Root hard-tissue demineralization rate measured by 125I absorptiometry: comparison with lesion-depth measurements

In vitro Induction of residual caries lesions in dentin: comparative mineral loss and nano-hardness analysis

Artificially inducing dentinal lesions mimicking those remaining after selective excavation should allow to investigate the effects and limits of such selective excavation, for example regarding the mechanical properties of treated teeth or the remineralisation of sealed residual lesions. Such analyses might otherwise be limited by the variability of natural lesions or ethical and practical concerns. This study compared different demineralisation protocols for their suitability to induce lesions similar to natural residual caries. Twelve natural deep lesions were excavated until leathery dentin remained, and analysed for their mineral loss (ΔZ), lesion depth (LD), mineral loss ratio (R), the slope of the mineral gradient and their nano-hardness profile. Artificial lesions were induced using four different demineralisation protocols (acetic acid pH = 4.95; 0.1 M lactic acid gel pH = 5.0; 0.5 M ethylenediaminetetraacetic acid pH = 7.2; Streptococcus mutans biofilms) and their depths monitored over different demineralisation times. Lesions with depths most according to those of natural lesions were analysed using transversal microradiography. Lesions induced by acetic acid solution did not significantly differ with regards to LD, ΔZ, R and mineral profile. Seven dentin specimens were subsequently submitted to a moderately acidic (pH = 5.3) methylhydroxydiphosphonate-buffered acetate solution for 12 weeks. Natural and artificial residual lesions were similarly deep (mean ± SD: LD = 626 ± 212 and 563 ± 88 µm), demineralised (R = 19.5 ± 4.7 and 29.8 ± 4.1%), showed a flat and continuous mineral gradient (slope = 0.10 ± 0.05 and 0.13 ± 0.06 vol%/µm) and did not significantly differ regarding their nano-hardness profile. The described protocol induces lesions with mineral content and mechanical properties similar to natural residual lesions.

A newly designed automatic pH-cycling system to simulate daily pH fluctuations

The aim of this study was to develop and evaluate an automatic pH-cycling system, which was intended for performing time-lapse analyses of dental caries. Two single-section specimens prepared from each of the five extracted human incisors were studied under a condition of 3- or 9-cycles/day for seven weeks. Increase of mineral loss (delta delta Z) and increase of Ld (delta Ld) were examined and compared at the end of every week during the study. In the 3-cycles/day condition, delta delta Z and delta Ld significantly increased only at Week 7. In the 9-cycles/day condition, delta deltaZ increased significantly from Week 5. delta Ld increased from Week 2, and then there were no further increases for the subsequent five weeks. Based on the results of this study, progression pattern was found to be significantly different between the two conditions. We therefore concluded that the automatic pH-cycling system which we have developed qualified as a model system that simulated the human oral cavity. As such, it could be beneficially employed to clarify the roles of many factors that cause or prevent caries development in human teeth.

Effect of intermittent delivery of fluoride to solution on root hard-tissue de- and remineralization measured by 125I absorptiometry

The effect of intermittent fluoride levels on root hard-tissue de- and remineralization was studied once daily for 21 days in a pH-cycling caries model with simulated fluoride clearance curves. Four root hard-tissue blocks, from each of 12 human teeth, were cut out parallel to the cementum surface. During a daily 15-hour period, the blocks were subjected 12 times to pH changes similar to those which occur in plaque after a carbohydrate intake. The fluoride was delivered immediately before a daily nine-hour remineralization period. Four experiments were independently carried out: One block from each tooth was subjected to pH-cycling without and with fluoride delivery, simulating a rinse with 0.025, 0.2, and 1.0% sodium fluoride (NaF), respectively. The mineral change in the blocks was monitored by 125I absorptiometry and expressed as the change in transmission (delta T). The surface between the data points (delta T values) and the x axis (time points) was used as a summary measure, i.e., the area under the curve (AUC). When no fluoride was delivered, the delta T increased over 21 days, indicating loss of mineral. The AUC was, on average, 5.85 +/- 0.68 (mean +/- S.E.) %.day. In the 0.025% NaF-rinse experiment, there was a marked reduction in mineral loss, indicated by an average AUC of 1.66 +/- 0.59%.day. In both the 0.2 and 1.0% NaF-rinse experiments, a decrease in delta T, indicating gain of mineral, was observed from day 2. Negative delta T values occurred after 7 and 3 days, respectively.(ABSTRACT TRUNCATED AT 250 WORDS)