Effect of wear, acetabular cup inclination angle, load and serum degradation on the friction of a large diameter metal-on-metal hip prosthesis

BACKGROUND

The large-scale clinical problem caused by unacceptable tribological behaviour of certain large diameter metal-on-metal prosthetic hips has directed attention to adverse condition testing. High metal-on-metal wear is connected with adverse reaction to metal debris. Friction is important because high friction may be associated with high wear, risk the fixation of the cup, and cause detrimental heating of periprosthetic tissues.

METHODS

A friction measurement system was added to a multidirectional, established hip joint wear simulator, and its functionality was evaluated. In preliminary tests, a 50 mm diameter metal-on-metal prosthesis was tested in an optimal acetabular cup inclination angle (48°) and in a steep angle (70°) using a normal peak load (2 kN) and an increased peak load (3 kN). The test length was 100 h. Long-term adverse condition tests of 3 million cycles were run for three 52 mm metal-on-metal prostheses. The lubricant was diluted calf serum at 37 °C.

FINDINGS

In the 100 h tests, metal-on-metal frictional torque was not highly sensitive to the angle, load and serum degradation, and it was close to that of a conventional 28 mm prosthesis with a polyethylene cup, mostly below 5 Nm. However, a manyfold higher frictional torque (10 to 20 Nm) was observed in long-term metal-on-metal tests with substantial wear.

INTERPRETATION

To obtain a realistic prediction of the frictional behaviour of a hip design, long-term, multidirectional wear tests are necessary. The friction should preferably be measured during the wear test. In addition to normal conditions, adverse condition testing is strongly recommended.

Three-dimensional friction measurement during hip simulation

Objectives

Wear of total hip replacements has been the focus of many studies. However, frictional effects, such as high loading on intramodular connections or the interface to the bone, as well as friction associated squeaking have recently increased interest about the amount of friction that is generated during daily activities. The aim of this study was thus to establish and validate a three-dimensional friction setup under standardized conditions.

Materials and methods

A standard hip simulator was modified to allow for high precision measurements of small frictional effects in the hip during three-dimensional hip articulation. The setup was verified by an ideal hydrostatic bearing and validated with a static-load physical pendulum and an extension-flexion rotation with a dynamic load profile. Additionally, a pendulum model was proposed for screening measurement of frictional effects based on the damping behavior of the angular oscillation without the need for any force/moment transducer. Finally, three-dimensional friction measurements have been realized for ceramic-on-polyethylene bearings of three different sizes (28, 36 and 40 mm).

Results

A precision of less than 0.2 Nm during three-dimensional friction measurements was reported, while increased frictional torque (resultant as well as taper torque) was measured for larger head diameters. These effects have been confirmed by simple pendulum tests and the theoretical model. A comparison with current literature about friction measurements is presented.

Conclusions

This investigation of friction is able to provide more information about a field that has been dominated by the reduction of wear. It should be considered in future pre-clinical testing protocols given by international organizations of standardization.