Biodegradable Hydrogel Beads Combined with Calcium Phosphate Bone Cement for Bone Repair: In Vitro and In Vivo Characterization

This study evaluated the in vitro characterizations of biodegradable hydrogel beads with calcium phosphate bone cement (CPC). Commercial fast-setting CPC and hydrogel beads were compared with 25%-volume hydrogel in CPC (C/0.25) in vivo. The histological behaviors and absorption rates of CPC only, hydrogel beads, and hydrogel/CPC composite were measured and compared at 4, 8, and 12 weeks. The results indicated that the C/0.25 composite can be molded and does not disintegrate when immersed in the solution, but this delays the phase transition of the CPC into the product in the early reaction process. The osteoprogenitor D1 cell affinity of the C/0.25 composite was equally competitive with that of the CPC-only. Adding hydrogel beads to CPC did not inhibit cell proliferation as well as differentiation of osteoprogenitor cells. In vivo histological evaluations did not indicate any significant difference in the CPC-only, hydrogel-only, and C/0.25 composite after 4 weeks of implantation; however, significantly less residue was observed in the C/0.25 composite relative to the CPC-only after 8 weeks. After 12 weeks of hydrogel beads implantation, the hydrogel degraded substantially, creating vacancies that were subsequently occupied by a large amount of soft tissue. New bone was formed in large quantities in the C/0.25; therefore, the C/0.25 composite is a promising option for a wide range of dental, craniofacial, and orthopedic applications.

In Vitro Evaluation of Calcium Phosphate Bone Cement Composite Hydrogel Beads of Cross-Linked Gelatin-Alginate with Gentamicin-Impregnated Porous Scaffold

Calcium phosphate bone cement (CPC) is in the form of a paste, and its special advantage is that it can repair small and complex bone defects. In the case of open wounds, tissue debridement is necessary before tissue repair and the subsequent control of wound infection; therefore, CPC composite hydrogel beads containing antibiotics provide an excellent option to fill bone defects and deliver antibiotics locally for a long period. In this study, CPC was composited with the millimeter-sized spherical beads of cross-linked gelatin–alginate hydrogels at the different ratios of 0 (control), 12.5, 25, and 50 vol.%. The hydrogel was impregnated with gentamicin and characterized before compositing with CPC. The physicochemical properties, gentamicin release, antibacterial activity, biocompatibility, and mineralization of the CPC/hydrogel composites were characterized. The compressive strength of the CPC/hydrogel composites gradually decreased as the hydrogel content increased, and the compressive strength of composites containing gentamicin had the largest decrease. The working time and setting time of each group can be adjusted to 8 and 16 min, respectively, using a hardening solution to make the composite suitable for clinical use. The release of gentamicin before the hydrogel beads was composited with CPC varied greatly with immersion time. However, a stable controlled release effect was obtained in the CPC/gentamicin-impregnated hydrogel composite. The 50 vol.% hydrogel/CPC composite had the best antibacterial effect and no cytotoxicity but had reduced cell mineralization. Therefore, the optimal hydrogel beads content can be 25 vol.% to obtain a CPC/gentamicin-impregnated hydrogel composite with adequate strength, antibacterial activity, and bio-reactivity. This CPC/hydrogel containing gentamicin is expected to be used in clinical surgery in the future to accelerate bone regeneration and prevent prosthesis infection after surgery.

Biological and mechanical performance and degradation characteristics of calcium phosphate cements in large animals and humans

