In vitro study on the response of RAW264.7 and MS-5 fibroblast cells on laser-induced periodic surface structures for stainless steel alloys

Cell attachment and growth can be controlled by stent surface topography. In some cases fibroblast cells attach while monocytes failed on the structured surface of Pt:SS and 316LSS stents.

Crack prevention of biodegradable polymer coating on metal facilitated by a nano-coupled interlayer

Crack prevention of biodegradable polymer coatings on drug-eluting stents was investigated by introducing a nano-coupled layer at the interface between the metal surface and the polymer coating layer using surface-initiated ring-opening polymerization of ε-caprolactone. Poly(d,l-lactide-co-glycolide) coating on cobalt-chromium control and ricinoleic acid-poly(caprolactone)–grafted cobalt-chromium was carried out using electrospraying. The cracking of the biodegradable polymer coating on drug-eluting stents during ballooning was addressed by introducing a nano-coupled interlayer on the cobalt-chromium surface. The ricinoleic acid-poly(caprolactone) nano-coupled interlayer and poly(d,l-lactide-co-glycolide)-coated top layer were characterized using attenuated total reflection Fourier transform infrared, contact angle, ellipsometry, X-ray photoelectron spectroscopy, and atomic force microscopy. Based on scratch tests, the nano-coupled samples had stronger interfacial adhesion compared to the control sample without the nano-coupled layer. Scanning electron microscope images indicated that the cracking on the poly(d,l-lactide-co-glycolide) coating was addressed. Introducing a nano-coupling interlayer may be an important strategy to preventing polymer coating cracking on drug-eluting stents.