Stain removal from a pigmented silicone maxillofacial elastomer

In vitro study of effects of aging and processing conditions on colour change in maxillofacial silicone elastomers

Background

The inherent colour change in maxillofacial silicone elastomers becomes perceptible 6–12 months after fabrication. Determining the factors that accelerate the degradation of the prosthesis can help the clinicians increase its life span. Therefore, the aim of the study was to investigate the effect of time passage, processing temperature, and molding-stone colour on the colour change of maxillofacial silicone elastomers after darkroom storage for 6000 h.

Methods

A total of ten study molds, each incorporating ten specimen gaps were fabricated using five different colors of dental stones. The gaps were filled with coloured Cosmesil M511 maxillofacial silicone elastomer. Five of the study molds, one of each stone color, were processed at room temperature (25 °C) for 24 h while the remainder were vulcanized at 100 °C for 1 h. Two stainless-steel molds were also fabricated to obtain a total of twenty control-group specimens of the same dimensions that were processed under the same conditions as the study molds. Colour measurements of the vulcanized silicone samples were performed using a Konica Minolta spectrophotometer. Initial measurements were obtained after the blocks were removed from the molds and the final measurements were recorded 6000 h after storage in the dark at 25 °C and 40% relative humidity. The CIEDE2000 colour-difference formula was used to measure the changes in the colour. One-way and two-way ANOVA, and an independent-sample t-test were used for statistical assessments.

Results

For every group, the colour change exceeded the perceptible thresholds. Thus, either the vulcanization temperature or the colour of the molding stone has a significant effect on the colour change over time. Those samples vulcanized in green and white molding stones at 100 °C exhibited a significantly higher ∆L*, ∆a*, and ∆b* values relative to the samples vulcanized at room temperature.

Conclusion

The molding-stone colour and vulcanization temperature both affect the degree of colour change after storage in a dark environment. The L*, a*, and b* values for the maxillofacial silicone elastomers are influenced by the direction of the increase or decrease according to the selected colour. This effect varies as the temperature increases.

Effect of vulcanization temperature and dental stone colour on colour degradation of maxillofacial silicone elastomers

Background

Colour degradation is a major problem in maxillofacial silicone elastomers. Recent studies have focused on colour stability and the mechanical properties of the silicone elastomers. A colour match is also essential for the acceptance of the prosthesis by the patient. The aim of this study is to assess the colour degradation of the silicone elastomer after being moulded in different colours of dental stones at two different vulcanization temperatures.

Methods

Five different colours of dental stones were used to fabricate a total of 120 silicone blocks using a Cosmesil M511 maxillofacial silicone elastomer. Vulcanization was completed at two different temperatures (25 and 100° Celsius). Colour measurements were obtained with a Conica Minolta spectrophotometer. The CIEDE2000 formula was used to calculate the colour differences (∆E00). Two-way ANOVA, one-way ANOVA with Bonferroni corrected post-hoc p values and independent samples t-test were used for the statistical analyses.

Results

High temperature vulcanization causes lightening of the maxillofacial silicone elastomers without regard to the dental stone colour (p = 0.001). Specimens moulded in green stone lightened least at room temperature (p = 0.999). Compared to the control group, at high temperature, all specimens moulded in coloured dental stones darkened significantly (p < 0.001 for white, blue and yellow; p = 0.006 for green; p = 0.045 for reddish-brown). In the high temperature group, the shift to a green chroma was significant in the white, yellow and green dental stones groups (p = 0.001, p = 0.002, p < 0.001, respectively). The mean b* of the high temperature control group was higher than that of the room temperature control group (p < 0.001). The only ∆E00 score lower than the perceptibility threshold for dental materials (∆E00 = 1.30) was between the room temperature control group and the room temperature green dental stone group (∆E00 = 0.96).

Conclusions

Green and blue dental stones cause less colour degradation in silicone elastomers. Reddish-brown dental stones cause the most colour degradation in silicone elastomers. At 100 °C, the colour of the silicone elastomer lightens and yellows even if the elastomer is vulcanized in a stainless steel mould. White, yellow and reddish-brown dental stones make the silicone elastomer appear more yellow even if the elastomer is vulcanized at room temperature.

Cigarette staining and cleaning of a maxillofacial silicone

In this study, a maxillofacial silicone elastomer was stained with cigarette smoke. The stain was then removed by solvent extraction using 1,1,1-trichloroethane. The cigarette smoke produced large color changes in the elastomer as measured from spectrophotometric reflectance curves. The solvent was totally effective in removing the cigarette stain without changing the color of the silicone base.