 10wt% S-PRG filler were prepared as GE0, GE5, and GE10, respectively. A total of 50 bovine enamel specimens were used, and the polished enamel surface of a 3 × 3 mm2 window area was exposed. The specimens were then subjected to a demineralization solution for seven days to create a subsurface enamel lesion. Remineralization was then conducted for seven days using a protocol whereby the specimens were immersed three times a day in prepared gum extracts (0wt%, 5wt%, and 10wt%) and artificial saliva of pH 7 (Control) for 20 min at 37 °C. Thereafter, remineralization assessment was performed by using Swept Source Optical Coherence Tomography (SS-OCT) and micro-computed tomography (μCT). Surface morphology and elemental analysis were conducted by scanning electron microscopy (SEM) and energy-dispersive X-ray spectrometry (EDS).

RESULTS

The depths of the demineralized lesions in the GE5 and GE10 groups were significantly lower than those of the Control and the GE0 groups. SEM observations of the enamel surface morphology of the GE5 and GE10 groups indicated remineralization with S-PRG filler-related elements present.

CONCLUSION

The GE5 and GE10 S-PRG filler containing gum-base materials showed significantly improved surface remineralization and reduced demineralization of the enamel lesions. EDS analysis suggested that the released ions from the S-PRG filler might be responsible for surface remineralization.

CLINICAL SIGNIFICANCE

The S-PRG filler containing gum-base material may have a significant remineralization effect and improve the surface morphology of enamel subsurface lesions.

Comparative evaluation of the spectral-domain optical coherence tomography and microhardness for remineralization of enamel caries lesions

This study aimed to evaluate the Cirrus high-definition (HD) spectral-domain optical coherence tomography (SD-OCT) for the remineralization of artificial enamel caries and to compare it with the comparison surface microhardness (SMH) analysis. Artificial caries lesions were produced on forty human enamel samples. Then, three different remineralization agents containing casein phosphopeptide amorphous calcium phosphate; casein phosphopeptide amorphous calcium fluoride phosphate; calcium glycerophosphate, magnesium chloride, and xylitol; and remineralization solution (control) were applied with pH cycling for six days. The optical depth of backscattered light and microhardness of enamel were measured using SD-OCT and SMH. All remineralization agents were significantly efficient in reducing optical lesion depth on enamels (p₁=0.001, p₂=0.002, p₃=0.006, p₄=0.025), and in increasing the SMH of enamels (p_1-3=0.005, p₄=0.017). However, the optical lesion depths of the enamel showed no correlation with the SMH in the groups. In conclusion, demineralization and remineralization of artificial lesions can be assessed with both SD-OCT and SMH.

Detection and analyzing plane of non-cavitated approximal caries by cross-polarized optical coherence tomography (CP-OCT)

OBJECTIVE

The objective was to assess the detection ability and the effect of analyzing plane of CP-OCT for non-cavitated approximal caries.

METHODS

Thirty human extracted premolars were selected based on micro-computed tomography [μ-CT: μ- CT = 0: sound (n = 12), μ-CT = 1/2: caries into outer-/inner-half of enamel (n = 6 each), μ-CT = 3: caries into outer one-third of dentine (n = 6)]. Teeth were mounted in a custommade device to simulate approximal contact, and scanned from the marginal ridge above the contact area. CP-OCT images were analyzed by deepest caries extension from horizontal and coronal planes, and repeated 48-hrs later. Sensitivity, specificity,percent correct, area under the ROC curve (Az), intra-examiner repeatability and correlation with μ-CT were determined.

RESULTS

Sensitivity/specificity/Az for Horizontalplane, Coronal-plane, and Deepest from both planes were 94percent/58percent/0.76,81percent/100percent/0.90, and 94 %/58 %/0.82. Coronal-plane had significantly higher specificity than Horizontal-plane and Deepest (p = 0.004) but Horizontal-plane and Deepest were not different (p = 1.00). Horizontal-plane had significantly lower Az than Deepest (p = 0.048), but Coronal-plane was not different than Horizontal-plane (p = 0.07) or Deepest (p = 0.20). Correlation coefficients were Horizontal-plane (0.53, p < 0.001), Coronal-plane (0.84, p < 0.001), and Deepest (0.66, p < 0.001).

CONCLUSION

Within the limitations of this study, CP-OCT could be used to detect non-cavitated approximal caries. Analysis using the Coronal-plane is superior to the Horizontal-plane.

