Milovanovic S, Lukic I, Horvat G, Novak Z, Frerich S, Petermann M, García-González CA. Green Processing of Neat Poly(lactic acid) Using Carbon Dioxide under Elevated Pressure for Preparation of Advanced Materials: A Review (2012-2022). Polymers (Basel) 2023; 15:polym15040860. [PMID: 36850144 PMCID: PMC9960451 DOI: 10.3390/polym15040860] [Citation(s) in RCA: 5] [Impact Index Per Article: 5.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/11/2023] [Revised: 02/03/2023] [Accepted: 02/07/2023] [Indexed: 02/12/2023] Open
Abstract
This review provides a concise overview of up-to-date developments in the processing of neat poly(lactic acid) (PLA), improvement in its properties, and preparation of advanced materials using a green medium (CO2 under elevated pressure). Pressurized CO2 in the dense and supercritical state is a superior alternative medium to organic solvents, as it is easily available, fully recyclable, has easily tunable properties, and can be completely removed from the final material without post-processing steps. This review summarizes the state of the art on PLA drying, impregnation, foaming, and particle generation by the employment of dense and supercritical CO2 for the development of new materials. An analysis of the effect of processing methods on the final material properties was focused on neat PLA and PLA with an addition of natural bioactive components. It was demonstrated that CO2-assisted processes enable the control of PLA properties, reduce operating times, and require less energy compared to conventional ones. The described environmentally friendly processing techniques and the versatility of PLA were employed for the preparation of foams, aerogels, scaffolds, microparticles, and nanoparticles, as well as bioactive materials. These PLA-based materials can find application in tissue engineering, drug delivery, active food packaging, compostable packaging, wastewater treatment, or thermal insulation, among others.
Collapse
Affiliation(s)
- Stoja Milovanovic
- Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000 Belgrade, Serbia
- Łukasiewicz Research Network—New Chemical Syntheses Institute, Al. Tysiąclecia Państwa Polskiego 13a, 24-110 Puławy, Poland
- Correspondence: (S.M.); (I.L.)
| | - Ivana Lukic
- Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000 Belgrade, Serbia
- Correspondence: (S.M.); (I.L.)
| | - Gabrijela Horvat
- Faculty of Chemistry and Chemical Engineering, University of Maribor, Smetanova 17, SI-2000 Maribor, Slovenia
| | - Zoran Novak
- Faculty of Chemistry and Chemical Engineering, University of Maribor, Smetanova 17, SI-2000 Maribor, Slovenia
| | - Sulamith Frerich
- Faculty of Mechanical Engineering, Institute of Thermo and Fluid Dynamics, Ruhr-University Bochum, Universitätsstraße 150, 44801 Bochum, Germany
| | - Marcus Petermann
- Faculty of Mechanical Engineering, Institute of Thermo and Fluid Dynamics, Ruhr-University Bochum, Universitätsstraße 150, 44801 Bochum, Germany
| | - Carlos A. García-González
- I+D Farma Group (GI-1645), Department of Pharmacology, Pharmacy and Pharmaceutical Technology, Faculty of Pharmacy, iMATUS and Health Research Institute of Santiago de Compostela (IDIS), Universidade de Santiago de Compostela, E-15782 Santiago de Compostela, Spain
| |
Collapse
|
2
|
Boruszewski P, Borysiuk P, Jankowska A, Pazik J. Low-Density Particleboards Modified with Blowing Agents—Characteristic and Properties. MATERIALS 2022; 15:ma15134528. [PMID: 35806654 PMCID: PMC9267788 DOI: 10.3390/ma15134528] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 04/29/2022] [Revised: 06/20/2022] [Accepted: 06/23/2022] [Indexed: 11/16/2022]
Abstract
Although lightweight particleboards have been commercially available for years, they still have a number of disadvantages, including difficulty to process, brittleness, low impact strength, and other mechanical resistance. The aim of the paper was to determine the possibility of producing particleboards of reduced density (dedicated for furniture industry) as a result of using blowing agents from the group of hydrazides, dicarboxamides, or tetrazoles, which were modifiers of the adhesive resin used for bonding the particles of the core layer of three-layer particleboards. The concept presents the possibility of producing low-density particleboards in a standard technological process by modifying the adhesive resin, which has not been practiced by others until now. Analysis of the results of testing the particleboards properties with various types of modifiers (blowing agents), glue content (high 10%/12% and low 8%/10%), differing in glue dosing method, and different particle sizes allowed concluding that the most satisfactory effect was found in particleboards made of the variant modified with p-toluenesulfonyl hydrazide. This variant was characterised by the highest mechanical properties (bending strength, modulus elasticity, and internal bond strength) with high dimensional stability. The presented technology proposal can be applied in the industry.
