Crack propagation directions in unfilled resins

Wear and Mechanical Properties of Nano-silica-fused Whisker Composites

Resin composites must be improved if they are to overcome the high failure rates in large stress-bearing posterior restorations. This study aimed to improve wear resistance via nano-silica-fused whiskers. It was hypothesized that nano-silica-fused whiskers would significantly improve composite mechanical properties and wear resistance. Nano-silicas were fused onto whiskers and incorporated into a resin at mass fractions of 0%-74%. Fracture toughness (mean ± SD; n = 6) was 2.92 ± 0.14 MPa•m½ for whisker composite with 74% fillers, higher than 1.13 ± 0.19 MPa•m½ for a prosthetic control, and 0.95 ± 0.11 MPa•m½ for an inlay/onlay control (Tukey’s at 0.95). A whisker composite with 74% fillers had a wear depth of 77.7 ± 6.9 μm, less than 118.0 ± 23.8 μm of an inlay/onlay control, and 172.5 ± 15.4 μm of a prosthetic control (p < 0.05). Linear correlations were established between wear and hardness, modulus, strength, and toughness, with R = 0.95–0.97. Novel nano-silica-fused whisker composites possessed high toughness and wear resistance with smooth worn surfaces, and may be useful in large stress-bearing restorations.

Degradation, fatigue, and failure of resin dental composite materials

The intent of this article is to review the numerous factors that affect the mechanical properties of particle- or fiber-filler-containing indirect dental resin composite materials. The focus will be on the effects of degradation due to aging in different media, mainly water and water and ethanol, cyclic loading, and mixed-mode loading on flexure strength and fracture toughness. Several selected papers will be examined in detail with respect to mixed and cyclic loading, and 3D tomography with multi-axial compression specimens. The main cause of failure, for most dental resin composites, is the breakdown of the resin matrix and/or the interface between the filler and the resin matrix. In clinical studies, it appears that failure in the first 5 years is a restoration issue (technique or material selection); after that time period, failure most often results from secondary decay.

Effect of filler content on bending properties of dental composites: Numerical simulation with the use of the finite-element method

The purpose of this work is to investigate the influence of filler content on the bending properties of dental composites by use of the finite-element method (FEM). The proposed numerical model was constructed from isotropic shell elements representing silica filler, and isotropic beam elements representing the remaining matrix resin. The proposed model was applied to failure analysis under three-point bending conditions. The validity of applying the numerical model to the failure progression analysis of composites was checked through comparison with experimental results. The results show that, in both the analytical and experimental results, the bending properties, such as maximum bending stress and bending modulus, increase with filler content. Also, the proposed method of failure progression analysis could better simulate the failure process of composites under three-point bending conditions. In addition, close agreement between the analytical and experimental results was confirmed. The above results indicate that the proposed numerical model is effective for evaluating the bending properties of dental filler composites of any content range.