Magnesium-Based Temporary Implants: Potential, Current Status, Applications, and Challenges

Biomedical implants are important devices used for the repair or replacement of damaged or diseased tissues or organs. The success of implantation depends on various factors, such as mechanical properties, biocompatibility, and biodegradability of the materials used. Recently, magnesium (Mg)-based materials have emerged as a promising class of temporary implants due to their remarkable properties, such as strength, biocompatibility, biodegradability, and bioactivity. This review article aims to provide a comprehensive overview of current research works summarizing the above-mentioned properties of Mg-based materials for use as temporary implants. The key findings from in-vitro, in-vivo, and clinical trials are also discussed. Further, the potential applications of Mg-based implants and the applicable fabrication methods are also reviewed.

In-vivo bone remodeling potential of Sr-d-Ca-P /PLLA-HAp coated biodegradable ZK60 alloy bone plate

Magnesium and its alloys are widely applied biomaterials due to their biodegradability and biocompatibility. However, rapid degradation and hydrogen gas evolution hinder its applicability on a commercial scale. In this study, we developed an Mg alloy bone plate for bone remodeling and support after a fracture. We further coated the Mg alloy plate with Sr-D-Ca-P (Sr dopped Ca-P coating) and Sr-D-Ca-P/PLLA-HAp to evaluate and compare their biodegradability and biocompatibility in both in vitro and in vivo experiments. Chemical immersion and dip coating were employed for the formation of Sr-D-Ca-P and PLLA-HAp layers, respectively. In vitro evaluation depicted that both coatings delayed the degradation process and exhibited excellent biocompatibility. MC3T3-E1cells proliferation and osteogenic markers expression were also promoted. In vivo results showed that both Sr-D-Ca-P and Sr-D-Ca-P/PLLA-HAp coated bone plates had slower degradation rate as compared to Mg alloy. Remarkable bone remodeling was observed around the Sr-D-Ca-P/PLLA-HAp coated bone plate than bare Mg alloy and Sr-D-Ca-P coated bone plate. These results suggest that Sr-D-Ca-P/PLLA-HAp coated Mg alloy bone plate with lower degradation and enhanced biocompatibility can be applied as an orthopedic implant.

Effect and mechanism of a novel Mg-Nd-Gd-Sr alloy on osteogenic differentiation of bone marrow mesenchymal stem cells

We investigated the effect and mechanism of a novel Mg-3Nd-1Gd-0.3Sr-0.2Zn-0.4Zr (abbreviated to Mg-Nd-Gd-Sr) alloy on the osteogenic differentiation of bone marrow mesenchymal stem cells extracted from Sprague-Dawley rats. Cultured cells were divided into five groups: a control group cultured in osteogenic induction medium alone without Mg-Nd-Gd-Sr alloy extract, and four experimental groups cultured in the same medium with 25%, 50%, 75%, and 100% Mg-Nd-Gd-Sr alloy extracts, respectively. After 14 days of culture, ALP activity was determined and expressions of osteogenesis-related factors Runx2, OCN, and OPN at the mRNA level and Runx2, OCN, and OPN at the protein level were detected by RT-PCR and western blot, respectively. After 21 days of culture, mineralized nodules were detected by alizarin red staining. The results showed that bone marrow mesenchymal stem cells from Sprague-Dawley rats were successfully isolated in vitro using the whole bone marrow adherence method. Flow cytometry revealed that the cells expressed high levels of CD44 and CD90, but low levels of CD31 and CD45. Alizarin red staining indicated the formation of mineralized nodules in all five groups. Compared with the control group, the number of mineralized nodules was increased significantly in the four experimental groups (p < 0.05). The ALP activity in each group was significantly higher on day 14 than on day 7, and was significantly higher in the four experimental groups compared with the control group (p < 0.05). Moreover, the ALP activity was highest when the concentration of Mg-Nd-Gd-Sr alloy extract was 75% (p < 0.05). RT-PCR results showed that, compared with the control group, the mRNA expression of Runx2, OPN, and OCN was significantly higher in the four experimental groups (p < 0.05), and the highest mRNA expression of Runx2, OPN, and OCN was observed in the 75% experimental group (p < 0.05). Western blotting showed that Mg-Nd-Gd-Sr alloy extract significantly increased the protein expression of Runx2, OCN, and OPN compared with the control group (p < 0.05). Our data indicate that the novel Mg-Nd-Gd-Sr alloy can promotes the osteogenic differentiation of bone marrow mesenchymal stem cells isolated from Sprague-Dawley rats. During this process, there is an increase in the expressions of Runx2, OPN, and OCN mRNAs and Runx2, OCN, and OPN proteins.