Water absorption of poly(methyl methacrylate) measured by vertical interference microscopy

PMMA (poly(methyl methacrylate)) is widely used to prepare orthopedic cements. They are in direct contact with cells and body fluids. PMMA, despite its hydrophobic nature, can absorb ~2% w/w water. We have evaluated by vertical interference microscopy if water absorption can produce a significant swelling in different types of PMMA blocks: pure, with a plasticizer, with a cross-linker, and in two types of commercial bone cements. Graphite rods which do not swell in water were used as internal standard. Hardness, indentation modulus, plastic, and elastic works were determined by nanoindentation under a 25mN fixed force. Vertical interference microscopy was used to image the polymer in the dry state and hydrated states (after 24 h in distilled water). On the surface of the polished polymers (before and after hydration), we measured roughness by the fractal dimension, the swelling in the vertical and the lateral directions. For each polymer block, four images were obtained and values were averaged. Comparison and standardization of the images in the dry and hydrated states were done with Matlab software. The average value measured on the graphite rod between the two images (dried and hydrated) was used for standardization of the images which were visualized in 3D. After grinding, a small retraction was noticeable between the surface of the rod and the polymers. A retraction ring was also visible around the graphite rod. After hydration, only the pure PMMA and bone cements had a significant swelling in the vertical direction. The presence of polymer beads in the cements limited the swelling in the lateral direction. Swelling parameters correlated with the nanoindentation data. PMMA can swell by absorbing a small amount of water and this induces a swelling that varies with the polymer composition and particle inclusions.

Free radicals and side products released during methylmethacrylate polymerization are cytotoxic for osteoblastic cells

Polymerization of orthopedic cements makes use of a peroxide initiator which is decomposed by an accelerator to provide free radicals. Free radicals which act on the monomer molecules are also known to induce cell lesions and cell death. We used an in vitro model of cement polymerization to study the effects of free radicals release on osteoblast-like cells. Initiation of methylmethacrylate was done with benzoyl peroxide and acceleration by N,N-dimethylaniline. Bulk polymerization was done in calibrated test tubes which were left aging until use. Polymers (aged from J1 to J31 days after completion of the polymerization process) were sawed to produce slices. Slices were rinsed in distilled water and free radical release was measured by spectrophotometric titration with p-iodonitrotetrazolium. Saos-2 osteoblast-like cells were cultured in parallel on the slices. Cells appeared to be round and were altered when grown on slices prepared freshly after polymerization. Cytomorphometric analysis of the cell shape (surface area and form-factor polyethylene confirmed that they spread and flatten on slices prepared a long time after polymerization. Free radical release from polymethylmethacrylate cements is a long-lasting event that can induce bone cells alterations in their neighborhood. Two cytotoxic mechanisms were evidenced: (a) polymer slices released a stable toxic component which could be removed by extensive washing; (b) they released free radicals which were still detectable several days after the end of polymerization. The titration curve was a negative exponential.