Collapse
Affiliation(s)
- Piotr Boruszewski
- Institute of Wood Sciences and Furniture, Warsaw University of Life Sciences—SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland; (P.B.); (A.J.)
- Correspondence: ; Tel.: +48-22-5938582
| | - Piotr Borysiuk
- Institute of Wood Sciences and Furniture, Warsaw University of Life Sciences—SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland; (P.B.); (A.J.)
| | - Agnieszka Jankowska
- Institute of Wood Sciences and Furniture, Warsaw University of Life Sciences—SGGW, 159 Nowoursynowska St., 02-776 Warsaw, Poland; (P.B.); (A.J.)
| | - Jolanta Pazik
- Fabryki Mebli “FORTE” S.A., 1 Biała St., 07-300 Ostrów Mazowiecka, Poland;
| |
Collapse
|
3
|
Kumar RS, Sinha A, Sharma H, Sharma T. High performance carbon dioxide foams of nanocomposites of binary colloids for effective carbon utilization in enhanced oil recovery applications. J Mol Liq 2021. [DOI: 10.1016/j.molliq.2021.117659] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.3] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 10/20/2022]
|
4
|
Xu LQ, Huang HX. Tuning cell structure and expansion ratio of thick-walled biodegradable poly(lactic acid) foams prepared using supercritical CO2. J CELL PLAST 2019. [DOI: 10.1177/0021955x19864389] [Citation(s) in RCA: 3] [Impact Index Per Article: 0.6] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/16/2022]
Abstract
Thick-walled poly(lactic acid) samples are foamed using supercritical carbon dioxide as physical foaming agent over a wide saturation time range using a constant-temperature mode and a wide foaming pressure range using the constant-temperature mode and a varying-temperature mode. Using the constant-temperature mode, three regions with no-celled core and two regions with cells of different diameters appear on the fractured surfaces of the foamed samples prepared at 5 and 10 min saturation times, respectively, whereas a relatively uniform cellular structure is obtained at 20–180 min saturation times. Raising the foaming pressure can improve the cellular structure uniformity. Moreover, prolonging saturation time or raising foaming pressure results in rupture of more cell walls and so formation of open-celled structure to a certain extent. Using the varying-temperature mode, a bimodal cellular structure with stamen-like cells and a trimodal cellular structure with an extraordinarily high expansion ratio (76.2) are successively achieved during raising the foaming pressure (18–22 MPa). The formation mechanisms for the bimodal and trimodal cellular structures are analyzed based on the result of the foaming pressure effect on the cellular structure in the foamed poly(lactic acid) samples prepared using the constant-temperature mode.
Collapse
Affiliation(s)
- Lin-Qiong Xu
- Lab for Micro Molding and Polymer Rheology, Guangdong Provincial Key Laboratory of Technique and Equipment for Macromolecular Advanced Manufacturing, South China University of Technology, Guangzhou, China
| | - Han-Xiong Huang
- Lab for Micro Molding and Polymer Rheology, Guangdong Provincial Key Laboratory of Technique and Equipment for Macromolecular Advanced Manufacturing, South China University of Technology, Guangzhou, China
| |
Collapse
|
5
|
Plummer CJG, Yonghoon Y, Garin L, Månson JAE. Crystallization of polylactide during impregnation with liquid CO2. Polym Bull (Berl) 2014. [DOI: 10.1007/s00289-014-1262-7] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.2] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/30/2022]
|