Reactions of powdered human enamel and fluoride solutions with and without intermediate CaHPO4 x 2H2O formation

Alkali-soluble fluoride deposition on enamel after professional application of topical fluoride in vitro

Since the efficacy of topical fluoride products is related to the fluoride (F) availability and its reactivity with enamel, this study was conducted. The F concentration of the following materials was verified: I- acidulated phosphate fluoride (APF) gel (1.23% F), II- APF foam (1.23% F) and III- Varnish (2.26% F). Forty blocks of bovine enamel were divided into 4 groups and treated according to the materials described, being one of them used as control. Loosely bound fluoride (''CaF2'') was determined on enamel after extraction with 1.0M KOH and analyzed by ion-selective electrode. Total F concentration found in gel was 12,642, in foam 12,755 and in varnish 23,183 mg F/g. All products formed statistically higher amounts of ''CaF2'' on enamel compared to the control group (p < 0.05), but the difference between them was not significant (p > 0.05). Thus, ''CaF2'' formation was not proportional to the total F content in the products, suggesting that the pH and the vehicle used are more important.

Mechanistic aspects of the interactions between fluoride and dental enamel

For many years after the discovery of its caries preventive effect, fluoride was thought to be primarily active by lowering the solubility of the apatitic mineral phase of the dental hard tissues. Recent findings have shed new light on the mechanisms by which fluoride inhibits or delays dental caries. Fluoride present in the oral fluids alters the rate of the naturally occurring dissolution and reprecipitation processes at the tooth-oral fluid interface. Demineralization of enamel is inhibited by concentrations of fluoride in the sub-ppm range. Likewise, remineralization of incipient caries lesions (the earliest stage of enamel caries) is accelerated by trace amounts of fluoride. As these two processes comprise dental caries the physiological balance between hard tissue breakdown and repair is favorably shifted by fluoride. The driving force for both phenomena is thermodynamic, that is, fluorapatite or a fluoridated hydroxyapatite may form when fluoride is supplied at low concentrations. This article critically reviews the current information about tooth-fluoride interactions, both from laboratory and clinical studies.

Improvement of the caries resistance of human dental roots by a two-step conversion of the root mineral into fluoridated hydroxylapatite

Roots of extracted human molars were treated for both 10 and 30 min with a saturated solution of dicalcium phosphate dihydrate (DCPD) of pH 2.4 and subsequently with a 5.3 mmol.L-1 solution of sodium fluoride of pH 7.0. The objective of these combined treatments was to convert the highly-soluble root mineral into the less-soluble fluoridated hydroxylapatite, with DCPD as an intermediate, to improve caries resistance. The mineral content of the surface layer was not affected in a significant way. Roots treated in this way were subjected to 50 mmol.L-1 acetate buffer solutions of pH 5.5 and with pIOHA-values of 112, 116, and 122. The proportional reduction of the rate of demineralization (Vdem) of similarly treated roots subjected to buffer solutions of pIOHA 112 and 116 appeared to be equal initially. Since fluoridated hydroxylapatite is insoluble under these conditions, these findings are in agreement with expectations. The reduction of V dem amounted to about 45 and 70% for roots treated for 10 and 30 min, respectively. When roots were treated for 10 and 30 min and then exposed to buffer solutions with a pIOHA 122, reductions of V dem of about 30 and 55%, respectively, were found. Conversion of the root mineral into fluoridated hydroxylapatite can eliminate, in principle, the existing difference in caries susceptibility of the root and of the dental enamel.

The effect of contact time of acidulated phosphate fluoride on fluoride concentration in human enamel

Polished enamel blocks with known surface areas were obtained from human mandibular incisors. Acidulated phosphate fluoride was applied for 4 min and washed off after additional contact times of 0, 2, 6 and 24 h, respectively. The enamel fluoride concentrations were determined in three successive etch depths before and after extraction in 1 M KOH for 24 h. The predominant reaction product was CaF2. The concentration of the fluoride bound as fluorapatite or fluorhydroxyapatite reached an optimal level after a 6-h contact time.