CLINICAL SIGNIFICANCE

It is challenging to detect non-cavitated approximal caries clinically due to the adjacent tooth. CP-OCT is a nondestructive, no ionized-radiation caries detection technique. CP-OCT seems suitable to detect non-cavitated approximal caries and observing the Coronal-plane appears better than Horizontal-plane.

Early detection of enamel demineralization by optical coherence tomography

Enamel is the outermost layer of the tooth that protects it from invasion. In general, an acidic environment accelerates tooth demineralization, leading to the formation of cavities. Scanning electron microscopy (SEM) is conventionally used as an in vitro tool for the observation of tooth morphology changes with acid attacks. Yet, SEM has intrinsic limitations for the potential application of in vivo detection in the early demineralization process. In this study, a high-resolution optical coherence tomography (OCT) system with the axial and transverse resolutions of 2.0 and 2.7 μm in teeth has been utilized for characterizing the effect of the acidic environment (simulated by phosphoric acid) on the enamel topology. The scattering coefficient and the surface roughness of enamel can be directly derived from the OCT results, enabling a quantitative evaluation of the topology changes with demineralization. The dynamic process induced by the acid application is also recorded and analyzed with OCT, depicting the evolution of the demineralization process on enamel. Notably, the estimated enamel scattering coefficient and surface roughness significantly increase with the application time of acid and the results illustrate that the values of both parameters after demineralization are significantly larger than those obtained before the demineralization, illustrating both parameters could be effective to differentiate the healthy and demineralized teeth and determine the severity. The obtained results unambiguously illustrate that demineralization of the tooth surface can be successfully detected by OCT and further used as an indicator of early-stage cavity formation.

An Experimental Review of Optical Coherence Tomography Systems for Noninvasive Assessment of Hard Dental Tissues

Optical coherence tomography (OCT) is a noninvasive, high-resolution, cross-sectional imaging technique. To date, OCT has been demonstrated in several areas of dentistry, primarily using wavelengths around 1,300 nm, low numerical aperture (NA) imaging lenses, and detectors insensitive to the polarization of light. The objective of this study is to compare the performance of three commercially available OCT systems operating with alternative wavelengths, imaging lenses, and detectors for OCT imaging of dental enamel. Spectral-domain (SD) OCT systems with (i) 840 nm (Lumedica, OQ LabScope 1.0), (ii) 1,300 nm (Thorlabs, Tel320) center wavelengths, and (iii) a swept-source (SS) OCT system (Thorlabs OCS1300SS) centered at 1,325 nm with optional polarization-sensitive detection were used. Low NA (0.04) and high NA (0.15) imaging lenses were used with system (iii). Healthy in vivo and in vitrohuman enamel and eroded in vitro bovine enamel specimens were imaged. The Tel320 system achieved greater imaging depth than the OQ LabScope 1.0, on average imaging 2.6 times deeper into the tooth (n = 10). The low NA lens provided a larger field of view and depth of focus, while the high NA lens provided higher lateral resolution and greater contrast. Polarization-sensitive imaging eliminated birefringent banding artifacts that can appear in conventional OCT scans. In summary, this study illustrates the performance of three commercially available OCT systems, objective lenses, and imaging modes and how these can affect imaging depth, resolution, field of view, and contrast in enamel. Users investigating OCT for dental applications should consider these factors when selecting an OCT system for clinical or basic science studies.

The effect of base material composition on demineralization assessment in CPOCT dental imaging

Cross-polarization optical coherence tomography (CP-OCT) is a promising imaging modality to detect demineralization under the margins of composite restorations. The aim of this study was to assess how base materials applied under composite resin may affect CP-OCT image assessment. Base materials are commonly used for managing deep dentinal decay but once applied residual amounts of the base materials can be inadvertently left on the inner enamel walls. This study determined that base materials have significantly different scattering properties. The order grouping in the mean backscattered reflectivity (mR) of the base material was Dycal>caries phantom>Fuji IX, Vitrebond, Fuji II (p<0.05). The calcium hydroxide base (Dycal) had a higher mR than demineralized dentin and Vitrebond before and after the resin restoration was placed (p<0.05). While calcium hydroxide maybe a confounder in CPOCT imaging, several protective base materials are compatible with this type of imaging modality.