Load application for the contact mechanics analysis and wear prediction of total knee replacement

Effects of implant precoating and fat contamination on the stability of the tibial baseplate

BACKGROUND

Approximately 5% of primary total knee arthroplasty patients require revision within 10 years, often due to distal component loosening. Application of a thin layer of PMMA cement as precoating on the tibial component aims to prevent aseptic loosening. This study investigates the impact of precoating and fat contamination on tibial baseplate stability.

METHODS

Two groups of NexGen® stemmed tibial implants (size 4) were studied: Option implants (N = 12) and PMMA Precoat implants (N = 12). Each implant design was divided into two subgroups, (N = 6), with one subgroup featuring bone marrow fat at the implant-cement interface and the other without contamination. In a mechanical testing machine, the implants underwent uniaxial loading for 20,000 cycles, while recording vertical micromotion and migration of the tibial baseplates. Subsequently, a push-out test assessed fixation strength at the cement interfaces. Results were compared using non-parametric statistics and presented as median and min-to-max ranges.

RESULTS

Option implants exhibited higher micromotion in dry conditions compared to precoated implants (p = 0.03). Under contamination, both designs demonstrated similar micromotion values. Fixation strength did not significantly differ between designs under dry, uncontaminated conditions (p > 0.99). However, under contaminated conditions, the failure load for the non-coated Option implant was nearly half that of the uncontaminated counterparts (3517 N, 2603-4367 N vs 7531 N, 5163-9000 N; p = 0.002). Precoat implants displayed less susceptibility to fat contamination (p = 0.30).

CONCLUSION

NexGen® implant PMMA precoating might reduce the risk of aseptic loosening and revision surgery in case of eventual bone-marrow fat contamination.

Influence of posterior cruciate ligament tension on tibiofemoral and patellofemoral joint contact mechanics in cruciate-retaining total knee replacement: a combined musculoskeletal multibody and finite-element simulation

The influence of posterior cruciate ligament (PCL) tension on the clinical outcome of cruciate-retaining total knee replacement (CR-TKR) remains controversial. Various numerical approaches have been used to study this influence systematically, but the models used are limited by certain assumptions and simplifications. Therefore, the objective of this computational study was to develop a combined musculoskeletal multibody and finite-element simulation during a squat motion to 90° knee flexion with a CR-TKR design to overcome previous limitations regarding model inputs. In addition, different PCL tensions (tight, lax, resected) were modeled and the influence on tibiofemoral and resurfaced patellofemoral joint dynamics and contact stresses was evaluated. The effect of the PCL on knee joint dynamics and contact stresses was more pronounced at higher flexion angles. Tibiofemoral joint dynamics were influenced and a tight PCL induced increased posterior femoral translation during flexion. The maximum contact stress in the tibial insert increased from 20.6 MPa to 22.5 MPa for the resected and tightest PCL at 90° knee flexion. Patellofemoral joint dynamics were only slightly affected by PCL tension. However, the maximum contact stress in the patellar component decreased from 58.0 MPa to 53.7 MPa for the resected and tightest PCL at 90° knee flexion. The combination of musculoskeletal multibody and finite-element simulation is a sufficient method to comprehensively investigate knee joint dynamics and contact stresses in CR-TKR. The PCL tension after CR-TKR affects joint dynamics and contact stresses at the articulating implant surfaces.

Finite Element Analysis Contact Stresses on Tibiofemoral Joint and Post Polyethylene Components Used to Evaluated Predesign Knee Implant

At the time of prayer, most Muslims kneel with fully extended limbs (between 150° and 165°). Meanwhile, incidents such as hyperflexion in total knee arthroplasty (TKA) implant outside their designated configuration can lead wear or fracture of the polyethylene component. In this study, polyethylene component of posterior-stabilized right knee joint implant have been developed to facilitate higher range of motion (ROM). Finite element analysis (FEA) was used to analyze contact stresses on the polyethylene component. FEA was used to simulate weight-bearing condition at 0°, 30°, 60°, 90°, 120°, and 150° of knee flexion. Modified polyethylene component results in better performance in terms of contact stresses, especially at 120° of knee flexion. Current result shows contact stresses above 120 MPa were measured at the posterior post polyethylene, when 4000 N force was applied. Minimum contact stress on the medial condyles was 630 KPa at 120° of knee flexion, while on the lateral condyles, the minimum contact stress was 250 KPa at 150° of knee flexion. With this finding, the current polyethylene component design is expected to accommodate deep knee flexion movement in daily activities and can reduce potential of wear or fracture of the polyethylene component during deep knee flexion.

Stress response envelopes of intact tibiofemoral joint and knee osteoarthritis

The purpose of this study was to determine stress envelopes for an intact tibiofemoral joint and to study how they vary with knee loading, external–internal rotation, varus–valgus rotation and cartilage degradation (osteoarthritis) using the finite element method. The envelopes were presented in terms of knee flexion angle. The maximum von Mises stress for all tibiofemoral joint components increased with increasing the axial compressive force magnitude. Menisci exhibited the highest magnitude of maximum von Mises stress as compared to the femoral and tibial cartilages. In a range of flexion angles between 0° and 100°, the medial meniscus exhibited the highest maximum von Mises stress than the lateral meniscus and the stress in medial meniscus tended to increase with increasing the flexion angle. External–internal and varus–valgus rotations changed the stress distribution: higher stress on lateral compartment but lower stress on medial compartment, and conversely. The internal rotation provided more extreme effect than the external rotation. For the knee osteoarthritis, cartilage degradation (early stage) caused maximum von Mises stress to increase on the intact menisci revealing that knee osteoarthritis could also cause meniscal tear. The late osteoarthritis caused the maximum von Mises stress to increase on the calcified cartilage and subchondral bone.

Enhanced In-Silico Polyethylene Wear Simulation of Total Knee Replacements During Daily Activities

A computational wear simulator is an efficient tool for evaluating the wear of artificial knee joints. The classical Archard's wear law-based simulator has questionable accuracy and is focused on walking. In this study, an in silico polyethylene wear simulation of total knee replacements was developed considering the various highly demanding daily activities. A good predicted accuracy (error = 8.1%) was found through comparison of the experimental results. A relatively larger averaged wear loss was found under the loading condition (1.53 mg/mc) of daily activities compared with the walking condition (1.32 mg/mc). The squatting movement (2.57 mg/mc) produces the highest overall wear rate. In addition, a relatively larger amount of wear was found on the medial side knee prosthesis than that on the lateral side. The enhanced in silico polyethylene wear simulator provides an accurate and comprehensive tool for wear prediction in preclinical wear testing.