Calcium phosphate cements (CPCs) have been used to treat bone defects and support bone regeneration because of their good biocompatibility and osteointegrative behavior. Since their introduction in the 1980s, remarkable clinical success has been achieved with these biomaterials, because they offer the unique feature of being moldable and even injectable into implant sites, where they harden through a low-temperature setting reaction. However, despite decades of research efforts, two major limitations concerning their biological and mechanical performance hamper a broader clinical use. Firstly, achieving a degradation rate that is well adjusted to the dynamics of bone formation remains a challenging issue. While apatite-forming CPCs frequently remain for years at the implant site without major signs of degradation, brushite-forming CPCs are considered to degrade to a greater extent. However, the latter tend to convert into lower soluble phases under physiological conditions, which makes their degradation behavior rather unpredictable. Secondly, CPCs exhibit insufficient mechanical properties for load bearing applications because of their inherent brittleness. This review places an emphasis on these limitations and provides an overview of studies that have investigated the biological and biomechanical performance as well as the degradation characteristics of different CPCs after implantation into trabecular bone. We reviewed studies performed in large animals, because they mimic human bone physiology more closely in terms of bone metabolism and mechanical loading conditions compared with small laboratory animals. We compared the results of these studies with clinical trials that have dealt with the degradation behavior of CPCs after vertebroplasty and kyphoplasty.

Calcium Phosphate Cement loaded with 10% vancomycin delivering high early and late local antibiotic concentration in vitro

BACKGROUND

Antibiotics impregnated calcium phosphate cement (CPC) has emerged as a local treatment of osteomyelitis. However, there is no study investigating the optimal concentrations of vancomycin (VCM) included in CPC to obtain prolonged drug release (≥8 weeks) and also with enough compressive strength (>the normal cancellous bone, 11MPa) for osteomyelitis therapy. Therefore, we bring forward two questions: 1) Was antibiotic activity of the eluates correlated to the load of antibiotics within the cement? 2) Were the mechanical properties of CPC affected by VCM-loading?

HYPOTHESIZED

There was an optimal concentrations of vancomycin (VCM) loaded in CPC which could provide sufficient effective antibacterial time (≥8 weeks) and enough compressive strength (>11MPa).

MATERIALS AND METHODS

CPC specimens were obtained by incorporating different doses (weigh ratios of 0%, 5%, 10%, 15%, 20%, 25 and 30%) of injectable VCM into CPC. The antibacterial effect of released VCM solution against Staphylococcus aureus was assessed by inhibition ring assays. The physicochemical properties such as compressive strengths were characterized and compared among these specimens.

RESULTS

Drug release profiles showed only 5 and 10% VCM-loaded CPC displayed a long enough drug release time (at least 8 weeks) and maintained the eluate concentrations (>4μg/mL) with effective antibacterial ability. The concentration of VCM in 10% group at 8th week was twice higher than 5% group. Compressive strength test showed that the proportional increase of VCM/CPC ratios resulted in a significant decrease of compressive strength (r=-0.906, p<0.001).

CONCLUSION

10% VCM-loaded CPC offered the optimal physicochemical properties and drug releasing profile and appears as the most suitable concentration for clinical use.

LEVEL OF EVIDENCE

III.

Effects of Adding Polysaccharides and Citric Acid into Sodium Dihydrogen Phosphate Mixing Solution on the Material Properties of Gelatin-Hybridized Calcium-Phosphate Cement

We have succeeded in improving the material properties of a chelate-setting calcium-phosphate cement (CPC), which is composed of hydroxyapatite (HAp) the surface of which has been modified with inositol hexaphosphate (IP6) by adding α-tricalcium phosphate (α-TCP) powder. In order to create a novel chelate-setting CPC with sufficient bioresorbability, gelatin particles were added into the IP6-HAp/α-TCP cement system to modify the material properties. The effects of adding polysaccharides (chitosan, chondroitin sulfate, and sodium alginate) into the sodium dihydrogen phosphate mixing solution on the material properties of the gelatin-hybridized CPC were evaluated. The results of mechanical testing revealed that chondroitin sulfate would be the most suitable for fabricating the hybridized CPC with higher compressive strength. Moreover, further addition of an appropriate amount of citric acid could improve the anti-washout capability of the cement paste. In summary, a gelatin-hybridized IP6-HAp/α-TCP cement system prepared with a mixing solution containing chondroitin sulfate and citric acid is expected to be a beneficial CPC, with sufficient bioresorbability and material properties.